Environment-friendly and flame-retardant polypropylene material and preparation method thereof

A polypropylene material and flame-retardant technology, which is applied in the field of polypropylene composite material preparation to achieve the effects of preventing migration, short production process and easy availability of raw materials

Inactive Publication Date: 2017-11-24
JIANGSU CHANGHAI COMPOSITE MATERIALS CO LTD
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are very few reports on the simultaneous application of these three materials to flame retardant polypropylene.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] An environmentally friendly flame-retardant polypropylene material, comprising the following components by weight: 100 parts of polypropylene, 0.1 part of modified graphene, 0.5 part of modified carbon nanotubes, 10 parts of aluminum hydroxide, grafted with maleic anhydride 5 parts of polypropylene, 3 parts of SEBS toughening agent, 0.1 part of monophenolic antioxidant, 0.1 part of 1,4-butanediol bis(β-aminobutyroic acid) ester.

[0038] The preparation method of the environment-friendly flame-retardant polypropylene material comprises the following steps:

[0039] (1) Preparation of modified graphene

[0040] Dissolve graphene powder with a sheet thickness of 0.5-5nm in deionized water to prepare a graphene aqueous solution with a concentration of 0.1mg / mL, then add a silane coupling agent for ultrasonic dispersion, and then perform high-speed shear grinding after the dispersion is uniform Processing, promptly obtains modified graphene solution, and described silane c...

Embodiment 2

[0047] An environmentally friendly flame-retardant polypropylene material, comprising the following components by weight: 100 parts of polypropylene, 2 parts of modified graphene, 3 parts of modified carbon nanotubes, inorganic flame retardants (magnesium hydroxide, red phosphorus According to the mass ratio of 1:1 mixed) 20 parts, 10 parts of maleic anhydride grafted polypropylene, 10 parts of SEBS toughening agent, 0.3 parts of antioxidant (bisphenol, triphenol according to the mass ratio of 1:1 mixture) , 0.3 parts of tris(nonylphenyl)phosphite.

[0048] A preparation method of an environmentally friendly flame-retardant polypropylene material, comprising the following steps:

[0049] (1) Preparation of modified graphene

[0050] Dissolve graphene powder with a sheet thickness of 0.5-5nm in deionized water to prepare a graphene aqueous solution with a concentration of 10mg / mL, then add a titanate coupling agent for ultrasonic dispersion, and then undergo high-speed shearin...

Embodiment 3

[0057] An environmentally friendly flame-retardant polypropylene material, comprising the following components by weight: 100 parts of polypropylene, 1 part of modified graphene, 2 parts of modified carbon nanotubes, inorganic flame retardant (ammonium polyphosphate, boric acid 15 parts of zinc according to the mass ratio of 1:1 mixture), 8 parts of polypropylene compatibilizer grafted with maleic anhydride, 6 parts of SEBS toughening agent, 0.2 parts of hydroquinone antioxidant, 1,4-butyl 0.2 part of diol bis(β-aminobutenoic acid) ester heat stabilizer.

[0058] A preparation method of an environmentally friendly flame-retardant polypropylene material, comprising the following steps:

[0059] (1) Preparation of modified graphene

[0060] Get sheet thickness at 0.5~5nm graphene powder and be dissolved in deionized water and be mixed with the graphene aqueous solution that concentration is 5mg / mL, then add surfactant (long-chain alkylamine, polyvinylpyrrolidone according to ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
oxygen indexaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of preparation of polypropylene composite materials, in particular to an environment-friendly and flame-retardant polypropylene composite material. The environment-friendly and flame-retardant polypropylene composite material is prepared from 100 parts of polypropylene, 0.1-2 parts of modified graphene, 0.5-3 parts of modified carbon nano tubes, 10-20 parts of an inorganic flame retardant, 5-10 parts of a compatilizer, 3-10 parts of a toughening agent, 0.1-0.3 parts of an antioxidant and 0.1-0.3 parts of a heat stabilizer. Graphene, the carbon nano tubes and the inorganic flame retardant are added to polypropylene resin, and a brand-new flame retardant system is formed; dispersing performance of graphene in a polymer system is improved through modification of graphene; migration of combustible matter in a polymer matrix can be effectively inhibited; a compact protective carbon layer is formed on the surface of the polymer matrix by graphene in the burning process of the composite material, and finally, the flame-retardant effect is achieved.

Description

technical field [0001] The invention relates to the field of polypropylene composite material preparation, in particular to an environment-friendly, flame-retardant, chlorine- and bromine-free halogen-free polypropylene composite material and a preparation method thereof. Background technique [0002] Polypropylene is a crystalline high polymer with the characteristics of light weight, non-toxic, odorless, etc., and has high mechanical strength. It has better transparency and tensile strength than polyethylene, especially has unique bending characteristics of repeated bending resistance , and thus has been highly supported as a plastic material for replacement vehicle components. In addition, polypropylene is excellent in high rigidity, impact resistance, transparency and high fluidity, and has been widely used not only in the automobile industry but also in household appliances, disposable syringes, transparent containers, cleaning non-woven fabrics, packaging Raw material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08L53/02C08K13/06C08K9/04C08K9/06C08K3/04C08K7/24C08K3/22C08K3/02C08K3/32C08K3/38
CPCC08K2003/026C08K2003/2224C08K2003/2227C08K2003/323C08K2003/387C08K2201/011C08L23/12C08L2201/02C08L2201/22C08L2205/03C08L51/06C08L53/02C08K13/06C08K9/04C08K9/06C08K9/08C08K3/04C08K7/24C08K3/22C08K3/02C08K3/32C08K3/38C08K3/2279
Inventor 李修兵贾革文李韦韦莫剑臣
Owner JIANGSU CHANGHAI COMPOSITE MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com