A kind of preparation method of mesoporous β-tricalcium phosphate powder

A tricalcium phosphate powder and mesoporous technology, applied in chemical instruments and methods, phosphorus compounds, inorganic chemistry, etc., can solve the problems of mesoporous β-TCP crystal habit, preparation difficulties, etc., achieve continuous adjustable pore size, energy The effect of low consumption and mild reaction conditions

Active Publication Date: 2016-09-14
WUHAN UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, mesoporous β-TCP has not been reported due to its crystal habit and difficulty in preparation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of mesoporous β-tricalcium phosphate powder
  • A kind of preparation method of mesoporous β-tricalcium phosphate powder
  • A kind of preparation method of mesoporous β-tricalcium phosphate powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Prepare two transparent solutions containing surfactant CTAB, co-surfactant n-butanol and water, wherein the volume of water is 40 mL, the concentration of surfactant is 12.5 g / L, and the concentration of co-surfactant is 100 mL / L, and then to Add 0.5mol / L Ca(NO 3 ) 2 4H 2 O solution 20mL and 0.5mol / L (NH 4 ) 2 HPO 4 solution, and fully stirred at 40°C to obtain a mixed solution of calcium-containing inorganic salts and a mixed solution of phosphorus-containing inorganic salts. Keeping the temperature constant, add phosphorus-containing A mixed solution of inorganic salts, and the molar ratio of the added element calcium to phosphorus is 1.5:1, with NH 3 ·H 2 O solution to adjust the pH to 7.5, continue magnetic stirring for 21 hours, then stand at room temperature for 48 hours, centrifuge at 10,000 rpm for 3 minutes, wash the precipitate with water three times, then wash it with alcohol three times, and finally put the precipitate in a drying box After drying at...

Embodiment 2

[0026] Prepare two clear solutions containing the surfactant polyethylene glycol 6000, the co-surfactant 1-octanol, and water, where the volume of water is 30 mL, the concentration of surfactant is 10 g / L, and the concentration of co-surfactant is 50 mL / L. L, then add 0.1mol / L CaCl to the two transparent solutions 2 Solution 30mL and 0.1mol / L NaH 2 PO 4solution, and fully stirred at 25°C to obtain a mixed solution of calcium-containing inorganic salts and a mixed solution of phosphorus-containing inorganic salts. Keep the temperature constant, add the mixed solution of phosphorus-containing inorganic salt to the mixed solution of calcium-containing inorganic salt at a speed of 0.2mL per minute, and make the molar ratio of the added element calcium to phosphorus be 1.5:1, and use NH 3 ·H 2 The pH of the O solution was adjusted to 6.0, and magnetic stirring was continued for 2 hours, then left to age at room temperature for 12 hours, centrifuged at 9500 rpm for 3 minutes, and...

Embodiment 3

[0028] Prepare two transparent solutions containing surfactant polyoxyethylene-polyoxypropylene-polyoxyethylene, co-surfactant n-propanol and water, wherein the volume of water is 200mL, the concentration of surfactant is 100g / L, co-surfactant The agent concentration was 250mL / L, and then 1.0mol / L of CaSO was added to the two transparent solutions 4 Solution 80mL and 1.0mol / L Na 3 PO 4 solution, and fully stirred at 90°C to obtain a mixed solution of calcium-containing inorganic salts and a mixed solution of phosphorus-containing inorganic salts. Keep the temperature constant, add the mixed solution of phosphorus-containing inorganic salt to the mixed solution of calcium-containing inorganic salt at a rate of 0.6mL per minute, and make the molar ratio of the added element calcium to phosphorus 1.5:1, use NH 3 ·H 2 The pH of the O solution was adjusted to 9.0, and the magnetic stirring was continued for 24 hours, then left to age at room temperature for 24 hours, centrifuged...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of mesoporous beta-TCP (tricalcium phosphate) powder. The preparation method comprises steps as follows: 1), two parts of transparent solutions containing surfactants, cosurfactants and water are prepared; 2), a calcium-containing inorganic salt solution and a phosphorus-containing inorganic salt solution are added to the transparent solutions respectively and stirred, a phosphorus-containing inorganic salt mixed solution is added to a calcium-containing inorganic salt mixed solution, the pH value is adjusted, and the mixture is stirred to obtain an emulsion; and 3), the mixture is left to stand, subjected to ageing, centrifugation, washing and drying, placed in a high-temperature furnace, heated and subjected to heat preservation, and mesoporous beta-TCP powder is obtained. The preparation method has the benefits as follows: 1, the operation is simple, energy consumption is low, the cost is low, the reaction condition is mild, and harmful substances are not generated in the preparation process; and 2, the obtained mesoporous beta-TCP powder has smaller pore diameter and has a three-dimensional pore structure, the average pore diameter of the mesoporous beta-TCP powder is 8.80-21.36 nm, and the specific surface area is 10.11-153.43 m<2> / g.

Description

technical field [0001] The invention relates to a preparation method of mesoporous β-tricalcium phosphate powder. Background technique [0002] Ca 3 (PO 4 ) 2 [TCP] There are two types of high-temperature α-phase and low-temperature β-phase. Among them, the low-temperature type β-TCP[β-Ca 3 (PO 4 ) 2 ] is mainly composed of calcium and phosphorus, and its composition is similar to that of the inorganic components of the bone matrix [Ca 10 (PO 4 ) 6 (OH) 2 ] similar, with good biocompatibility. Scholars have confirmed that β-TCP can be absorbed by the body without inflammation or rejection, and without local or systemic toxicity. The degree of hemolysis of β-TCP is less than 5%; it is classified as non-toxic according to the measurement of toxicity; β-TCP can be directly combined with bone tissue without fibrous tissue growing in between. After β-TCP is implanted into bone tissue, a solid-liquid balance of calcium and phosphorus is formed at the interface. The i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B25/32
Inventor 戴红莲黄岸喻莹韩颖超李世普
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com