High-heat-conductivity anti-aging anti-rusting paint for outdoor equipment and preparation method of high-heat-conductivity anti-aging anti-rusting paint

A technology for outdoor equipment and thermal conductivity, applied in anti-corrosion coatings, coatings, epoxy resin coatings, etc., can solve the problems of shortening the service life of equipment, waste of manpower and financial resources, poor high temperature resistance, etc., and achieves remarkable anti-rust effect. Reduce environmental hazards, good anti-rust effect

Inactive Publication Date: 2015-03-25
李勇智
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing antirust coatings have poor high temperature resistance
Because the temperature of high and low voltage power equipment is high when working, and it is in a high temperature environment for a long time, if the heat cannot be dissipated, the service life of the equipment will be greatly shortened, and it will cause a huge waste of manpower and financial resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] An antirust paint for outdoor equipment with high thermal conductivity and aging resistance, made of the following raw materials in parts by weight (kg): phosphating slag 5, iron powder 3, diacetone alcohol 1, propylene glycol 5, zinc carbonate 2, anionic emulsified silicone oil 0.6, triethanolamine 3, alcohol ester dodecyl 3, stearyl polyoxyethylene ether 0.5, epoxy butyl oleate 1, titanate coupling agent 1, cuprous oxide 2, oxidized petroleum grease barium soap 3 , titanium dioxide 5, bisphenol A epoxy resin 35, high wear-resistant elastic resin 18, butyl acetate 13, xylene 9, additive 4;

[0016] The auxiliary agent is made of the following raw materials in parts by weight (kg): nano ceramic fiber 6, rock wool fiber 5, oxidized petroleum grease barium soap 2, petroleum sulfonate barium 2, animal glue 3, white oil 12, monohard Fatty glyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-heat-conductivity anti-aging anti-rusting paint for outdoor equipment. The paint is characterized by being prepared from the following raw materials in parts by weight: 4-5 parts of phosphated residue, 3-5 parts of iron powder, 1-2 parts of diacetone alcohol, 3-5 parts of propylene glycol, 2-3 parts of zinc carbonate, 0.5-1.0 part of an anionic silicone emulsion, 2-3 parts of triethanolamine, 3-4 parts of dodecanol, 0.5-1.0 part of octadecanol polyoxyethylene ether, 1-2 parts of epoxy fatty acid butyl ester, 1-2 parts of a titanate coupling agent, 1-2 parts of cuprous oxide, 2-4 parts of oxidized petrolatum barium soap, 5-6 parts of titanium dioxide, 32-36 parts of bisphenol A epoxy resin, 18-24 parts of highly wear-resistant elastic resin, 10-14 parts of butyl acetate, 9-11 parts of xylene and 4-7 parts of auxiliaries. The paint provided by the invention is good in heat conductivity, high in ageing resistance, good in anti-rusting effect, remarkable in noise reduction, high in film hardness and good in glossiness, and has an excellent maintaining and preserving effect when being applied to a shell of the outdoor power equipment.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to an antirust paint for outdoor equipment with high thermal conductivity and aging resistance and a preparation method thereof. Background technique [0002] High thermal conductivity anti-rust coatings are widely used in high-temperature places such as steel chimneys, high-temperature pipelines, high-temperature furnaces, petroleum cracking devices, and high-voltage and low-voltage power equipment to delay thermal oxidation corrosion of metal equipment such as steel at high temperatures and ensure long-term use of equipment. The existing antirust paint has poor high temperature resistance. Because the temperature of high and low voltage power equipment is high when working, and it is in a high temperature environment for a long time, if the heat cannot be dissipated, the service life of the equipment will be greatly shortened, and it will cause a huge waste of manpower a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D201/00C09D5/10C09D7/12
CPCC09D163/00C08L2205/035C09D5/10C09D7/40C08L101/00C08L83/04C08L71/02C08K13/08C08K11/00C08K2003/0856C08K5/053C08K3/26C08K9/00C08K7/04C08K7/10
Inventor 李勇智
Owner 李勇智
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products