Modified alveolar stone doped bioactive polylactic acid-polypropylene composite fiber carrier material and preparation method thereof

A bioactive and composite fiber technology, applied in plant fiber, fiber treatment, chemical instruments and methods, etc., to achieve good compatibility, improve efficiency, and broaden the scope of use

Inactive Publication Date: 2015-10-21
HEFEI ZHONGYUE HEALTH TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to prepare a new type of bioactive polylactic acid-polypropylene biofilm composite fiber carrier material doped with modified honeycomb to obtain good microbial hanging film and Water purification effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0015] The present invention will be further described below in conjunction with embodiment.

[0016] A bioactive polylactic acid-polypropylene biofilm composite fiber carrier material doped with modified honeycomb, characterized in that: the carrier material is made of the following raw materials in parts by weight: 200 mesh colloidal graphite powder 1.5, honeycomb Stone 8, polylactic acid 15, corn starch 4, polypropylene 40, epoxy soybean oil 2, ethylene-acrylic acid copolymer 8, sodium lauryl sulfate 0.1, sodium humate 0.5, compound silica sol amount, water 20;

[0017] The composite silica sol is made of the following raw materials in parts by weight: 12-16 silica sol with a solid content of 30-35%, 5-8 aldehyde-oxygenated starch, and 30-35 water. The preparation method is: put aldehyde-oxygenated starch into Stir in water at a temperature of 40-50°C until it is completely dissolved, then add silica sol, and keep stirring for 2-3 hours to obtain composite silica sol.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a biomembrane carrier material, and specifically relates to a modified alveolar stone doped bioactive polylactic acid-polypropylene composite fiber carrier material and a preparation method thereof. The conventional pure inorganic and organic carriers are mixed to prepare the composite material; the fiber silk made of polymer materials such as polypropylene, polylactic acid, and the like has a better compatibility with microbes and good hydrophilicity. Moreover, the doped modified alveolar stone has a uniform and efficient adsorption performance. The added colloid graphite powder improves the mechanical performance of fiber silk and improves the adsorption performance of carrier on microbes. The fiber bundle is soaked in composite silica gel, after the treatment, the fiber bundle can adhere to a carbon source in fibers, and the growth of microbes is accelerated. The provided composite fiber carrier material has the advantages of light weight, large activated surface area, high bioactivity, and suitability for microbial growth and propagation and is capable of forming a film in a short time. The filling material made of the composite fiber carrier material has the advantages of good fluidity, difficulty in clustering, and aging resistant property, and is capable of improving the water purification efficiency.

Description

technical field [0001] The invention relates to a biofilm carrier material, in particular to a bioactive polylactic acid-polypropylene biofilm composite fiber carrier material doped with modified honeycomb stone and a preparation method thereof. Background technique [0002] Biofilm wastewater treatment technology is a technology that fixes microorganisms on the carrier to form a biofilm to degrade the pollutants in the wastewater. Therefore, the performance of the biofilm carrier will directly affect the efficiency of sewage treatment. To obtain efficient water treatment effects, It is particularly important to select suitable and efficient carrier materials. At present, the most widely used carrier materials are mainly soft polymer materials such as polyethylene, polystyrene, polyamide, and polypropylene, and inorganic fillers such as activated carbon, slag, and limestone. However, these Materials have some defects in biocompatibility, stability, durability, regeneration, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/79D06M15/11D04H1/4382D01F1/10C02F3/00D06M101/32D06M101/04D06M101/20
Inventor 高雅
Owner HEFEI ZHONGYUE HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products