High-hardness grit powder coating and preparation method thereof

A powder coating, high hardness technology, applied in the direction of powder coating, anti-corrosion coating, polyester coating, etc., can solve the problems of high production cost, low scratch resistance and wear resistance, etc., and achieve easy cleaning, strong decoration and high hardness Effect

Inactive Publication Date: 2017-09-22
浙江绿能塑粉科技股份有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional sand grain powder coating has low scratch and abrasion resistance after film formation, and the current thermosetting sand grain powder coating usually makes the final coating film appear evenly distributed sand grain shape by adding sand grain agent, but the material The production cost is relatively high. In order to reduce the production cost of the thermosetting sand grain powder coating and at the same time make the film have high scratch resistance and wear resistance, it is necessary to propose a high hardness sand grain powder coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The embodiment of the present invention also proposes a method for preparing a high-hardness sand grain powder coating, comprising the following steps:

[0027] S1. Weighing ingredients: Accurately weigh epoxy resin, carboxyl-terminated polyester resin, silicone resin, fluorocarbon resin, methylimidazole, nepheline powder, kaolin, pure polytetrafluoroethylene and pigments according to parts by weight.

[0028] S2. Pre-mixing: Put the weighed raw materials into a high-speed mixer and mix them.

[0029] S3. Melt extrusion: put the mixed and stirred raw materials into a screw extruder to melt and homogenize, and extrude and tablet into semi-finished products.

[0030] S4. Grinding: put the semi-finished product into a grinder and grind it into powder.

[0031] S5. Screening: the powdery semi-finished product is first separated from the ultrafine powder by the separator, and the ultrafine powder is discarded, and then sieved by the sieve according to the particle size requ...

Embodiment 1

[0034] A high-hardness sand grain powder coating, its raw materials include the following components by weight: 30 parts of epoxy resin; 30 parts of carboxyl-terminated polyester resin; 7.5 parts of silicone resin; 7.5 parts of fluorocarbon resin; 0.75 parts of methylimidazole 10 parts of nepheline powder; 7.5 parts of kaolin; 2 parts of pure polytetrafluoroethylene; 1.5 parts of pigment; prepare according to the following steps:

[0035] S1. Weighing ingredients: Accurately weigh epoxy resin, carboxyl-terminated polyester resin, silicone resin, fluorocarbon resin, methylimidazole, nepheline powder, kaolin, pure polytetrafluoroethylene and pigments according to parts by weight.

[0036] S2. Pre-mixing: Put the weighed raw materials into a high-speed mixer and mix them.

[0037] S3. Melt extrusion: put the mixed and stirred raw materials into a screw extruder to melt and homogenize, and extrude and tablet into semi-finished products.

[0038] S4. Grinding: put the semi-finishe...

Embodiment 2

[0042] A high-hardness sand grain powder coating, its raw materials include the following components in parts by weight: 25 parts of epoxy resin; 25 parts of carboxyl-terminated polyester resin; 5 parts of organic silicon resin; 5 parts of fluorocarbon resin; 5 parts; 5 parts of nepheline powder; 5 parts of kaolin; 1 part of pure polytetrafluoroethylene;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-hardness grit powder coating. The raw material of the high-hardness grit powder coating is prepared from the following components in parts by weight: 25-35 parts of epoxy resin, 25-35 parts of terminal carboxyl polyester resin, 5-10 parts of organosilicon resin, 5-10 parts of fluorocarbon resin, 0.5-1 part of methylimidazole, 5-15 parts of nepheline powder, 5-10 parts of kaolin, 1-3 parts of pure polytetrafluoroethylene and 1-2 parts of pigments. The invention also provides a preparation method of the high-hardness grit powder coating. The preparation method of the high-hardness grit powder coating comprises the steps of weighing and preparing materials, premixing, melting and extruding, grinding, screening and packing finished product to obtain the high-hardness grit powder coating. According to the high-hardness grit powder coating and the preparation method thereof, the crosslinking density of the resin during reacting, the hardness of the fillers and the smoothness of additives are increased, so that the hardness of the coating surface is improved; the production cost is reduced; meanwhile, the uniformly distributed grit shape is formed in the surface of the film cured by the coating; the coating is high in decorativeness; the defects such as roughness and unevenness of the surface and the like can be remedied and covered.

Description

【Technical field】 [0001] The invention relates to the technical field of powder coatings, in particular to a high-hardness sand grain powder coating and a preparation method thereof. 【Background technique】 [0002] Powder coating exists in the state of fine powder. It is a new type of solvent-free 100% solid powder coating. It is solvent-free, pollution-free, recyclable, environmentally friendly, saves energy and resources, reduces labor intensity and mechanical strength of the coating film. advanced features. The powder coating is sprayed on the surface of the coated object in powder form, melted and leveled by baking, and solidified to form a film. Due to the advantages of improving coating performance, reducing costs, and eliminating the generation of volatile organic compounds, powder coatings have been continuously and rapidly developed. [0003] Thermosetting sand texture powder coatings not only have many advantages of general thermosetting powder coatings, but also...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D167/00C09D5/03C09D5/16C09D5/08C09D7/12
CPCC09D163/00C08K2201/003C08K2201/011C08L2201/08C08L2205/025C08L2205/035C08L2312/00C09D5/031C09D5/032C09D5/033C09D5/08C09D5/1637C09D5/1687C09D167/00C08L63/00C08L67/00C08L83/04C08L27/12C08L27/18C08K3/34C08K3/346
Inventor 范若谷周光阳徐锦丽江红兵丁武轩周天明徐能峰张爱华杨建芬
Owner 浙江绿能塑粉科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com