Application of polymerizable deep-eutectic solvents to preparing transparent conductive elastomers

A low eutectic solvent, transparent conductive technology, applied in the field of ionic liquids, can solve the problems of reduced conductivity, poor conductivity, high price of nanoparticles, and achieve the effects of low cost, low pollution and simple preparation method

Active Publication Date: 2017-09-19
广州纽楷美新材料科技有限公司
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the difference in elastic modulus between the nano-conductive particles and the polymer, the conductive performance of the prepared elastic conductive material becomes poor during the long-term folding cycle; the same nano-conductive particles are easy to react with various substances in the air to reduce the conductivity. And the price of nanoparticles is higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of polymerizable deep-eutectic solvents to preparing transparent conductive elastomers
  • Application of polymerizable deep-eutectic solvents to preparing transparent conductive elastomers
  • Application of polymerizable deep-eutectic solvents to preparing transparent conductive elastomers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A transparent conductive elastomer, the preparation process is as follows:

[0032] S1: Preparation of a polymerizable deep eutectic solvent: 13.96 g of hydrogen bond acceptor choline chloride and 14.41 g of hydrogen bond donor acrylic acid were stirred and reacted at 90° C. for 4 h to obtain a clear and transparent polymerizable deep eutectic solvent.

[0033] S2: Preparation of transparent conductive elastomer prepolymer mixed solution: 0.34g of polyethylene glycol diacrylate, 0.57g of 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone Mix evenly with the deep eutectic solvent, stir and react for 2 hours to obtain a transparent conductive elastomer prepolymer mixed solution.

[0034] S3: Preparation of conductive elastomer: take 2.83ml of the transparent conductive elastomer prepolymer mixed solution described in step S2, pour it into a polytetrafluoroethylene petri dish (radius 3cm), and cure it under ultraviolet light (2Kw) for 8s to obtain a transparent conducti...

Embodiment 2

[0036] A transparent conductive elastomer, the preparation process is as follows:

[0037] S1: Preparation of a polymerizable deep eutectic solvent: 13.96 g of hydrogen bond acceptor choline chloride and 14.41 g of hydrogen bond donor acrylic acid were stirred and reacted at 90° C. for 4 h to obtain a clear and transparent polymerizable deep eutectic solvent.

[0038] S2: Preparation of transparent conductive elastomer prepolymer mixed solution: 0.68g of polyethylene glycol diacrylate, 0.58g of 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone Mix evenly with the deep eutectic solvent, stir and react for 2 hours to obtain a transparent conductive elastomer prepolymer mixed solution.

[0039] S3: Preparation of conductive elastomer: take 2.83ml of the transparent conductive elastomer prepolymer mixed solution described in step S2, pour it into a polytetrafluoroethylene petri dish (radius 3cm), and cure it under ultraviolet light (2Kw) for 8s to obtain a transparent conducti...

Embodiment 3

[0041] A transparent conductive elastomer, the preparation process is as follows:

[0042] S1: Preparation of a polymerizable deep eutectic solvent: 13.96 g of hydrogen bond acceptor choline chloride and 14.41 g of hydrogen bond donor acrylic acid were stirred and reacted at 90° C. for 4 h to obtain a clear and transparent polymerizable deep eutectic solvent.

[0043]S2: Preparation of transparent conductive elastomer prepolymer mixed solution: 1.02 of polyethylene glycol diacrylate, 0.59 g of 2-hydroxy-4'-(2-hydroxyethoxy)-2-methyl propiophenone and The deep eutectic solvent was mixed evenly, and stirred and reacted for 2 hours to obtain a transparent conductive elastomer prepolymer mixed solution.

[0044] S3: Preparation of conductive elastomer: take 2.83ml of the transparent conductive elastomer prepolymer mixed solution described in step S2, pour it into a polytetrafluoroethylene petri dish (radius 3cm), and cure it under ultraviolet light (2Kw) for 8s to obtain a transpa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses application of polymerizable deep-eutectic solvents to preparing transparent conductive elastomers. Hydrogen bond receptors and hydrogen bond donors are mixed with one another at the temperatures of 60-100 DEG C to obtain the polymerizable deep-eutectic solvents, a molar ratio of the hydrogen bond donors to the hydrogen bond receptors is not smaller than 1:1, and the hydrogen bond donors comprise acrylic acid or methacrylic acid. The polymerizable deep-eutectic solvents, cross-linking agents and photoinitiators are mixed with one another to obtain mixed solution, and the mixed solution can be cured in polytetrafluoroethylene culture dishes under ultraviolet irradiation to obtain the transparent conductive elastomers. The application has the advantage that the transparent conductive elastomers are high in light transmission and conductivity, excellent in tensile property and bendability and good in environmental stability.

Description

technical field [0001] The invention relates to the field of ionic liquids, in particular, the invention relates to the application of a polymerizable deep eutectic solvent in preparing transparent conductive elastomers. Background technique [0002] Deep eutectic solvents are a subset of ionic liquids. On the basis of inheriting the advantages of ionic liquids such as low vapor pressure, non-aqueous biocompatibility, non-flammability, chemical stability, and high solubility, they also have low cost and low toxicity. , 100% atom utilization and environmental friendliness in the preparation process, and is expected to replace ionic liquids in the future. At present, deep eutectic solvents are mainly used in such aspects as capturing carbon dioxide, dissolving metal oxides, dissolving drugs and purification, catalysts, electrodeposition, material preparation and processing biopolymers. However, there are relatively few reports on polymerizable deep eutectic solvents in the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/06C08F220/06C08F222/20C08F222/14
CPCC08F220/06C08F283/065C08F222/20C08F222/14
Inventor 何明辉李仁爱苏彬崔艳艳
Owner 广州纽楷美新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com