Medium corrosion-resistant fluorubber sealing gasket and production method thereof

A technology of fluororubber and sealing gasket, which is applied in the field of medium corrosion resistant fluororubber sealing gasket and its preparation, can solve the problems of short service life, poor medium corrosion resistance, etc., and achieve excellent wear resistance and outstanding effect of medium corrosion resistance

Inactive Publication Date: 2016-11-09
HUAINAN CAOAN RUNLONG PLASTIC CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of science and technology and industry, the performance requirements of fluororubber sealing materials are getting higher and higher. The existing fluororubber gaskets on the market have the disadvantage of poor corrosion resistance to medium, which leads to their short service life and cannot meet the needs of the market. needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medium corrosion-resistant fluorubber sealing gasket and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A medium corrosion-resistant fluororubber gasket, made of the following raw materials by weight (kg): perfluoroether rubber 40, neoprene rubber 30, bisphenol AF 6, white ointment 7, thioisobutyramide 3, calcium Nepheline powder 24, asbestos wool 18, double peroxy carbamate 4, colloidal graphite powder 16, tetraethylamine chloride 4, C5 petroleum resin 8, pentachlorobiphenyl 5, carbon black N990 25, 2,2'- Methylenebis(4-ethyl-6-tert-butylphenol) 2.5, N-phenyl-2-naphthylamine 1.5, modifier 17;

[0016] The preparation method of described modifying agent is as follows: (1) get the raw material of following weight (kg): blast furnace water-quenched slag 18, titanium carbide 16, aluminum magnesium spinel 12, silicon boride 12, cocoyl methyl boron Sodium Sulfonate 2.5, Lauryl Phosphate Betaine 2, Glucosaminoglycan 1.5, Tallow Amine Polyoxyethylene Ether 6, Jojoba Acid Polyoxypropylene Ester 4.5, Sorbitol Polyoxyethylene Ether Tetraoleate 3; (2) Take blast furnace water-quenc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a medium corrosion-resistant fluorubber sealing gasket and a production method thereof. The sealing gasket is produced from, by weight, 30-50 parts of perfluoroether rubber, 20-40 parts of chloroprene rubber, 4-8 parts of bisphenol AF, 6-9 parts of white factice, 2-4 parts of thioisobutyramide, 19-33 parts of cancrinite powder, 12-24 parts of asbestos wool, 4-5 parts of diperoxocarbamate, 15-20 parts of colloid graphite powder, 3-5 parts of tetraethylammonium chloride, 7-11 parts of C5 petroleum resin, 4-6 parts of 1,2,3,4,5-pentachlorobibenzene, 20-30 parts of carbon black N990, 2-3 parts of 2,2'-methylenebis(4-ethyl-6-tert-butyl phenol), 1-2 parts of N-phenyl-2-naphthylamine and 15-20 parts of a modifier. The sealing gasket produced in the invention has the advantages of very protruding medium corrosion resistance, resistance to oil, acids, alkalis, salts, ethers, alcohols, water vapor and other corrosive media, and excellent wear, ageing and high temperature resistance.

Description

technical field [0001] The invention relates to a rubber sealing gasket, in particular to a medium corrosion resistant fluorine rubber sealing gasket and a preparation method thereof. Background technique [0002] Fluorine rubber (fluororubber) refers to a synthetic polymer elastomer containing fluorine atoms on the carbon atoms of the main chain or side chain. The introduction of fluorine atoms endows rubber with excellent heat resistance, oxidation resistance, oil resistance, corrosion resistance and atmospheric aging resistance, and has been widely used in the field of sealing materials. With the rapid development of science and technology and industry, the performance requirements of fluororubber sealing materials are getting higher and higher. The existing fluororubber gaskets on the market have the disadvantage of poor corrosion resistance to medium, which leads to their short service life and cannot meet the needs of the market. demand. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/18C08L11/00C08L57/02C08K13/08C08K11/00C08K9/04C08K3/22C08K3/14C08K3/38C08K3/04C08K7/12C08K3/34
CPCC08K2201/014C08L27/18C08L2201/08C08L2205/035C08L11/00C08L57/02C08K13/08C08K11/005C08K9/04C08K3/22C08K3/14C08K3/38C08K3/04C08K7/12C08K3/34
Inventor 徐良建张群
Owner HUAINAN CAOAN RUNLONG PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products