High-dispersion modified nanometer molybdenum disulfide lubricant and preparation method thereof

A nano-molybdenum disulfide, high-dispersion technology, applied in chemical instruments and methods, dyeing polymer organic compound treatment, lubricating composition, etc., can solve the problems of easy aggregation of nano-molybdenum disulfide, low friction coefficient, anti-pressure and anti-wear properties, Difficult to disperse and other problems, to avoid agglomeration, improve anti-pressure and anti-wear performance, and not easy to agglomerate

Inactive Publication Date: 2018-11-30
界首市鑫全龙粮食机械购销有限公司
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above problems, the present invention aims to provide a highly dispersed modified nano-molybdenum disulfide lubricant and its preparation method to solve the problem that nano-molybdenum disulfide is easy to agglomerate and difficult to disperse in the lubricant, and at the same time provide a friction Lubricant with low coefficient and good anti-pressure and anti-wear properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A highly dispersed modified nano molybdenum disulfide lubricant is characterized in that it is made of the following raw materials in parts by weight:

[0025] Modified nano molybdenum disulfide 10, base oil 80, palm oil 5, polymethacrylate 2, polyethylene glycol 1.

[0026] Further, the preparation method of the modified nano molybdenum disulfide comprises the following steps:

[0027] (1) Pretreatment of nano molybdenum disulfide:

[0028] Put 10 parts of nano-molybdenum disulfide in a tube furnace at 200°C, roast for 3 hours, then cool down to room temperature at a rate of 4°C / min, put it in a pressure box, and keep the pressure at 2MPa for 1 hour, then adjust the pressure To negative pressure, keep the pressure at -3MPa for 40 minutes, return to normal pressure, and put it into a ball mill for 20 minutes;

[0029] (2) Zirconium dioxide modified nano molybdenum disulfide

[0030] Dissolve 5 parts of zirconium nitrate in deionized water to make a zirconium nitrate ...

Embodiment 2

[0040] A highly dispersed modified nano molybdenum disulfide lubricant is characterized in that it is made of the following raw materials in parts by weight:

[0041] Modified nano molybdenum disulfide 15, base oil 90, palm oil 6, polymethacrylate 3, polyethylene glycol 2.

[0042] Further, the preparation method of the modified nano molybdenum disulfide comprises the following steps:

[0043] (1) Pretreatment of nano molybdenum disulfide:

[0044] Put 15 parts of nano-molybdenum disulfide in a tube furnace at 210°C, roast for 4h, then cool down to room temperature at a rate of 5°C / min, put it in a pressure box, and keep pressure at 3MPa for 1.5h, then adjust From pressure to negative pressure, keep the pressure at -4MPa for 60 minutes, return to normal pressure, and put it into a ball mill for ball milling for 25 minutes;

[0045] (2) Zirconium dioxide modified nano molybdenum disulfide

[0046] Dissolve 7 parts of zirconium nitrate in deionized water to make a zirconium n...

Embodiment 3

[0056] A highly dispersed modified nano molybdenum disulfide lubricant is characterized in that it is made of the following raw materials in parts by weight:

[0057] Modified nano molybdenum disulfide 20, base oil 100, palm oil 10, polymethacrylate 3, polyethylene glycol 2.

[0058] Further, the preparation method of the modified nano molybdenum disulfide comprises the following steps:

[0059] (1) Pretreatment of nano molybdenum disulfide:

[0060] Put 20 parts of nano-molybdenum disulfide in a tube furnace at 230°C, roast for 4 hours, then cool down to room temperature at a rate of 6°C / min, put it in a pressure box, keep the pressure at 5MPa for 2 hours, and then adjust the pressure To negative pressure, keep the pressure at -4MPa for 70 minutes, return to normal pressure, and put it into the ball mill for 30 minutes;

[0061] (2) Zirconium dioxide modified nano molybdenum disulfide

[0062] Dissolve 8 parts of zirconium nitrate in deionized water to make a zirconium nit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-dispersion modified nanometer molybdenum disulfide lubricant and a preparation method thereof. The dispersity of the prepared modified nanometer molybdenum disulfide inthe lubricant is good, the prepared modified nanometer molybdenum disulfide is not easy to agglomerate and stable in property, and the obtained lubricant has relatively high maximum non-seizure load,the grinding spot diameter is small, the friction coefficient is low, and the anti-compression and anti-wear performance is excellent. After the nano molybdenum disulfide is pretreated, the internal structure of the nano molybdenum disulfide is loose and dispersed, and the dispersity is improved and the stability of the nano-molybdenum disulfide in the lubricant is enhanced; and the surface of thenano-molybdenum disulfide is wrapped by using zirconium dioxide; on one hand, the nano-molybdenum disulfide is collaborative with the zirconium dioxide, so that the friction coefficient of the lubricant is reduced, the compression resistance and wear resistance are enhanced, and on the other hand, the dispersity of molybdenum disulfide and its own in a lubricant is also promoted, and the agglomeration phenomenon is avoided.

Description

technical field [0001] The invention belongs to the technical field of lubricants, in particular to a highly dispersed modified nano molybdenum disulfide lubricant and a preparation method thereof. Background technique [0002] Lubricant is an essential substance in the mechanical field, mainly to reduce friction, improve the operating speed of the machine and prolong the life of the machine. With the increasing demand for lubricants in the industry, there are more and more types of lubricants. When people choose lubricants, they generally have to consider the coefficient of friction, material, surface roughness, working environment and working conditions, and the performance of lubricants. Performance and other factors, in mechanical equipment, lubricants are mostly delivered to the parts that need to be lubricated through the lubrication system. Nano-nano molybdenum disulfide has a layered structure, and the sliding between layers is very easy, which can significantly red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/22C10M159/12C10M167/00C09C1/00C09C3/06C09C3/10C09C3/04C10N30/06
CPCC01P2004/64C09C1/0003C09C3/006C09C3/048C09C3/06C09C3/10C10M125/22C10M159/12C10M167/00C10M2201/14C10M2207/40C10M2209/08C10M2209/103C10N2030/06
Inventor 申慧君
Owner 界首市鑫全龙粮食机械购销有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com