A preparation method of composite anti-corrosion, wear-resistant and high-temperature-resistant pipe

A high temperature resistant pipe, composite technology, applied in the direction of preventing damage/wear of pipes, anti-corrosion/anti-rust protection of pipes, pipes, etc., can solve the problems of difficult processing of ceramic pipes, easy rupture of inner ceramic walls, and poor impact resistance. , to improve the anti-shedding performance, low processing and production difficulty, and good impact resistance.

Active Publication Date: 2022-01-07
襄阳慧通电力科技有限公司
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of the existing ceramic composite pipe is complicated, the processing of the ceramic pipe is difficult, and the cost is extremely high
Secondly, the existing ceramic composite pipes have poor impact resistance, the inner ceramic wall is easy to break, damage and fall off, and the service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of composite anti-corrosion, wear-resistant and high-temperature-resistant pipe
  • A preparation method of composite anti-corrosion, wear-resistant and high-temperature-resistant pipe
  • A preparation method of composite anti-corrosion, wear-resistant and high-temperature-resistant pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The principles and features of the present invention are described below in conjunction with the accompanying drawings, and the examples given are only used to explain the present invention, and are not intended to limit the scope of the present invention.

[0032] In the description of the present invention, it should also be noted that, unless otherwise clearly specified and limited, the terms "setting", "installation" and "connection" should be interpreted in a broad sense, for example, it can be a fixed connection or an optional connection. Detachable connection, or integral connection; it can be mechanical connection or electrical connection; it can be direct connection or indirect connection through an intermediary, and it can be the internal communication of two components. Those of ordinary skill in the art can understand the specific meanings of the above terms in the present invention in specific situations.

[0033] Such as Figure 1 ~ Figure 3 Shown, the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a composite anticorrosion, wear-resistant, and high-temperature-resistant pipe, which comprises the following steps: 1) making porcelain tiles: according to the proportion, select raw material powders with a particle size of 50 μm, mix them evenly, and mix the evenly mixed The powder is made into a green body of ceramic chips, and then sintered at high temperature to make ceramic chips; 2) Making ceramic tubes: according to the size of the pipe diameter, select an appropriate number of ceramic chips and splice them into a circular ceramic ring. Bonding with a high temperature and corrosion resistant adhesive, and then bonding the ceramic ring with a high temperature and corrosion resistant adhesive to form a ceramic tube; 3) Prepare a composite tube: coat a layer of inorganic layer in the metal tube body, and When it is not solidified, insert the ceramic tube into the metal tube body to ensure the seamless bonding of the ceramic tube and the inorganic layer. After the inorganic layer is solidified, a composite anti-corrosion, wear-resistant, and high-temperature-resistant tube is produced. The invention can process the metal composite ceramic tube with good corrosion resistance, wear resistance, high temperature resistance and impact resistance, and the production process is simple and the cost is low.

Description

technical field [0001] The invention relates to the technical field of special pipes, in particular to a method for preparing a composite anti-corrosion, wear-resistant and high-temperature-resistant pipe. Background technique [0002] Special pipes are pipes used in special environments. Different from ordinary pipes, the use environment of special pipes determines that they need to have special properties, such as high temperature resistance, wear resistance, impact resistance, etc. For example, the tertiary air pipe of a cement kiln is a special pipe used in a cement kiln. When the cement kiln is running, the temperature inside the pipe changes greatly, the wind speed inside the pipe is high, and the hot air flow contains a large number of fine clinker particles. Scouring and erosion of dusty hot air. Another example is oil pipelines, which are used to transport crude oil and work under high pressure and corrosion conditions for a long time. These special scenarios requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L9/22F16L57/06F16L58/14C04B35/10
CPCF16L9/22F16L57/06F16L58/14C04B35/10C04B2235/3418C04B2235/3244C04B2235/3208C04B2235/3206C04B2235/3826C04B2235/3232C04B2235/5436
Inventor 刘元银
Owner 襄阳慧通电力科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com