A kind of lightweight green non-heat-sealable tea filter paper and preparation method thereof

A non-heat-sealing, tea filter paper technology, applied in chemical instruments and methods, filter paper, separation methods, etc., can solve the problems of shortage of papermaking raw materials, low paper strength, and high cost, and improve market competitiveness and paper quality. The effect of uniform softness and saving packaging costs

Active Publication Date: 2022-01-04
ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Not only is the cost expensive, the strength of the paper is low, but also the papermaking process and the addition of additives have caused some pollution to the environment, and there is a shortage of papermaking raw materials in my country. We should not blindly use traditional wood pulp, but should look for new high-quality fiber raw materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lightweight green non-heat-sealable tea filter paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing lightweight green non-heat-sealable tea filter paper, comprising the steps of:

[0021] (1) Beating: Three fiber pulps are beaten respectively, the concentration of the bark pulp is 5%, and the conical refiner beats until the degree of beating is 45°SR; the concentration of the full chlorine-free bleached coniferous wood pulp is 4%, and the double disc refiner beats The controlled beating degree is 42°SR; the concentration of viscose fiber pulp is 0.6%, and the volt type beater is beaten until the beating degree is 15°SR. The beaten pulp is mixed according to the mass ratio, and treated with a leveling refiner for 30s.

[0022] The said bark fiber is prepared by chemical thermo-mechanical method, the bark is first mechanically rubbed to remove the black bark on the surface to obtain the white bark, which is cut into small sections of 20 mm to 30 mm; the white bark is pretreated with biological enzymes for 8 hours , washed; then 4% NaOH and 2% H 2...

Embodiment 2

[0031] A method for preparing lightweight green non-heat-sealable tea filter paper, comprising the steps of:

[0032] (1) Beating: Three kinds of fiber pulp are beaten respectively, the concentration of the bark pulp is 4%, and the conical refiner beats until the degree of beating is 45°SR; the concentration of the full chlorine-free bleached coniferous wood pulp is 5%, and the double disc refiner beats The controlled beating degree is 42°SR; the concentration of viscose fiber pulp is 0.8%, and the beating degree is 15°SR with a volt type beater.

[0033] The said bark fiber is prepared by chemical thermo-mechanical method, the bark is first mechanically rubbed to remove the black bark on the surface to obtain the white bark, which is cut into small sections of 20 mm to 30 mm; the white bark is pretreated with biological enzymes for 8 hours , washed; then 4% NaOH and 2% H 2 o 2 Treat at 80°C for 60-80 minutes, and finally use a twin-screw press to make pulp, with a screw spe...

Embodiment 3

[0042] A method for preparing lightweight green non-heat-sealable tea filter paper, comprising the steps of:

[0043] (1) Beating: Three kinds of fiber pulp are beaten separately, the concentration of the bark pulp is 3%, and the conical refiner beats until the degree of beating is 45°SR; the concentration of the full chlorine-free bleached coniferous wood pulp is 6%, and the double disc refiner beats the pulp The controlled beating degree is 42°SR; the concentration of viscose fiber pulp is 1.0%, and the beating degree is 15°SR with a volt type beater.

[0044] The said bark fiber is prepared by chemical thermo-mechanical method, the bark is first mechanically rubbed to remove the black bark on the surface to obtain the white bark, which is cut into small sections of 20 mm to 30 mm; the white bark is pretreated with biological enzymes for 8 hours , washed; then 4% NaOH and 2% H 2 o 2 Treat at 80°C for 60-80 minutes, and finally use a twin-screw press to make pulp, with a sc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of papermaking, in particular to a non-heat-sealable tea filter paper. The filter paper is made from a mixture of bark pulp, bleached coniferous wood pulp and viscose fiber. The chemical additives added to the pulp are all green natural polymer additives, which have the characteristics of complete natural circulation and biodegradation. The invention also discloses a preparation method of the tea filter paper, which includes the following steps: (1) beating; (2) mixing; (3) forming on the net; (4) pressing (5) drying; (6) cutting the roll paper . The tea filter paper obtained by the preparation method has good dry and wet strength, uniform and soft paper quality, high air permeability which facilitates the penetration of tea aroma, and the light weight of the product can save packaging costs for users and improve market competitiveness.

Description

technical field [0001] The invention relates to a method for making tea filter paper, in particular to a lightweight green non-heat-sealable tea filter paper and a preparation method thereof. Background technique [0002] Teabags are very popular in European and American countries because of their convenient and hygienic drinking, quick dissolution of active ingredients in the tea leaves, and accurate quantification when drinking. More than 80% of the tea leaves in Canada, Italy, Holland, France and other countries are consumed in the form of teabags, and the UK and the U.S. have also reached about 80%. my country's teabag production started in the 1960s, with an annual output of about 30,000 tons of teabags, accounting for about 5% of the country's total tea production, and domestic consumption of teabags accounts for about 2% of the total tea sales. Tea raw materials, packaging materials and teabag packaging machines are the three elements of teabag production, and packag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/08D21H11/08D21H13/08D21H17/29D21H17/15D21H17/32D21F11/02D21H21/14D21H21/18D21H21/20B01D39/14
CPCD21H27/08D21H11/08D21H13/08D21H17/29D21H17/15D21H17/32D21F11/02D21H21/14D21H21/18D21H21/20B01D39/14B01D2239/0407B01D2239/10
Inventor 翟睿刘全鑫胡志军李国毅周怡恒郭大亮
Owner ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com