Weather-resistance and low-temperature-resistance chloroprene rubber adhesive

A chloroprene rubber and low temperature resistance technology, applied in the direction of chloroprene adhesives, adhesives, adhesive additives, etc., can solve the problems of unsatisfactory low temperature resistance and weather resistance, limited application scope, poor storage stability, etc. Achieve the effect of improving weather resistance, increasing the degree of crosslinking, and reducing low temperature frost resistance

Active Publication Date: 2016-01-13
安徽大松树脂有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, neoprene adhesives have the disadvantages of poor storage stability, unsatisfactory low temperat...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A weather-resistant and low-temperature resistant neoprene adhesive proposed by the present invention, its raw materials include the following components in parts by weight: 70 parts of neoprene rubber, 3 parts of natural rubber, 5 parts of alkyl benzoic acid resin, 8 parts of phenolic resin, 8 parts of epoxy resin, 10 parts of terpene resin, 2 parts of trans-1,4-polyisoprene rubber, 10 parts of activated magnesium oxide, 2 parts of nano-silica, 1 part of ethylene thiourea, oxidation 8 parts of zinc, 50 parts of ethyl acetate, 15 parts of cyclohexane, 15 parts of acetone, 15 parts of propylene glycol, 10 parts of methylcyclopentane, 70 parts of dimethyl carbonate, 1 part of anti-aging agent RD, 2 parts of cerium oxide, 3 parts - 1 part of aminopropyltrimethoxysilane, 2 parts of silane coupling agent KH-5602, 2 parts of dioctyl adipate.

Embodiment 2

[0022] A weather-resistant and low-temperature resistant chloroprene rubber adhesive proposed by the present invention, its raw materials include the following components by weight: 30 parts of chloroprene rubber, 10 parts of natural rubber, 15 parts of alkyl benzoic acid resin, 2 parts of phenolic resin, 2 parts of epoxy resin, 5 parts of terpene resin, 8 parts of trans-1,4-polyisoprene rubber, 3 parts of activated magnesium oxide, 10 parts of nano silicon dioxide, 5 parts of ethylene thiourea, oxidation 2 parts of zinc, 30 parts of ethyl acetate, 5 parts of cyclohexane, 10 parts of acetone, 5 parts of propylene glycol, 50 parts of methylcyclopentane, 70 parts of dimethyl carbonate, 1 part of anti-aging agent MB, 2 parts of anti-aging agent H, anti-aging 2 parts of agent 4010NA, 8 parts of cerium oxide, 3.5 parts of 3-aminopropyltrimethoxysilane, 0.5 parts of silane coupling agent KH-5600, 1 part of butyl oleate, 3 parts of trioctyl phosphate, butyl epoxy stearate 1 part of e...

Embodiment 3

[0024]A weather-resistant and low-temperature resistant chloroprene rubber adhesive proposed by the present invention, its raw materials include the following components in parts by weight: 50 parts of chloroprene rubber, 9 parts of natural rubber, 9 parts of alkyl benzoic acid resin, 6 parts of phenolic resin, 6 parts of epoxy resin, 6 parts of terpene resin, 6 parts of trans-1,4-polyisoprene rubber, 8 parts of activated magnesium oxide, 7 parts of nano-silica, 3 parts of ethylene thiourea, oxidation 4 parts of zinc, 38 parts of ethyl acetate, 9 parts of cyclohexane, 14 parts of acetone, 9 parts of propylene glycol, 35 parts of methylcyclopentane, 65 parts of dimethyl carbonate, 2463.5 parts of anti-aging agent, 6 parts of cerium oxide, 3 - 2 parts of aminopropyltrimethoxysilane, 1.6 parts of silane coupling agent KH-560, 3.6 parts of plasticizer;

[0025] Wherein, the plasticizer is a mixture of dioctyl adipate and epoxy butyl stearate in a weight ratio of 1:6; the cerium ox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a weather-resistance and low-temperature-resistance chloroprene rubber adhesive, wherein the raw materials comprise a chloroprene rubber, a natural rubber, an alkyl benzoic acid resin, a phenolic resin, an epoxy resin, a terpene resins, a trans-1,4-polyisoprene rubber, active magnesium oxide, nanometer silicon dioxide, ethylene thiourea, zinc oxide, ethyl acetate, cyclohexane, acetone, propylene glycol, methyl cyclopentane, dimethyl carbonate, an anti-aging agent, cerium oxide, 3-aminopropyl trimethoxy silane, a silane coupling agent KH-560, and a plasticizer. The weather-resistance and low-temperature-resistance chloroprene rubber adhesive of the present invention has characteristics of high bonding strength, good low-temperature resistance, good weather resistance, and excellent storage stability.

Description

technical field [0001] The invention relates to the technical field of neoprene adhesives, in particular to a weather-resistant and low-temperature resistant neoprene adhesive. Background technique [0002] Neoprene is the main raw material of neoprene adhesive, its molecular structure is regular, and there are polar chlorine atoms on the molecular chain, which makes neoprene have high cohesive strength and flame resistance at room temperature And the aging resistance is good, the adhesive formulated with it can be cold-cured at room temperature, the initial adhesion is very large, the strength is quickly established, and the bonding strength is high. It can be used for bonding rubber, leather, fabric, Artificial leather, plastic, wood, paper, glass, ceramics, etc. However, neoprene adhesives have the disadvantages of poor storage stability, unsatisfactory low temperature resistance and weather resistance, which limit their application range and affect their performance dur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J111/00C09J11/04C09J11/06C09J11/08
Inventor 朱立芳
Owner 安徽大松树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap