TPU (thermoplastic polyurethane) composite membrane used for fan blades and preparation method for TPU composite membrane

A technology for fan blades and composite membranes, applied in the field of polymer materials, can solve the problems of heat resistance, corrosion resistance, strength and adhesiveness of the adhesive are not ideal, and achieve difficult separation, prolonged use time, heat resistance strong effect

Inactive Publication Date: 2015-12-16
DONGGUAN XIONGLIN NEW MATERIAL TECH
View PDF11 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, TPU film is used for the film on the surface of fan blades, and its heat resistance, corrosion resistance, strength and adhesion with adhesive are not ideal enough, so it is necessary to study a new type of TPU composite film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TPU (thermoplastic polyurethane) composite membrane used for fan blades and preparation method for TPU composite membrane
  • TPU (thermoplastic polyurethane) composite membrane used for fan blades and preparation method for TPU composite membrane
  • TPU (thermoplastic polyurethane) composite membrane used for fan blades and preparation method for TPU composite membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of TPU composite film for fan blade, described TPU composite film is mainly prepared from the following raw materials by weight:

[0041]

[0042] The TPU particles are prepared from the following raw materials in parts by weight:

[0043]

[0044] Wherein, the number average molecular weight of the polycaprolactone diol is 2000-2500. The number average molecular weight of the polycarbonate diol is 1500-2000. The molecular weight of the aliphatic diisocyanate is 100-200. The chain extender is ethylene glycol. The catalyst is an organotin catalyst.

[0045] The porogen is azodicarbonamide. The compatibilizer is SMA resin. The antioxidant is a hindered phenolic antioxidant.

[0046] The preparation method of described TPU composite film is:

[0047] 1) Weigh the TPU particles, glass fiber reinforced polybutylene terephthalate, PVDF, compatibilizer, porogen, antioxidant and ultraviolet absorber of the formula amount, and mix them uniformly to obtain the...

Embodiment 2

[0050] A kind of TPU composite film for fan blade, described TPU composite film is mainly prepared from the following raw materials by weight:

[0051]

[0052] The TPU particles are prepared from the following raw materials in parts by weight:

[0053]

[0054] Wherein, the number average molecular weight of the polycaprolactone diol is 2500-3500. The number average molecular weight of the polycarbonate diol is 2000-2500. The molecular weight of the aliphatic diisocyanate is 200-300. The chain extender is a combination of 1,4 butanediol and 1,6-hexanediol ethylene glycol. The catalyst is an organozinc catalyst.

[0055] The porogen is azodicarbonamide. The compatibilizer is a combination of organic acid chromium complex and organic coupling agent. The antioxidant is a hindered amine antioxidant.

[0056] The preparation method of described TPU composite film is:

[0057] 1) Weigh the TPU particles, glass fiber reinforced polybutylene terephthalate, PVDF, compatibil...

Embodiment 3

[0060] A kind of TPU composite film for fan blade, described TPU composite film is mainly prepared from the following raw materials by weight:

[0061]

[0062] The TPU particles are prepared from the following raw materials in parts by weight:

[0063]

[0064]

[0065] Wherein, the number average molecular weight of the polycaprolactone diol is 3500-4500. The number average molecular weight of the polycarbonate diol is 2500-3000. The molecular weight of the aliphatic diisocyanate is 300-500. The chain extender is a combination of 1,3-butanediol, diethylene glycol, 1,6-hexanediol and neopentyl glycol. The catalyst is an organic bismuth catalyst.

[0066] The porogen is azodicarbonamide. The compatibilizer is a combination of a titanate coupling agent and an aluminate coupling agent. The antioxidant is a phosphite antioxidant.

[0067] The preparation method of described TPU composite film is:

[0068] 1) Weigh the TPU particles, glass fiber reinforced polybuty...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a TPU (thermoplastic polyurethane) composite membrane used for fan blades and a preparation method for the TPU composite membrane. The TPU composite membrane is prepared from the following raw materials in parts by weight: 70 to 90 parts of TPU particles, 10 to 25 parts of glass fiber reinforced polybutylene terephthalate, 2 to 10 parts of PVDF (polyvinylidene fluoride), 3 to 8 parts of compatilizer, 1 to 5 parts of pore-foaming agent, 1 to 3 parts of antioxygen and 0.5 to 1 parts of ultraviolet light absorber. The TPU composite membrane provided by the invention is high in strength (the tensile strength can reach 85.1mpa) and high in heat resistance (the maximum vicat softening temperature is 128 DEG C), has good heat insulation property (the minimum heat conductivity coefficient is 0.012w / (m.k)), and is not is easy to separate from adhesive; when the TPU composite membrane is used for the fan blades, the fan blades can be protected to prolong the service life of the fan blades; moreover, the preparation method for the TPU composite membrane is simple.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a TPU composite film for fan blades and a preparation method thereof. Background technique [0002] In today's global background of increasing shortage of non-renewable energy, rapid climate change, and deteriorating environment, wind energy, as a renewable and green energy source, has attracted great attention from all countries. productive forces. According to the calculation that the cost of blades accounts for 1 / 4 of the cost of the total machine, the domestic market size of China's wind turbine blades will exceed 50 billion yuan in the next 15 years. The "Eleventh Five-Year Plan" clearly stated that the localization rate of wind power equipment such as fan blades in newly-built wind farms must reach more than 70%. Domestic wind power heat. [0003] During the working process of the fan, the fan blades are subjected to external effects such as strong ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/06C08L67/02C08L27/16C08K13/04C08K7/14C08G18/66C08G18/42C08G18/44C08J9/10
Inventor 何建雄王一良
Owner DONGGUAN XIONGLIN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products