Automobile cable insulating material and preparation method thereof

A technology for cable insulation and automobiles, applied in the direction of insulated conductors, insulated cables, organic insulators, etc., can solve the problem of poor compatibility between magnesium hydroxide and polymer materials, lower surface temperature of burning materials, high decomposition temperature of magnesium hydroxide, etc. problems, to achieve the effect of simple and controllable preparation method, enhanced compatibility and low cost

Inactive Publication Date: 2015-11-25
HEFEISHI SHENZHAO ELECTRONICS
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The combustion of polyvinyl chloride can be divided into several stages of heating, decomposition, ignition, combustion and propagation. During the combustion of polyvinyl chloride, there is a lot of smoke and it will produce HCl toxic gas, so it is necessary to add flame retardants to reduce the risk of polyvinyl chloride. The flammable products produced by the decomposition of ethylene can prevent or dilute the escape of flammable gas products produced by the decomposition. The decomposition temperature of magnesium hydroxide is high, and a dehydration reaction occurs after decomposition, which can absorb a large amount of heat on the surface of polymer materials and reduce the surface of burning materials. temperature, dehydration at the same time produces a large amount of water vapor, dilutes combustible gas and oxygen concentration, but the compatibility of magnesium hydroxide with polymer materials is not very good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A cable insulation material for automobiles and a preparation method thereof, which is made of the following raw materials in parts by weight (kg): EVA resin 4, anhydrous lithium chloride 3, polyvinyl chloride 100, magnesium hydroxide 13, antimony trioxide 8 , nanoclay 13, silane coupling agent kh5500.5, polyvinyl alcohol 0.8, sodium dodecylbenzenesulfonate 0.2, sodium bicarbonate 0.8, styrene 4, potassium persulfate 0.04, dioctyl terephthalate 13 , tributyl citrate 4, hard wax 2, fumed silica 4, wood flour 3, water in proper amount;

[0016] A kind of automobile cable insulation material and its preparation method described in the present invention are prepared by the following specific steps:

[0017] (1) Mix magnesium hydroxide, nanoclay, antimony trioxide and silane coupling agent kh550, add it to a grinder, grind and disperse evenly, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an automobile cable insulating material and a preparation method thereof. The automobile cable insulating material is characterized by being prepared by, by weight, 3-6 parts of EVA resin, 2-4 parts of anhydrous lithium chloride, 90-100 parts of polyvinyl chloride, 10-15 parts of magnesium hydrate, 5-10 parts of antimony trioxide, 10-14 parts of nanometer clay, 0.3-0.7 part of silane coupling agent kh550, 0.5-1 part of polyvinyl alcohol, 0.1-0.3 part of sodium dodecyl benzene sulfonate, 0.5-2 parts of sodium bicarbonate, 2-5 parts of styrene, 0.02-0.05 part of potassium persulfate, 10-15 parts of dioctyl terephthalate, 3-5 parts of tributyl citrate, 1-3 parts of hard wax, 3-5 parts of fumed silica, 2-4 parts of wood flour and an appropriate amount of water. The cable material can meet the requirement for environmental friendliness and has good comprehensive performance, the preparation method is simple and controllable, and the cost is low.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to a cable insulating material for automobiles and a preparation method thereof. Background technique [0002] Digital communication transmission cables are the fastest growing among all kinds of cables, but the cables also bring the risk of fire while providing convenience to the society. If the cables are ignited due to their own and external reasons, it is possible to burn along the cables. The direction of laying spreads from inside to outside of the building, and then ignites other combustibles, causing a bigger fire. At the same time, the cable will produce toxic smoke when burning, causing loss of life and property. Therefore, with the improvement of safety awareness, people That is to say, the flame retardant requirements of cables are getting higher and higher. The flame retardant performance of cables mainly depends on the coating materials used. Commonly used cable material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/08C08L97/02C08L91/06C08K13/06C08K9/06C08K9/10C08K9/04C08K3/16C08K3/22C08K3/34C08K3/36H01B7/17H01B3/44B29B7/00B29C35/02
Inventor 尚广东
Owner HEFEISHI SHENZHAO ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products