Flame-retardant wood-plastic compound material tray

A wood-plastic composite material, flame-retardant technology, applied in the field of plastic product processing, can solve problems such as burning, discharge, safety hazards and so on

Inactive Publication Date: 2018-12-07
WUHU ASIA PACIFIC GENERAL TRAY PACKING CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because thermoplastics, one of the main raw materials of wood-plastic composite materials used in wood-plastic composite pallets, are good electrical insulators, they are still poor conductors of electricity after being combined with wood fiber materials, and they tend to accumulate a large amount of electricity during use. Electrostatic charge, causing dust suction, discharge, breakdown and other dangers, and even burning or explosion, there is a huge potential safety hazard
In addition, wood-plastic composite materials are flammable materials, which largely limits the application of wood-plastic composite pallets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A flame-retardant wood-plastic composite tray, characterized in that it includes the following raw materials in parts by weight: 50 parts of bamboo powder, 60 parts of high-density polyethylene, 1 part of silane coupling agent KH550, and 2 parts of maleic anhydride grafted polyethylene , 0.5 parts of sodium stearate, 2 parts of polyethylene wax, 0.5 parts of azobisisobutyronitrile, 7 parts of muscovite, 0.2 parts of p-phenylenediamine, 1 part of antioxidant 1076, 1 part of black masterbatch, composite barrier 13 parts of fuel, 6 parts of modified carbon black.

Embodiment 2

[0021] A flame-retardant wood-plastic composite tray, characterized in that it includes the following raw materials in parts by weight: 70 parts of bamboo powder, 45 parts of high-density polyethylene, 4 parts of silane coupling agent KH550, and 0.3 parts of maleic anhydride grafted polyethylene , 2 parts of sodium stearate, 1 part of polyethylene wax, 1 part of azobisisobutyronitrile, 3 parts of muscovite, 1 part of p-phenylenediamine, 0.2 parts of antioxidant 1076, 2 parts of black masterbatch, composite barrier 9 parts of fuel, 10 parts of modified carbon black.

Embodiment 3

[0023] A flame-retardant wood-plastic composite tray, characterized in that it includes the following raw materials in parts by weight: 50 parts of bamboo powder, 60 parts of high-density polyethylene, 1 part of silane coupling agent KH550, and 2 parts of maleic anhydride grafted polyethylene , 0.5 parts of sodium stearate, 2 parts of polyethylene wax, 0.5 parts of azobisisobutyronitrile, 7 parts of muscovite, 0.2 parts of p-phenylenediamine, 1 part of antioxidant 1076, 1 part of black masterbatch, composite barrier 13 parts of combustion agent and 6 parts of modified carbon black; the composite flame retardant is composed of expandable graphite, nano magnesium hydroxide and red phosphorus in a weight ratio of 3:3:1.

[0024] The preparation of the modified carbon black: put the conductive carbon black in an oven, bake it at 102°C for 5 hours, then mix the conductive carbon black with the silane coupling agent KH550 and absolute ethanol in a weight ratio of 50:2 : 110 mixed ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
heat release rateaaaaaaaaaa
water contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of plastic product production, and particularly discloses a flame-retardant wood-plastic compound material tray. The tray is prepared from the following raw materials in parts by weight: 50-70 parts of bamboo powder, 45-60 parts of high-density polyethylene, 1-4 parts of silane coupler KH550, 0.3-2 parts of maleic anhydride grafted polyethylene, 0.5-2 parts of sodium stearate, 1-2 parts of polyethylene wax, 0.5-1 part of azodiisobutyronitrile, 3-7 parts of muscovite, 0.2-1 part of p-phenylenediamine, 0.2-1 part of antioxidant 1076, 1-2 parts of black masterbatch, 9-13 parts of compound flame retardant and 6-10 parts of modified carbon black. The flame-retardant wood-plastic compound material tray has excellent electrostatic resistance and flameretardance.

Description

technical field [0001] The invention relates to the technical field of plastic product processing, in particular to a flame-retardant wood-plastic composite tray. Background technique [0002] At present, the pallets on the market are mainly wooden pallets and plastic pallets. Wooden pallets have a large demand for wood, which is not conducive to the protection of forest resources. In addition, fumigation or high-temperature disinfection treatment is required; and the common problem of plastic pallets is the quality of pallets. The rigidity is not enough, and it is prone to creep phenomenon when it is applied to shelf storage. Wood-plastic composite pallets are made of wood powder or plant fibers filled with high-value thermoplastic resin or thermoplastic plastic recycled materials, and some related modifiers are added, and then extruded and injection-molded. These products can replace the corresponding wooden pallets and Plastic pallets can save a lot of forest resources, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L97/02C08L51/06C08K13/06C08K5/098C08K3/34C08K5/18C08K3/04C08K9/06C08K3/22
CPCC08K2003/2224C08K2201/011C08L23/06C08L97/02C08L2201/02C08L2201/04C08L2205/025C08L2205/035C08L2207/062C08L51/06C08K13/06C08K5/098C08K3/34C08K5/18C08K3/04C08K9/06C08K3/22
Inventor 夏则荣
Owner WUHU ASIA PACIFIC GENERAL TRAY PACKING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products