Porous foamy copper material and production method thereof

A technology of porous foam and bronze powder, applied in the field of foam materials, can solve the problems of high cost, narrow range of material selection, complicated process, etc., and achieve high platform stress, high porosity, and good mechanical properties

Inactive Publication Date: 2016-08-24
陈昌
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on metal foam mainly focuses on metal foam with low density and high porosity, but metal foam with high porosity has the disadvantages of complex process, narrow material selection range and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous foamy copper material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A porous copper foam material, which is prepared from the following components in parts by weight: 15 parts of polyurethane sponge, 5 parts of bronze powder, 0.2 part of sodium dodecylbenzenesulfonate, 0.5 part of phosphatidylcholine, p-hydroxybenzoic acid 0.1 part of methyl ester, 0.1 part of sodium diacetate, 0.5 part of polyvinyl alcohol, 0.2 part of polyvinyl formal, 0.1 part of glyceryl tristearate, 1 part of sodium hydroxide, 0.1 part of rosin, 0.2 part of methyl cellulose , 2 parts of ethanol, 0.3 parts of ammonia water, and 40 parts of water.

[0018] The preparation method of the above-mentioned porous copper foam material is as follows: (1) Mix and soak polyurethane sponge, sodium hydroxide and 25 parts of water for 1 hour; (2) Mix all the remaining components and stir for 3 minutes with a mixer at a speed of 80r / min Form a slurry and let it stand at room temperature for 23 hours; (3) Put the sponge into the slurry and impregnate it repeatedly 3 times, and dry...

Embodiment 2

[0020] A porous copper foam material, prepared from the following components in parts by weight: 17 parts of polyurethane sponge, 8 parts of bronze powder, 0.3 part of sodium dodecylbenzenesulfonate, 0.75 part of phosphatidylcholine, p-hydroxybenzoic acid 0.15 parts of methyl ester, 0.2 parts of sodium diacetate, 0.75 parts of polyvinyl alcohol, 0.35 parts of polyvinyl formal, 0.15 parts of glyceryl tristearate, 1.5 parts of sodium hydroxide, 0.2 parts of rosin, 0.3 parts of methyl cellulose , 3 parts of ethanol, 0.5 parts of ammonia water, and 60 parts of water.

[0021] The preparation method of the above-mentioned porous copper foam material is as follows: (1) Mix and soak polyurethane sponge, sodium hydroxide and 32 parts of water for 1.5 hours; (2) Mix all the remaining components and stir for 4 minutes with a mixer at a speed of 90r / min Form a slurry and let it stand at room temperature for 24 hours; (3) Put the sponge into the slurry and impregnate it repeatedly 4 times...

Embodiment 3

[0023] A porous copper foam material, prepared from the following components in parts by weight: 20 parts of polyurethane sponge, 10 parts of bronze powder, 0.4 part of sodium dodecylbenzenesulfonate, 1 part of phosphatidylcholine, p-hydroxybenzoic acid 0.2 parts of methyl ester, 0.3 parts of sodium diacetate, 1 part of polyvinyl alcohol, 0.5 parts of polyvinyl formal, 0.2 parts of glyceryl tristearate, 2 parts of sodium hydroxide, 0.3 parts of rosin, 0.4 parts of methyl cellulose , 4 parts of ethanol, 0.8 parts of ammonia water, and 80 parts of water.

[0024] The preparation method of the above-mentioned porous copper foam material is as follows: (1) mix and soak polyurethane sponge, sodium hydroxide and 40 parts of water for 2 hours; (2) mix all the remaining components, and stir for 5 minutes with a mixer at a speed of 100r / min Form a slurry and let it stand at room temperature for 25 hours; (3) Put the sponge into the slurry and impregnate it repeatedly 5 times, and dry i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a porous foamy copper material and a production method thereof. The porous foamy copper material is prepared from the following components: polyurethane sponges, bronzing powder, sodium dodecylbenzene sulfonate, phosphatidylcholine, methyl 4-hydroxybenzoate, sodium diacetate, polyvinyl alcohol, polyvinyl formal, tristearin, sodium hydroxide, colophony, methyl cellulose, ethyl alcohol, an ammonia solution, and water. The porous foamy copper material is prepared through the following steps of (1) mixing and soaking the polyurethane sponges, the sodium hydroxide and the water; (2) mixing all the remaining components, stirring the mixed components with a stirrer so as to form pulp, and leaving the pulp to stand at room temperature; (3) putting the processed sponges into the pulp for repeated infiltration, and drying the sponges after the infiltration in the air to form a foamy body biscuit; and (4) putting foamy bodies under high vacuum so that copper oxide is decomposed, and performing sintering so as to obtain the porous foamy copper material. The porous foamy copper material disclosed by the invention is high in porosity factor, high in apparent density, and rough in surfaces; besides, the porous foamy copper material disclosed by the invention has a high plateau stress, so that the mechanical property is good.

Description

technical field [0001] The invention relates to the field of foam materials, in particular to a porous copper foam material and a preparation method thereof. Background technique [0002] With the rapid development of my country's economy and technology, the development of the material industry is also showing vigorous growth. Among them, porous metal is a new type of engineering material with a functional structure that has developed rapidly in recent years. It has low density, impact resistance, and low thermal conductivity. , good noise reduction effect and high hardness, so it is widely used in environmental protection construction, aerospace and electrochemistry and other industries. At present, the research on metal foam mainly focuses on metal foam with low density and high porosity, but metal foam with high porosity has the disadvantages of complex process, narrow range of material selection and high cost. Therefore, the research and development of a porous metal foa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/08C22C9/00
CPCB22F3/1125C22C9/00
Inventor 陈昌
Owner 陈昌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap