Mineral crystal fancy glaze capable of releasing negative ions and ceramic tile produced by using mineral crystal fancy glaze

A technology of mineral crystals and ceramic bricks, applied in the field of ceramic bricks, can solve the problems of deformation of the green body and the overall performance is not optimal, and achieve the effect of increasing the electrostatic voltage difference

Inactive Publication Date: 2017-02-15
GUANGDONG KITO CERAMICS GROUP CO LTD
View PDF9 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the main component of tourmaline powder is a silicate material with a ring structure of aluminum, sodium, iron, and lithium, which is characterized by boron, a large amount of introduction into the green body will cause deformation of the green body, and introduction into the glaze will also cause It will have a certain impact on the characteristics of the glaze, especially for transparent glazes, so although there are related functional products, the overall performance is not optimal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral crystal fancy glaze capable of releasing negative ions and ceramic tile produced by using mineral crystal fancy glaze
  • Mineral crystal fancy glaze capable of releasing negative ions and ceramic tile produced by using mineral crystal fancy glaze
  • Mineral crystal fancy glaze capable of releasing negative ions and ceramic tile produced by using mineral crystal fancy glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment provides a kind of mineral crystal floral glaze, which is calculated in parts by mass and includes the following components:

[0036] 100 parts of dry mineral crystals, 0-50 parts of transparent glaze, 60-80 parts of printing paste, 0.2 parts of carboxymethyl cellulose, 25-40 parts of water,

[0037] The chemical components of the dry mineral crystal particles are calculated in parts by weight of oxides, and include the following components:

[0038] SiO 2 : 8 servings, Al 2 o 3 : 3 copies, B 2 o 3 : 20 parts, Fe 2 o 3 : 9 parts, MnO: 46 parts, TiO 2 : 8 servings.

[0039] Here transparent glaze selects ceramics to produce known transparent glaze for use and gets final product. The mineral crystal dry particles provided by the present invention contain a large amount of iron, manganese and titanium elements, and there will be multiple changes under different firing conditions and basic glaze components, especially in the way of combining with gl...

Embodiment 2

[0041] This embodiment provides a process for producing ceramics using the mineral crystal flower glaze provided in Embodiment 1.

[0042] A kind of ceramic tile production technology, it comprises the steps:

[0043] Step 1) Selecting known ceramic body powder to be stamped into brick adobe;

[0044] Step 2) applying a known top glaze on the surface of the green body by glazing to form a top glaze layer;

[0045] Step 3) printing on the glaze layer to form a printing layer;

[0046] Step 4) applying protective glaze on the surface of the printing layer;

[0047] Step 5) distributing the mineral crystal flower glaze, the mineral crystal flower glaze is calculated in parts by mass, and includes the following components: 100 parts of mineral crystal dry particles, 0-50 parts of transparent glaze, 60-80 parts of printing paste, and 0.2 parts of carboxymethyl cellulose parts, 25-40 parts of water, the chemical components of the dry mineral crystal grains are calculated in parts...

Embodiment 3

[0054] A kind of ceramic tile, its structure from bottom to top is as follows: including body layer, surface glaze layer, whitening glaze layer, printing pattern layer, powder-increasing flower glaze layer, color-helping flower glaze layer, protective glaze layer and mineral Crystal flower glaze layer.

[0055] Its preparation process comprises the following steps:

[0056] The present invention also provides a kind of production technology of ceramic brick, and it comprises the steps:

[0057] Step 1) raw materials for billet are prepared by batching and ball milling to obtain slurry, then iron removal, sieving, stale, spray milling and then sieving to obtain billet;

[0058] Step 2) Pressing and molding the blank by a press to prepare the blank;

[0059] Step 3) putting green body into drying kiln for drying;

[0060] Step 4) apply the surface glaze by glazing;

[0061] Step 5) adopt screen printing whitening glaze to carry out whitening;

[0062] Step 6) Carry out deco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention provides a mineral crystal fancy glaze capable of releasing negative ions and a ceramic tile produced by using the mineral crystal fancy glaze. The mineral crystal fancy glaze capable of releasing the negative ions is prepared from the following components in parts by mass: 100 parts of mineral crystal dry pellets, 0 to 50 parts of transparent glaze, 1 to 3 parts of tourmaline powder, 0.01 to 0.05 part of light rare earth oxide, 60 to 80 parts of printing paste, 0.2 part of carboxymethylcellulose and 25 to 40 parts of water; the mineral crystal dry pellets are prepared from the following chemical components in parts by weight of oxides: 8 parts of SiO2, 3 parts of Al2O3, 20 parts of B2O3, 9 parts of Fe2O3, 46 parts of MnO and 8 parts of TiO2. The fancy glaze contains a large amount of color development oxides, the small amount of tourmaline powder and the trace amount of light rare earth oxides; electrostatic voltage difference of the fancy glaze can be improved; a higher release effect of the negative ions is realized at less dosage. The ceramic tile produced by using the mineral crystal fancy glaze capable of releasing the negative ions can release the negative ions.

Description

technical field [0001] The invention relates to the field of building ceramics production, in particular to a mineral crystal flower glaze capable of releasing negative ions and ceramic tiles prepared therefrom. Background technique [0002] Negative ions are negatively charged gas ions in the air. The various gas components in the atmosphere do not exist completely in the form of molecules, but some of them exist in the free state of ions. Among them, negatively charged molecules or particles (commonly known as negative ions) can not only promote the synthesis and storage of vitamins in the human body, strengthen and activate the physiological activities of the human body, but also have a very important impact on the life activities of the human body and other organisms, so it is also called "air". Vitamins". [0003] Ceramic tiles are commonly used building materials for home decoration. Combining them can release negative ions to adjust indoor air quality and improve co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/04C03C8/14C04B41/89
CPCC03C8/04C03C8/14C03C8/20C03C2204/02C04B41/52C04B41/89C04B41/5022C04B41/4572
Inventor 戴永刚喻劲军钟礼丰李德英
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com