Heat-resistant styrene resin-containing hot melt glue

A technology of styrene resin and hot-melt adhesive, applied in the field of hot-melt adhesives, can solve the problems of EVA hot-melt adhesives that are not resistant to high and low temperatures, not suitable for large-area coating and bonding, and have limited high and low temperature resistance. Capacitance, improvement of various performances, and good air tightness

Inactive Publication Date: 2015-11-11
QUANJIAO HAIFENG PRINTING PACKAGING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since EVA resin is a thermoplastic resin, it has limited high and low temperature resistance and low softening point, and most of the main auxiliary tackifiers are polymers with small molecular weights, which only reduce the melt viscosity and improve the wettability and initial strength. The role of stickiness, itself is not resistant to high and low temperature, resulting in the shortcomings of EVA hot melt adhesive not resistant to high and low temperature; at the same time, EVA hot melt adhesive also has low bonding performance, not resistant to fat oil, easy to produce skinning and not suitable for large Disadvantages such as area coating and adhesion
[0003] At present, with the rapid development of the PET industry, the amount of discarded PET has also increased, which has brought serious pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A heat-resistant hot melt adhesive containing styrene resin, which is made from the following raw materials by weight (kg): EVA65, modified tackifying resin 10, cetyltrimethylammonium bromide 1, benzene Vinyl resin 10, xylene formaldehyde resin 10, crosslinking agent TAC1.3, neoprene rubber 20, paraffin oil 2, sodium carboxymethyl cellulose 0.5, epoxy soybean oil 2, nanopotassium feldspar powder 25, casein 1.5, Citric acid 1.5;

[0022] Described modified tackifying resin is made from the raw material of following weight (kg):

[0023] Waste PET fragments 40, zinc acetate 3, polysulfide rubber 10, chloroprene rubber 5, alkyl phenolic resin 20, styrene resin 10, trimethyl octadecyl ammonium chloride 1, carbide slag 10, activated carbon 2;

[0024] The preparation method of described modified tackifying resin is:

[0025] (1) After mixing calcium carbide slag and activated carbon, irradiate with ultraviolet rays for 12 hours, then soak in 6% hydrochloric acid solution f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses heat-resistant styrene resin-containing hot melt glue. The hot melt glue is prepared from the following raw materials in parts by weight: 65-70 parts of EVA, 10-20 parts of modified tackifying resin, 1-3 parts of cetyl trimethyl ammonium bromide, 5-10 parts of styrene resin, 10-15 parts of xylene formaldehyde resin, 1.3-1.5 parts of a crosslinking agent TAC, 15-20 parts of neoprene, 1-2 parts of paraffin oil, 0.5-0.8 part of sodium carboxymethylcellulose, 2-5 parts of epoxidized soybean oil, 25-30 parts of nano potassium feldspar powder, 1.3-1.9 parts of casein and 1.5-1.9 parts of citric acid. According to the heat-resistant styrene resin-containing hot melt glue, the heat resistance of the hot melt glue can be improved through the usage of nano potassium feldspar powder and casein; styrene resin and neoprene are subjected to intercalation modification, so that the mechanical property of the resin can be improved, the heat deflection temperature is increased, the water-absorbing property is low, and when the resin subjected to intercalation modification is used to prepare the hot melt glue, the compatibility among the raw materials of the hot melt glue is strengthened, and the viscosity, heat resistance and waterpfoofness of the hot melt glue are improved.

Description

technical field [0001] The invention belongs to the field of adhesives, in particular to a heat-resistant hot-melt adhesive containing styrene resin. Background technique [0002] EVA hot melt adhesive is formulated from EVA resin, tackifier, plasticizer, antioxidant, filler, etc. In today's society, EVA hot melt adhesives are widely used and used in the largest amount. It has excellent bonding performance, almost has thermal adhesion to various materials; excellent electrical properties; and its low melt viscosity, convenient sizing; good compatibility with other compounding agents, etc. EVA hot melt adhesives have been widely used in many fields such as book binding, food packaging, plastic bonding, ceramic repairing, mounting, clothing, shoes and hats molding, automobiles and building materials. Since EVA resin is a thermoplastic resin, it has limited high and low temperature resistance and low softening point, and most of the main auxiliary tackifiers are polymers with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J111/00C09J125/04C09J167/02C09J11/04
Inventor 毕全中
Owner QUANJIAO HAIFENG PRINTING PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products