Sodium ion positive electrode material with ternary layered structure, and preparation method for sodium ion positive electrode material

A positive electrode material and a ternary layered technology, applied in the field of sodium ion positive electrode materials and their preparation, can solve the problem of low cycle capacity of sodium ion positive electrode materials, and achieve the effects of high battery cycle performance, convenient operation and simple steps.

Pending Publication Date: 2016-01-06
HUNAN RESHINE NEW MATERIAL
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a sodium ion positive electrode material with a ternary layered structure and a preparation method thereof to solve the technical problem of low cycle capacity of the sodium ion positive electrode material in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sodium ion positive electrode material with ternary layered structure, and preparation method for sodium ion positive electrode material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] Another invention of the present invention also provides a kind of preparation method as above-mentioned sodium ion cathode material, comprises the following steps:

[0030] 1) The molar ratio of sodium atom, nickel atom, titanium atom and manganese atom is 2 / 3: 1 / 3: X: 2 / 3-X, mix sodium source, nickel source, titanium source and manganese source, and perform ball milling to obtain Mixtures where 0

[0031] 2) Calcining the mixture to obtain the sodium ion cathode material.

[0032] The method is easy to operate and is suitable for mass production in industrial production. According to this method, the sodium ion cathode material with the above structure can be prepared. Other parameters not detailed in the method can be operated according to other parameters commonly used in the art to prepare a sodium ion positive electrode material with a ternary layered structure.

[0033] Preferably, the method also includes grinding the obtained sodium ion positive elect...

Embodiment 1

[0043] Weigh the sodium-containing compound as anhydrous sodium carbonate (Na 2 CO 3 ), nickel source is nickel oxide (NiO), titanium source is anatase titanium dioxide (TiO 2 ) and manganese source as manganese dioxide (MnO 2 ), so that the molar ratio of sodium atoms, nickel atoms, titanium atoms and manganese atoms is 4:2:1:3, then put the weighed raw materials in the ball mill jar, and then weigh a certain amount of zirconium balls and put them into Among them, without adding any dispersant, the mass ratio of the ball milling medium to the raw material is 1:3. After dry mixing, ball milling is carried out. During mechanical mixing, the speed of the ball mill is 600r / min, and the duration is 12 hours to form a mixture; next, the mixture prepared above is placed in a high temperature resistant crucible, and then the crucible is sent into the muffle furnace In the process, calcining at 900°C for 12 hours in an air atmosphere, the heating and cooling rate is 2°C / min. After ...

Embodiment 2

[0045] Weigh the sodium-containing compound as anhydrous sodium carbonate (Na 2 CO 3 ), nickel source is nickel oxide (NiO), titanium source is rutile titanium dioxide (TiO 2 ) and manganese source as manganese dioxide (MnO 2 ), the molar ratio of sodium atom, nickel atom, titanium atom and manganese atom is changed to 2:1:1:1, then the raw materials weighed are all placed in the ball mill jar, the ball mill medium, raw material and organic dispersant After mixing according to the mass ratio of 3:1:1, the rotation speed of the ball mill during mechanical mixing is 600r / min, and the duration is 12 hours to form a mixture; the formed mixture is dried in a blast drying oven, and the addition of organic solvent, the drying time is 12 hours, and the temperature is 70°C. Next, place the dried mixture in a high-temperature-resistant crucible, then put the crucible into a muffle furnace, and calcine it at 950°C for 10 hours in an air atmosphere, with a heating and cooling rate of 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a sodium ion positive electrode material with a ternary layered structure, and a preparation method for the sodium ion positive electrode material. The sodium ion positive electrode material comprises Na2/3Ni1/3TixMn(2/3-x)O2, wherein the x is greater than 0 and less than 2/3. The sodium ion positive electrode material provided by the invention is provided with the ternary layered structure; when the sodium ion positive electrode material is charged or discharged at the 0.1 C, the specific discharge capacity is greater than 120mAhg-1; and the retention rate of the specific capacity reaches greater than 90% after the sodium ion positive electrode material is charged or discharged for 100 times.

Description

technical field [0001] The invention relates to the field of positive electrode materials for batteries, in particular to a sodium ion positive electrode material with a ternary layered structure and a preparation method thereof. Background technique [0002] With the massive consumption of non-renewable energy and environmental pollution, the development of green and sustainable new energy to replace traditional fossil energy has become a research hotspot all over the world. Among them, due to the advantages of high capacity, good cycle performance and no memory effect, lithium-ion batteries have been widely used in portable small devices such as electronic equipment and electric tools. Especially in recent years, with the rapid development of large energy storage devices With the development, the dependence on lithium-ion batteries is increasing, and the shortage of lithium resources will greatly increase the manufacturing cost of lithium-ion batteries, which will become a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/505H01M4/525H01M4/36H01M10/054
CPCH01M4/366H01M4/505H01M4/525H01M10/054Y02E60/10
Inventor 刘小雨公伟伟周贵海李魁高林蒋忠兵宋振伟黄海翔陈敏
Owner HUNAN RESHINE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap