Preparation process of carbon slide plate

A preparation process and technology of carbon skateboards, which are applied in electric vehicles, power collectors, transportation and packaging, etc., can solve the problems that cannot meet the requirements of motorcycles for skateboards, and are expensive

Inactive Publication Date: 2020-04-14
DATONG XINCHENG NEW MATERIAL CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of high-speed electric locomotives, these types of skateboards cannot meet the requirements of locomotives for skateboards.
At present, the material of foreign skateboards is mainly metal-impregnated carbon skateboards, which have superior performance, but there is no description of specific preparation methods in the literature, and the price is expensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0118] The following clearly and completely describes the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0119] A carbon slide preparation process, comprising the following steps:

[0120] S1. Extrusion: Extrude the granular material into a carbon strip of a certain size

[0121] (1) Raw materials: 5 parts by weight of flake graphite, 5 parts of carbon black, 60 parts of pitch coke, and 30 parts of pitch are used to prepare raw materials;

[0122] (2) Kneading: put flake graphite, carbon black, and pitch coke in S1 into a kneading pot for dry mixing, stir at a speed of 60 rpm for 40 minutes, and dry mixing temperature 120°C; add pitch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of carbon slide plate preparation. The invention relates to the technical field of pantograph carbon sliding plate manufacturing, in particular to a carbonsliding plate manufacturing process, a copper pipe groove is pre-embedded in one side of an inner arc of a carbon sliding strip of a pantograph carbon sliding plate, an intact copper pipe air channelis embedded during bonding and curing, and the two ends of a copper pipe are welded to air pipe connectors respectively to form the complete pantograph carbon sliding plate with the airtight safety function. By researching the raw material formula and the process method, the carbon slide strip capable of improving the process quality of a product forming process, a roasting process, an impregnation process and the like and key quality indexes of the product volume density, resistance, breaking strength, compressive strength, uniform structure, impact toughness and the like is prepared. Afterthe pantograph carbon slide plate without the copper pipe air passage is mounted on a pantograph device of an electric locomotive, the carbon slide plate is continuously abraded in continuous operation, the abrasion thickness of the carbon slide strip is continuously reduced, and crack air leakage of the carbon strip possibly occurs under the action of impact force.

Description

technical field [0001] The invention relates to the technical field of carbon slide preparation, and more specifically, relates to a carbon slide preparation process. Background technique [0002] At present, there are three main types of pantograph slides: powder metallurgy slides, pure carbon carbon slides and metal-impregnated carbon slides. Among them, the powder metallurgy sliding plate has high mechanical strength, good impact resistance, good electrical conductivity and wear resistance, but it has serious wear on the catenary wire. The pure carbon-carbon skateboard itself is a very good lubricant, with good self-lubricating performance and anti-friction performance, less wear on the catenary wire, and high temperature resistance, and it is not easy to weld with the catenary wire, but its mechanical strength is low. It has poor impact resistance and therefore breaks or cracks easily. Metal-impregnated carbon slides not only have the characteristics of high mechanical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B60L5/20C04B35/532C04B35/622C04B41/88C04B37/02
CPCB60L5/205C04B35/532C04B35/622C04B37/028C04B41/5127C04B41/88C04B2235/424C04B2235/425C04B2235/6562C04B2235/6567C04B2237/363C04B2237/402C04B41/4523
Inventor 张作文杨长命慕治勇曹贵平田海军杨维才王志辉张晨阳
Owner DATONG XINCHENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products