Method for preparing granite decorative plate from granite sawing mud

A technology for decorative plates and granite, which is applied in the field of preparing granite decorative plates by using granite sawdust, can solve problems such as difficulty in large-scale application, harsh maintenance conditions, complicated processing technology, etc., and achieves reduction of main structure cost and material bulk density. , the effect of reducing the structural load

Active Publication Date: 2020-04-14
SISHUI HUIFENG AGRI DEV ENG CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although granite stone powder has the incomparable structural strength advantage of natural stone, it is difficult to be widely used in the field of decorative engineering. In addition, its processing technology is complicated and the maintenance conditions are harsh, so the processing cost is high, so the application field is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A preparation method for preparing granite decorative plates by using granite sawing mud, comprising the following steps:

[0029] (1) Surface material configuration: The surface material is composed of the following materials by mass: PO42.5 white / ordinary Portland cement 90-110 parts, granite washed fine sand 50-130 parts, granite stone powder 10-30 parts, Fe3O4 magnetic 2-5 parts of iron ore powder, 1-3 parts of aluminum silicate, 0.5-10 parts of inorganic oxidation pigment;

[0030] (2) Forming of the surface layer material: select the surface layer material according to the proportion of step (1), after the above materials are fully mixed, add 20-30% clear water accounting for PO42.5 white / ordinary portland cement weight, and fully mix the material After the viscous paste is synthesized, it is poured into the mold for paving. The average thickness of the paving is not more than 3mm. After paving, the double vibrator platform is vibrated, and the vibrating time is n...

Embodiment 1

[0039] Preparation of imitation rust stone granite compound coarse grinding plate:

[0040] Take 100 parts of PO42.5 white cement, 130 parts of machine-made fine sand (40-120 mesh) for rust stone waste rock granite processing, 20 parts of granite (rust stone) stone powder (200 mesh), Fe3O4 magnetite powder (200 mesh) 5 parts, 1 part of aluminum silicate (200 mesh), 1.4 parts of iron oxide yellow (200 mesh), 25 parts of water were added and fully mixed to obtain the rust stone surface material.

[0041] Put the surface material into a high-gloss plastic mold, vibrate on a double-frequency high-frequency vibration platform for 65 seconds, and put it into a 45-degree pre-curing room for 15 minutes;

[0042] During the pre-cultivation period, take 100 parts of PO Portland ordinary cement, 25 parts of ferroalloy silica fume, 6 parts of vitrified microbeads, 0.1 part of loose carbon fiber, 3 parts of copper-plated steel fiber, and washed granite sand (18-120 Mesh) 110 parts, granit...

Embodiment 2

[0047] Preparation of imitation Lu gray granite composite fire plate:

[0048] Take 80 parts of PO Portland white cement, 20 parts of PO Portland ordinary cement, 130 parts of machine-made fine sand (40-120 mesh) processed from granite (Luhui waste rock), 20 parts of Luhui granite stone powder (200 mesh) , Fe O Magnetite powder (200 orders) 5 parts, aluminum silicate (200 orders) 1.4 parts, iron oxide black (200 orders) 4 parts, add 25 parts of water and fully mix, obtain Lu ash surface material;

[0049] After fully mixing the material into a viscous paste, pour it into the mold for paving. The average thickness of the paving is not more than 3mm. After paving, vibrate on the double vibrator platform. 15 minutes for initial cultivation in a constant temperature room;

[0050] During the pre-cultivation period, take 100 parts of PO Portland ordinary cement, 25 parts of ferroalloy silica fume, 7.5 parts of vitrified microspheres, 0.1 part of decomposed carbon fiber, 3 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for preparing a granite decorative plate from granite sawing mud. The method comprises the steps of surface layer material preparation, surface layer material forming, base layer material preparation, base layer material forming, composite material secondary forming and product maintenance. The machine-made fine sand and stone powder produced by processing granite solid waste are adopted to replace quartz sand and quartz powder, and the product cost can be effectively reduced on the basis that granite sawing mud is massively applied and the environmental influence is eliminated; after the product is formed at a time, the product is free of cracks in appearance and deformation in structure, and is excellent in stability, and has the advantages ofhigh strength, high bending resistance, low water absorption, acid and alkali resistance, fire resistance, weather resistance and the like of an RPC composite material, all indexes are superior to those of natural stone, and the product service life reaches 50 years or longer.

Description

technical field [0001] The invention relates to the technical field of plate preparation, in particular to a preparation method for preparing granite decorative plates by using granite sawing mud. Background technique [0002] During the cutting process of natural granite, about 5% of sawing mud will be produced. Because these sawing mud contains chemicals such as coolants and suspending agents, and materials with a diameter of ≤75 μm account for more than 80% of its weight ratio, there is still no great success in China. Applying the mature technology of granite sawing mud, most of the sawing mud is dumped randomly, resulting in serious water pollution; at the same time, sawing mud powder has a certain cohesive force and is repeatable, even if it is plowed or applied with farmyard manure, it cannot be completely eliminated. In the soil, it will make the soil harden quickly, and the air permeability, moisture retention and internal structure of the soil will lead to damage, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04B32B37/15B28B1/087B28B1/52
CPCC04B28/04B32B37/15B28B1/0873B28B1/523B28B1/52C04B2111/00612C04B14/048C04B14/308C04B14/041C04B2103/54C04B18/146C04B18/027C04B14/386C04B14/48C04B2103/302C04B2103/50Y02W30/91
Inventor 董忠
Owner SISHUI HUIFENG AGRI DEV ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com