A method for efficient extraction of valuable component titanium from titanium-containing blast furnace slag

A blast furnace slag, high-efficiency technology, applied in the field of efficient extraction of titanium, a valuable component in titanium-containing blast furnace slag, can solve problems such as equipment corrosion, poor cement activity, and low TiO2 content.

Active Publication Date: 2019-04-09
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

TiO in blast furnace slag 2 Low content, complex mineral phase structure, difficult to be used as raw material for titanium extraction
At present, only Panzhihua Iron and Steel Co., Ltd. discharges 3000Kt of titanium-containing blast furnace slag every year, and most of them are disposed of as waste stockpiles, which not only causes environmental pollution, but also causes waste of resources.
[0003] For the recovery of titanium resources in titanium-containing blast furnace slag, researchers have carried out a lot of work, mainly forming the following treatment methods: (1) acid extraction of TiO 2 , including sulfuric acid method and hydrochloric acid method, due to the stable phase structure of titanium-containing blast furnace slag, it needs to be decomposed with high acid, and the reaction is not complete, TiO 2 The extraction cost is high; (2) Alkaline extraction of TiO 2 , that is, NaOH or Na 2 CO 3 Isoalkali roasting treatment of titanium-containing blast furnace slag can promote the structural transformation of titanium and strengthen the acid decomposition performance, but the alkali medium circulation cost of this method is high, and the equipment corrosion is serious; (3) it is used to prepare building materials, but due to the titanium-containing blast furnace slag Strong crystallization performance makes the activity of cement poor; (4) Preparation of ferro-titanium and silicon-titanium alloys, but the demand for these alloys is low, which seriously does not match the production of blast furnace slag, and the application of this method is limited
Visible, adopt existing technology to handle titanium-containing blast furnace slag, can appear to be outweighed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for efficient extraction of valuable component titanium from titanium-containing blast furnace slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Weigh a certain mass of blast furnace slag, metal aluminum powder and auxiliary substance NaCl-KCl salt after ball milling, wherein the mass ratio of blast furnace slag to aluminum powder is 14:1, and the mass ratio of blast furnace slag to auxiliary substance salt is 1:1. The molar ratio of NaCl to KCl in the material salt is 1:1; after the raw materials are mixed evenly, pour the mixed material into the molybdenum crucible, and then place the molybdenum crucible containing the material in the high temperature zone of the tubular atmosphere furnace; before heating up, first Use nitrogen to exhaust the air in the furnace tube, then switch the air flow to argon, and raise the temperature to 800°C in an argon atmosphere for 8 hours; after the program ends and the furnace body drops to 50°C, take out the materials; The NaCl-KCl salt in the reduced material was washed away, and then H + Concentration of 1mol / L hydrochloric acid pickling washing material, the volume mass rat...

Embodiment 2

[0033] Weigh a certain mass of milled blast furnace slag, metal aluminum powder and auxiliary substance AlCl 3 -KCl salt, wherein the mass ratio of blast furnace slag to aluminum powder is 9:1, the mass ratio of blast furnace slag to auxiliary substance salt is 1:0.3, and the auxiliary substance salt is AlCl 3 The molar ratio with KCl is 1:1; after the raw materials are mixed evenly, pour the mixed materials into the alumina crucible, and then place the alumina crucible containing the materials in the high temperature zone of the tubular atmosphere furnace; before heating up, first use argon exhaust the air in the furnace tube, and then raise the temperature to 500°C for 3 hours in an argon atmosphere; after the program ends and the furnace body drops to 50°C, take out the material; first use water to reduce the AlCl in the material 3 -KCl salt washed away, then H + The hydrochloric acid pickling washing material with a concentration of 5mol / L, the volume-mass ratio of dilute...

Embodiment 3

[0035] Weigh a certain mass of blast furnace slag, metal magnesium powder and auxiliary substance MgCl after ball milling 2Salt, wherein the mass ratio of blast furnace slag to magnesium powder is 3.5:1, blast furnace slag and MgCl 2 The mass ratio of salt is 1:0.5; after the raw materials are mixed evenly, pour the mixed materials into a stainless steel crucible, and then place the stainless steel crucible containing the materials in the high temperature zone of the tubular atmosphere furnace; Exhaust the air in the tube, then switch to hydrogen, and heat up to 900°C in the hydrogen atmosphere for 0.5h; after the program ends and the furnace body drops to 50°C, switch to argon to exhaust the hydrogen in the furnace tube, and then Take out the material; use H + Concentration is 8mol / L hydrochloric acid acid leaching reducing material, the volume mass ratio of dilute hydrochloric acid and reducing material during acid leaching is 8:1 (mL / g), acid leaching temperature is 100 ℃,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an extraction method of titanium in titanium-containing blast furnace slag. The specific process steps are as follows: crushing titanium-containing blast furnace slag into 106 microns and less, and burdening slag, reducing agent metal powder and auxiliary matter salt according to a certain mass ratio; uniformly mixing materials and reacting in a specific atmosphere, washingto remove salt, and dissolving the titanium through the weak acid, thereby obtaining the acidic solution containing low-valent titanium; oxidizing, hydrolyzing, washing and calcining the titanium-containing acidic solution to acquire titanium dioxide, performing pyrohydrolysis on the hydrolyzed solution through the spray to acquire oxide residue and hydrochloric acid solution, returning the regenerated hydrochloric acid solution to the process of dissolving the titanium. One of the important key point of the invention is to realize the modification on the titanium-containing blast furnace slagthrough the metal thermal recovery process, the acid soluble performance in the weak acid medium is greatly improved, and the titanium can be selectively extracted from the acidic solution through ahydrolysis process.

Description

technical field [0001] The invention belongs to the field of chemical metallurgy and relates to a method for efficiently extracting titanium, a valuable component in titanium-containing blast furnace slag. Background technique [0002] my country is rich in titanium resources, with TiO 2 Totaling 965 million tons, accounting for 38.85% of the world's total reserves, ranking first in the world, of which 90.5% are distributed in the Panzhihua-Xichang area, which is a major national characteristic metal resource. Titanium mainly exists in the form of ilmenite. After beneficiation, about 54% of titanium enters titanium concentrate and becomes the raw material for blast furnace ironmaking; after blast furnace smelting and recovery of Fe and V resources, most of titanium is TiO 2 into blast furnace slag in the form of TiO 2 The content is about 25%, and it coexists with silicon oxide, magnesium oxide, aluminum oxide, etc. TiO in blast furnace slag 2 The content is low, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/04C22B34/12
CPCC22B7/001C22B7/007C22B7/04C22B34/1245C22B34/1259Y02P10/20
Inventor 郑诗礼张盈朱小芳房志刚李庆张洋李平
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products