Wear-resistant antibacterial cable material

A cable material and wear-resistant powder technology, applied in plastic/resin/wax insulators, organic insulators, etc., can solve the problem that conventional cables cannot meet the requirements of wear resistance, and achieve convenient and effortless cutting, good mechanical processing performance, good Antibacterial effect

Inactive Publication Date: 2017-03-29
ANHUI YILI CABLE
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For some special industries, cables need to be used on heavy machinery, and they need to move continuously with the equipment and keep in contact with the ground and wall lights. Conventional cables cannot meet their wear resistance requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A wear-resistant and antibacterial cable material, which is composed of the following raw materials in parts by weight: 50 parts of halogen-free flame-retardant polyolefin, 4 parts of silicon carbide, 3 parts of antioxidant, 2 parts of smoke suppressant, 5 parts of aluminum hydroxide, hydrogen 3 parts of magnesium oxide, 1 part of γ-ray absorber, 2 parts of zinc oxide, 3 parts of nano-barium sulfate, 1 part of heat stabilizer, 3 parts of calcium-zinc composite stabilizer, 2 parts of impact modifier, 1 part of ultraviolet absorber , 4 parts of carbon fiber, 3 parts of coupling agent, 0.3 part of anti-aging agent, and 8 parts of modified filler.

[0020] The modified filler is made of the following raw materials in parts by weight: 5-8 parts of 3,5-tertiary butyl-4-hydroxyphenyl, 1-2 parts of alum, 3-4 parts of vegetable oil, 3-4 parts of magnetite 5 parts, 1-3 parts of zinc borate, 2.5-4.5 parts of nano-alumina, 2-4 parts of aluminum polyphosphate, 4-6 parts of nano-tita...

Embodiment 2

[0023] A wear-resistant and antibacterial cable material, which is composed of the following raw materials in parts by weight: 60 parts of halogen-free flame-retardant polyolefin, 10 parts of silicon carbide, 8 parts of antioxidant, 6 parts of smoke suppressant, 8 parts of aluminum hydroxide, hydrogen 6 parts of magnesium oxide, 3 parts of gamma ray absorber, 5 parts of zinc oxide, 7 parts of nano barium sulfate, 5 parts of heat stabilizer, 8 parts of calcium zinc composite stabilizer, 4 parts of impact modifier, 2 parts of ultraviolet absorber , 6 parts of carbon fiber, 5 parts of coupling agent, 0.8 part of anti-aging agent, and 12 parts of modified filler.

[0024] The modified filler is made of the following raw materials in parts by weight: 5-8 parts of 3,5-tertiary butyl-4-hydroxyphenyl, 1-2 parts of alum, 3-4 parts of vegetable oil, 3-4 parts of magnetite 5 parts, 1-3 parts of zinc borate, 2.5-4.5 parts of nano-alumina, 2-4 parts of aluminum polyphosphate, 4-6 parts of ...

Embodiment 3

[0027] A wear-resistant and antibacterial cable material, which is composed of the following raw materials in parts by weight: 55 parts of halogen-free flame-retardant polyolefin, 7 parts of silicon carbide, 5 parts of antioxidant, 4 parts of smoke suppressant, 7 parts of aluminum hydroxide, hydrogen 4.5 parts of magnesium oxide, 2 parts of gamma ray absorber, 3.5 parts of zinc oxide, 5 parts of nano barium sulfate, 3 parts of heat stabilizer, 5 parts of calcium zinc composite stabilizer, 3 parts of impact modifier, 1.5 parts of ultraviolet absorber , 5 parts of carbon fiber, 4 parts of coupling agent, 0.6 part of anti-aging agent, and 10 parts of modified filler.

[0028] The modified filler is made of the following raw materials in parts by weight: 5-8 parts of 3,5-tertiary butyl-4-hydroxyphenyl, 1-2 parts of alum, 3-4 parts of vegetable oil, 3-4 parts of magnetite 5 parts, 1-3 parts of zinc borate, 2.5-4.5 parts of nano-alumina, 2-4 parts of aluminum polyphosphate, 4-6 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resistant antibacterial cable material which is composed of the following raw materials in parts by weight: 50-60 parts of halogen-free flame-retardant polyolefin, 4-10 parts of silicon carbide, 3-8 parts of antioxidant, 2-6 parts of smoke suppressor, 5-8 parts of aluminum hydroxide, 3-6 parts of magnesium hydroxide, 1-3 parts of gamma-ray absorbent, 2-5 parts of zinc oxide, 3-7 parts of nano barium sulfate, 1-5 parts of heat stabilizer, 3-8 parts of calcium zinc composite stabilizer, 2-4 parts of impact modifier, 1-2 parts of ultraviolet absorbent, 4-6 parts of carbon fiber, 3-5 parts of coupling agent, 0.3-0.8 part of anti-aging agent and 8-12 parts of modified filler. The cable material has the advantages of high safety, environment friendliness, high wear resistance, high antibacterial property, short biodegradation period, low production cost, high economic value and very wide prospects; and the dimagnetic property, water resistance, high temperature resistance and chemical corrosion resistance are obviously higher than those of the common cable material.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a wear-resistant and antibacterial cable material. Background technique [0002] Wires and cables include bare wires, wires and cables for electrical equipment, power cables, communication cables and optical cables, and winding wires. Cable materials are commonly known as plastics for wire and cable insulation and sheathing. The polymer materials used mainly include polyvinyl chloride, polyethylene, Polypropylene, fluoroplastics, chlorinated polyether and polyamide, etc. These polymer materials have the characteristics of light weight, chemical corrosion resistance, easy processing and molding, excellent electrical insulation performance, and excellent mechanical and fatigue resistance properties. [0003] For some special industries, cables need to be used on heavy machinery, and they need to move continuously with the equipment and keep in contact with the ground and wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L83/04C08L77/10C08L1/04C08L5/08C08K13/06C08K9/00C08K5/098C08K3/34C08K9/12C08K3/08C08K3/30C08K7/08C08K3/04C08K3/38C08K3/22C08K3/32H01B3/44
CPCC08L27/06C08K2201/011C08K2201/014C08L2201/02C08L2201/06C08L2201/08C08L2203/202C08L2205/035C08L2205/16H01B3/443
Inventor 毕力高敏陈鹏刘勇
Owner ANHUI YILI CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com