A kind of multilayer ceramic capacitor copper electrode paste

A technology for multilayer ceramics and capacitors, applied in fixed capacitor electrodes, laminated capacitors, fixed capacitor dielectrics, etc., can solve problems affecting the use of screen printing, large viscosity changes, and unstable viscosity, etc., to suppress cracking and delamination , shrinkage inhibition, good thixotropy effect

Active Publication Date: 2022-03-18
JIANGSU HOYI TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the viscosity of the existing copper internal electrode slurry system is extremely unstable. After a period of time, the viscosity changes greatly. It even forms a gel and loses fluidity after a long period of storage, which seriously affects the use of subsequent screen printing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of multilayer ceramic capacitor copper electrode paste
  • A kind of multilayer ceramic capacitor copper electrode paste
  • A kind of multilayer ceramic capacitor copper electrode paste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The slurry formula is according to the common method of slurry, such as weighing each formula in proportion for batching→stirring→dispersing→rolling→semi-finished product inspection→slurry mixing→finished product inspection→packaging to prepare copper internal electrode slurry for MLCC.

[0032] Synthesis of polyamide polyacid polymer salt: the surfactant is preferably CTAB, 8.2g AMPS (2-acrylamido-2-methylpropanesulfonic acid) is dissolved in deionized water, and the pH is adjusted to 7~8 with NaOH ; Then 21g AM (monomer acrylamide), 1.3g BA (monomer butyl acrylate) and 2.5g DMDAAC (dimethyl diallyl ammonium chloride) were dissolved in the aqueous solution containing 1g CTAB, stirred to make it fully mixed dissolved; through high-purity nitrogen 30min, remove the oxygen in the solution; then add initiator 0.08g K 2 S 2 o 8 solution and 0.03g NaHSO 3 After the solution was fully mixed, the stirring was stopped. During the experiment, the amount of deionized water us...

Embodiment 2

[0042] The difference between embodiment 2 and embodiment is: a kind of multilayer ceramic capacitor copper electrode slurry, is made up of the raw material of following weight part:

[0043] 45 parts of copper powder, the particle size D50 of flake copper powder is 0.3μm;

[0044] 7.5 parts of ceramic powder, ceramic powder adopts BaNd 2X (Sm (0~1 / 3) PR (0~1 / 3) ) 2 (l-x) Ti 5 o 14 ,

[0045] 1 part of dispersant;

[0046] 2.9 parts of cellulose resin, cellulose resin adopts ethyl cellulose and polyvinyl butyral resin 4:1 blending;

[0047] 45 parts of organic solvent, organic solvent adopts dihydroterpineol;

[0048] 0.1 part of plasticizer, the plasticizer adopts dibutyl phthalate;

[0049] The main dispersant is polyamide polyacid polymer salt, 0.8 part; the auxiliary dispersant is 0.2 part of DP270.

Embodiment 3

[0051] The difference between embodiment 3 and embodiment is: a kind of multilayer ceramic capacitor copper electrode slurry, is made up of the raw material of following weight part:

[0052] 45 parts of copper powder, the particle size D50 of spherical copper powder is 0.1 μm;

[0053] 15 parts of ceramic powder, ceramic powder adopts zirconia composite ceramic powder;

[0054] 1.5 parts of dispersant;

[0055] 3 parts of cellulose resin, cellulose adopts hydroxypropyl cellulose;

[0056] 35 parts of organic solvent, organic solvent adopts butyl carbitol acetate;

[0057] 0.5 part of plasticizer, dioctyl phthalate;

[0058] The main dispersant is polyamide polyacid polymer salt, 1.3 parts; the auxiliary dispersant is SILOK 70740.2 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a multilayer ceramic capacitor copper electrode slurry, which is composed of the following raw materials in parts by weight: 40-50 parts of copper powder; 5-15 parts of ceramic powder; 0.5-1.5 parts of dispersant; 1-3 parts of cellulose resin 35-45 parts of organic solvent; 0.1-1 part of plasticizer; the main dispersant and auxiliary dispersant of the dispersant, the main dispersant is polyamide polyacid polymer salt, and the auxiliary dispersant is One or two of DP270, glyceryl tristearate, and oxidized polyethylene; the main dispersant accounts for more than 80% of the total dispersant. The invention provides a paste for copper electrodes of multilayer ceramic capacitors with high viscosity stability after nanometer copper powder is made into paste.

Description

technical field [0001] The invention relates to the technical field of capacitor paste, in particular to a multilayer ceramic capacitor copper electrode paste. Background technique [0002] Ceramic capacitors use ceramics as the dielectric, and then form metal electrodes on both sides of the ceramic substrate (the materials used for the electrodes include silver, silver-palladium, nickel, and copper). The methods of forming electrodes generally include thin-film technology and thick-film technology. At present, the screen printing method commonly used in thick film technology transfers the electrode paste to the surface of the ceramic substrate to form a certain pattern, and then fires it into a whole. [0003] Silver-based electronic pastes have been widely used in the electrodes of electronic components and shielding coatings to prevent electromagnetic interference. However, in recent years, the price of precious metals has doubled, and the miniaturization of multilayer ce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01G4/008H01G4/12H01G4/30
CPCH01G4/008H01G4/12H01G4/30
Inventor 杨爱民司留启白宝柱
Owner JIANGSU HOYI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap