Kaolin-modified mildew-resistant paperboard paint and preparation method thereof
A kaolin and modified technology, applied in the field of coatings, can solve the problems of destroying the waterproof effect of the coating layer, reducing the mechanical strength of the carton, and degrading the product quality.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0015] The invention provides a kind of preparation method based on kaolin modified anti-mildew cardboard coating, comprising:
[0016] 1) The process of decocting Chinese herbal medicines in water to obtain Chinese herbal medicine extracts;
[0017] 2) In the presence of ultraviolet rays, the process of activating kaolin, plant ash, sodium chloroplatinate and molybdenum disulfide to obtain an activated product;
[0018] 3) Under acidic conditions, the process of mixing the activator with the amino acid and performing modification treatment to obtain the modified activator;
[0019] 4) Conduct a contact reaction of acrylic emulsion, polystyrene, dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and then add emulsifiers, modified activators, and Chinese herbal medicine extracts to the reaction system The process of mixing the liquid to obtain a kaolin-modified anti-mildew cardboard coating;
[0020] Among them, Chinese herbal medicines include mugwort leaf,...
Embodiment 1
[0033] 1) Take mugwort leaf, yam, borneol, honeysuckle vine, Chuanxiong, Tongcao, angelica, kudzu root, Trichosanthes bark, Coptis chinensis, and water according to the ratio of 100:52:48:39:28:77:42:31:36:92:500 Mixed by weight, and decocted at 160°C for 5 hours to obtain Chinese herbal medicine extract;
[0034] 2) In the presence of ultraviolet rays with a wavelength of 230nm, kaolin, plant ash, sodium chloroplatinate and molybdenum disulfide were mixed in a weight ratio of 100:62:19:37, and activated at 80°C for 14 hours to obtain an activated product;
[0035] 3) Under the condition of pH 5, the activated substance was mixed with amino acid (weight ratio 100:55) and modified at 55°C for 8 hours to obtain the modified activated substance;
[0036] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight: 5000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and mix them at 100°C and a vacuum of 8MPa The contact reaction was carried out a...
Embodiment 2
[0039] 1) Take mugwort leaf, yam, borneol, honeysuckle, chuanxiong, Tongcao, angelica, kudzu root, melon skin, coptis, and water according to the ratio of 100:45:42:36:24:74:36:22:29:88:400 Mixed in weight ratio, and decocted at 150°C for 4 hours to obtain Chinese herbal medicine extract;
[0040] 2) In the presence of ultraviolet light with a wavelength of 200nm, kaolin, plant ash, sodium chloroplatinate and molybdenum disulfide were mixed in a weight ratio of 100:55:14:32, and activated at 75°C for 12 hours to obtain an activated product;
[0041] 3) Under the condition of pH 4, the activated substance was mixed with amino acid (weight ratio 100:47) and then modified at 50°C for 6 hours to obtain the modified activated substance;
[0042] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight: 3000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and mix them at 95°C and a vacuum of 5MPa The contact reaction was carried out for 1 h, and th...
PUM
Property | Measurement | Unit |
---|---|---|
wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com