A high reflectivity photovoltaic module encapsulation adhesive film and its application

A photovoltaic module packaging, high reflectivity technology, applied in photovoltaic power generation, adhesives, electrical components and other directions, can solve the problems of reducing the processing temperature window of the film, reducing the production efficiency of the module, reducing the fluidity of the film, etc., to improve the photovoltaic Effect of conversion efficiency, improvement of UV resistance, and increased light utilization

Active Publication Date: 2016-08-17
HANGZHOU FIRST APPLIED MATERIAL CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By using a low-melt index resin as the raw material of the film and matching the appropriate component lamination process, the effect of preventing the overflow of the high-reflection film can be achieved, but the use of a low-melt index base resin reduces the processing temperature window of the film , which increases the processing cost; adopt the method of co-extrusion to form a composite structure of transparent film and high-reflection film, match the appropriate component lamination process, the transparent composite layer can play the role of isolation layer, but co-extrusion processing requires production Additional extrusion equipment is added to the line, which increases the processing cost; the above two high-reflection films usually need to be used in conjunction with a special lamination process, usually using a lower lamination temperature to reduce the fluidity of the film, and at the same time Extended lamination time to achieve the required degree of cross-linking, which further reduces the production efficiency of the assembly
The overall pre-crosslinking treatment of the high-reflection film enables the use of conventional lamination processes. However, since the pre-crosslinked film hardly flows during lamination, residual air bubbles and delamination are serious in the component, and the adhesion of the film The junction performance is difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In parts by mass, to 100 parts of ethylene-vinyl acetate copolymer (the mass content of vinyl acetate VA is 28%), add 1 part of photoinitiator benzophenone and 0.5 part of photoinitiator 2-methyl -2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1-propanone, add 0.3 parts of thermal initiator tert-butyl peroxyisopropyl carbonate and 0.3 parts of thermal initiator 2,5-Dimethyl-2,5-bis(tert-butylperoxy)hexane, 3 parts trimethylolpropane trimethacrylate and 2 parts pentaerythritol triacrylate , 0.1 part of tackifier vinyltrimethoxysilane, 0.1 part of tackifier γ-(2,3-epoxypropoxy) propyltrimethoxysilane and 0.1 part of N-(β-aminoethyl )-γ-aminopropyltrimethoxysilane, 2 parts of high reflection additive titanium dioxide, 2 parts of high reflection additive indium tin oxide and 3 parts of high reflection additive montmorillonite, and mix well.

[0019] The mixture is melted and extruded in the extruder, the temperature is controlled at 85°C, and the extruded product is cast into ...

Embodiment 2

[0021] In parts by mass, to 100 parts of ethylene-α-octene copolymer, add 0.01 part of photoinitiator isopropylthioxanthone, add 1.5 parts of thermal initiator 1-bis(tert-butyl peroxide)-3 , 3,5-trimethylcyclohexane, 10 parts of co-crosslinking agent trimethylolpropane trimethacrylate, 0.3 parts of tackifier vinyl trimethoxysilane, 10 parts of high reflection additive silica , and mix well.

[0022] The mixture is melted and extruded in the extruder, the temperature is controlled at 85°C, the extruded product is cast and formed into a film, and the irradiation intensity is 1800W / m in a 70°C drying tunnel 2 UV lamp irradiation for 100s, after cooling, slitting, and coiling processes, a highly reflective adhesive film with a thickness of 0.45mm and a surface pre-crosslinking depth of 0.05mm (crosslinking degree is 80%) is obtained, denoted as S -2.

Embodiment 3

[0024] In parts by mass, in 100 parts of ethylene-methyl methacrylate copolymer, add 0.9 parts of photoinitiator benzoin dimethyl ether, add 0.15 parts of thermal initiator 1-bis(tert-butyl peroxide)-3,3 , 5-trimethylcyclohexane, 0.7 parts of cross-linking agent trimethylolpropane triacrylate, 5 parts of tackifier γ-aminopropyl triethoxysilane, 15 parts of high reflection additive calcium carbonate, 30 parts antimony tin oxide of high reflection additive, and mix well.

[0025] The mixture is melted and extruded in the extruder, the temperature is controlled at 85°C, the extruded product is cast and formed into a film, and the irradiation intensity is 1800W / m in a 70°C drying tunnel 2UV lamp irradiation for 100s, after cooling, slitting, and coiling processes, a highly reflective film with a thickness of 0.45mm and a surface pre-crosslinking depth of 0.1mm (crosslinking degree of 85%) was obtained, denoted as S -3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-reflectivity photovoltaic component encapsulating adhesive film. A high-reflectivity photovoltaic module with a surface pre-crosslinked structure is obtained by pre-mixing transparent resin, high-reflection additives and other functional additives, melt-extruding, casting into a film, and performing surface pre-crosslinking treatment. Packaging film. By adding high-reflective additives, the UV resistance of the adhesive film can be improved, and at the same time, the utilization rate of sunlight by the module can be increased, so as to improve the service life of the module and the photoelectric conversion efficiency; at the same time, the surface pre-crosslinked structure can effectively prevent photovoltaic The overflow of the high-reflection layer adhesive film during the lamination process of the module effectively improves the appearance of the module and is universal to different lamination processes.

Description

technical field [0001] The invention relates to a high-reflectivity photovoltaic module packaging adhesive film, which is used for the packaging of solar cell components, can improve the reflectivity of the battery back layer structure, improve the utilization efficiency of sunlight by the components, and effectively avoid overflow during the lamination process. white phenomenon. Background technique [0002] In the current society, energy conflicts and environmental problems are becoming more and more prominent, and the development of various clean energy is an inevitable trend. In the past two years, the solar photovoltaic industry has recovered, and the demand for photovoltaic modules has gradually increased. Further improving the photoelectric conversion efficiency and durability of photovoltaic modules is the appeal of the entire photovoltaic industry. [0003] At present, more than 80% of solar cell components are crystalline silicon cell components. The theoretical l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/00C09J4/02C09J4/06C09J11/04C09J11/06B29C71/04H01L31/048
CPCY02E10/50
Inventor 熊曦彭瑞群侯宏兵周光大林建华
Owner HANGZHOU FIRST APPLIED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com