SPHC low-carbon type steel production technology

A technology of production process and steel type, which is applied in the field of SPHC low-carbon steel production process, can solve the problems of continuous casting castability, high aluminum content, serious flocculation and other problems, so as to improve the continuous casting furnace The effect of reducing the number of processes, reducing production costs, and reducing production volume

Active Publication Date: 2019-06-14
SD STEEL RIZHAO CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, reducing process costs is a problem that Zhuduo enterprises are focusing on solving. Among them, the short-process smelting process has a significant effect on reducing costs and increasing efficiency. However, in the production process, the oxygen content of SPHC steel grades entering the station is controlled as high as 600-800ppm, resulting in After the RH treatment, the oxygen level is higher, which indirectly leads to the addition of too much aluminum content, which has a great impact on the quality of molten steel and the castability of continuous casting. During the pouring process, the nozzle flocculation is serious. Replacing the nozzle caused serious flocculation. Simple replacement of the nozzle can no longer solve the pouring problem, resulting in single-flow production or even unplanned shutdown

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] In order to be able to understand the above objectives, features and advantages of the present invention more clearly, the present invention will be further described with reference to the following embodiments. It should be noted that the embodiments of the application and the features in the embodiments can be combined with each other if there is no conflict.

[0019] In the following description, many specific details are set forth in order to fully understand the present invention. However, the present invention can also be implemented in other ways than those described here. Therefore, the present invention is not limited to the specific embodiments disclosed in the following specification. limit.

[0020] A SPHC low-carbon steel production process adopts the following control methods:

[0021] (1) On the premise of ensuring that the final temperature of the converter meets the requirements, ensure the low-level control of the final content of the converter;

[0022] (2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an SPHC low-carbon type steel production technology. A following control method is adopted and comprises the steps that converter end point content low-level control is guaranteed on the premise that it is guaranteed that the converter end point temperature meets the requirements; the CAS refining effect is improved, slag inclusion adsorption is conducted, and meanwhile theRH station inlet oxygen content is decreased to ensure the pouring property of molten steel; a CAS argon blowing model is optimized, argon gas stirring pressure models in the different stages are made, therefore, full floating of inclusions is effectively promoted, and meanwhile the process temperature drop is reduced; RH low oxygen level control is achieved, the RH station inlet oxygen content is decreased, the RH residual oxygen content is precisely controlled, the aluminum consumption is reduced, and the production yield is indirectly decreased; and the continuous casting machine protective pouring argon gas flow is optimized, and the condition that the pouring property is influenced due to water port inclusion concentration is avoided. According to the SPHC low-carbon type steel production technology, the purposes that on the basis that a water port is not displaced in the pouring process, the continuous pouring number is increased, and meanwhile the production cost of the processes is reduced are achieved.

Description

Technical field [0001] The invention belongs to the field of steelmaking, and in particular relates to a production process of SPHC low-carbon steel grades. Background technique [0002] At present, the production process of iron and steel enterprises generally adopts molten iron pretreatment-converter-LF refining-slab continuous caster process for smelting. Although this kind of production process is relatively mature, it is prone to silicon recovery, phosphorus recovery and electrode carbon increase phenomenon, and at the same time refining Power consumption and slagging costs are high, and the cost of smelting per ton of steel is high. As a conventional hot-rolled product, SPHC low-carbon steel has a large market demand. Therefore, reducing the process cost is a problem that Zhuduo companies strive to solve. Among them, the short-flow smelting process has a significant effect on reducing costs and increasing efficiency. However, during the production process, the incoming oxy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/072C21C5/30B22D41/58
Inventor 温福新温维新胡勤东王学新毕永杰佟圣刚刘建伟赵珉王玉民马强陈常义王兴
Owner SD STEEL RIZHAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products