A kind of polymer material surface modification method and its product and application

A polymer material and surface modification technology, applied in the field of biomimetic modification, can solve the problems of cumbersome grafting process, complex and cumbersome operation process, and difficulty in realization, and achieve the effect of improving the physical and chemical properties of the surface and eliminating the restriction of sight

Active Publication Date: 2020-05-22
SHENZHEN INST OF ADVANCED TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the use of wet chemical cross-linking technology is not only relatively complicated and cumbersome to operate, but also introduces toxic organic cross-linking reagents
More importantly, this chemical method is difficult to graft multiple bioactive molecules on the surface at the same time, and the sequential grafting of multiple biomolecules will make the grafting process extremely cumbersome or even difficult to achieve.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer material surface modification method and its product and application
  • A kind of polymer material surface modification method and its product and application
  • A kind of polymer material surface modification method and its product and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A polytetrafluoroethylene sheet with a diameter of 15 mm and a thickness of 0.1 mm was ultrasonically cleaned with acetone, alcohol, and deionized water in sequence. This pretreated sample is called PTFE control.

[0056] The pretreated PTFE was treated by gas plasma immersion ion implantation technology. Use nitrogen injection, ammonia injection, or nitrogen injection followed by ammonia injection for treatment. The specific treatment process is: the background vacuum is 5×10 -3 Pa, the flow rate of the gas introduced is 30 sccm, the negative bias applied to the sample disk is 15 kV, the injection pulse width is 20 microseconds, the injection pulse frequency is 500 Hz, and the radio frequency power is 1000 W. Wherein, the injection time of nitrogen is 180 minutes, and the sample after this treatment is called N2PIII; The injection time of ammonia is 60 minutes, and the sample after this treatment is called NH3PIII; After injecting nitrogen 180 minutes, inject ammonia...

Embodiment 2

[0059] Using an atomic force microscope to characterize the surface roughness of the polytetrafluoroethylene sample processed in Example 1, the surface three-dimensional picture, section profile and corresponding mean square roughness (RMS) results shown in Figure 2 were obtained. From the three-dimensional image of the surface in Figure 2, it can be seen that the results obtained by the atomic force microscope are basically consistent with the surface morphology obtained by the scanning electron microscope in Example 1. Figure 2a The surface mean square roughness of the PTFE control shown is 17.9nm. Nitrogen plasma injection significantly increased the surface roughness of the sample to 134nm ( Figure 2b ). Ammonia plasma injection has basically no effect on the surface roughness, and the mean square roughness after treatment is 18.2nm ( Figure 2c ). The mean square roughness of the surface after nitrogen plasma injection and ammonia gas injection is basically the same ...

Embodiment 3

[0061] Carry out X-ray photoelectron energy spectrum (XPS) wide-field scanning to the polytetrafluoroethylene sample surface that processing obtains in embodiment 1, obtain image 3 The XPS full-spectrum spectrum is shown. The abscissa represents the binding energy, and the ordinate represents the peak intensity. By observing image 3 The peak heights of the C 1s peak, O 1s peak, N 1s peak and F 1s peak of each sample in the sample show that the nitrogen plasma immersion ion implantation treatment reduces the fluorine element content on the surface of PTFE to a certain extent, and in the material Oxygen was introduced into the surface; and ammonia plasma immersion ion implantation treatment significantly reduced the content of surface fluorine, and significantly increased the proportion of surface nitrogen and oxygen.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
elastic modulusaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

Disclosed are a polymer material surface modification method, and a product and a use thereof. The surface modification method particularly relates to treating the surface of a medical polymer material on the basis of plasma immersion ion implantation and covalently grafting bioactive molecules onto the treated surface to realize biomimetic modification of the material. The method specifically comprises the following steps: 1) treating a polymer material by gas plasma immersion ion implantation; and 2) incubating the treated polymer material in a solution containing biomolecules. The polymer material with the surface modified by gas plasma immersion ion implantation has good stability, and the grafting ability thereof does not significantly decrease even if the material is exposed to the air for a long time, and a chemical crosslinking agent is not used in the method. The entire surface modification process is simple and has low cost, making it suitable for batch and industrial production. The method and product thereof have broad application prospects in the fields of medical implant materials, functional materials, and bioactive materials.

Description

technical field [0001] The present invention relates to a method for surface modification of polymer materials and its products and applications. The surface modification method especially relates to the treatment of the surface of medical polymer materials based on plasma immersion ion implantation and the covalent grafting of biological substances on the surface after treatment. Active molecules to achieve their biomimetic modification. Background technique [0002] Polymer materials, also known as polymer materials, are widely used in the biomedical field for the repair, replacement and regeneration of biological tissues, as well as for nursing and medical appliances. Because of its special application environment (requires direct contact with body fluids, blood, organs, tissues, etc.), biomedical polymer materials must have good physical and mechanical properties, chemical stability, non-toxicity, and easy processability. It must also have biocompatibility, medical func...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/12C08L27/18C08L61/16
CPCC08J7/12C08J2327/18C08J2361/16
Inventor 王怀雨高昂朱剑豪
Owner SHENZHEN INST OF ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com