Method for plating zinc and nickel on neodymium-iron-boron material

A technology of electroplating zinc-nickel and neodymium-iron-boron, which is applied in the field of electroplating alloy technology, can solve problems such as poor corrosion resistance and reduced magnetic properties, and achieve the effects of improving corrosion resistance, reducing magnetic loss, and being easy to popularize and use

Inactive Publication Date: 2014-12-24
XIAN SANWEI SECURITY TECH
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its special loose and porous structure, NdFeB materials lead to poor corrosion resistance, and the surface coating will cause a decrease in their magnetic properties. At present, the surface treatment of NdFeB materials mainly adopts electroplating to improve their corrosion resistance. Usually electro-galvanized, double-layer nickel, triple-layer nickel, electroless plating, and some other alloy plating and composite plating, but the above plating methods cannot well meet the needs of the actual industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The method for the zinc-nickel electroplating of a kind of neodymium-iron-boron material of the present invention, comprises the steps:

[0020] (1) Firstly, the NdFeB material is rolled and chamfered, using vibration rolling, and the processing time is 4 hours;

[0021] (2) Ultrasonic oil is used, and NdFeB is placed in the degreasing solution. The components of the degreasing solution are 3~5g / L sodium hydroxide, 40~60g / L sodium carbonate, 40~60g / L Sodium phosphate and 20~30g / L water glass;

[0022] (3) Then use a nitric acid solution with a volume fraction of 10% for derusting treatment, and the time is 15s~25s;

[0023] (4) Use a low-temperature example plugging agent, and immerse for 20 minutes at a temperature of 30 ° C to 40 ° C for sealing treatment;

[0024] (5) Then use sulfosalicylic acid solution to perform activation treatment at room temperature;

[0025] (6) Electroplating the NdFeB material treated by the above steps, the solution composition is 70g / L...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for plating zinc and nickel on a neodymium-iron-boron material, and belongs to the field of alloy plating processes. The method comprises the following steps of: (1) firstly carrying out roll finish chamfer treatment on the neodymium-iron-boron material by adopting vibrating type roll finish; (2) placing the neodymium-iron-boron material into a deoiling solution and carrying out ultrasonic deoiling; (3) then carrying out derusting treatment by adopting a nitric acid solution with the volume fraction of 10%; (4) carrying out hole sealing treatment by using a low-temperature particule plugging agent; (5) then carrying out activating treatment under the condition of room temperature by using a sulfosalicylic acid solution; (6) plating the neodymium-iron-boron material subjected to the treatment; (7) carrying out polishing treatment on the plated neodymium-iron-boron material, and then carrying out zinc-nickel alloy plating layer passivating treatment; (8) finally carrying out subsequent impregnation treatment by adopting passivated impregnating resin. The method for plating zinc and nickel on the neodymium-iron-boron material, which is disclosed by the invention, greatly enhances the corrosion-resistant capacity of a neodymium-iron-boron surface after the neodymium-iron-boron surface is treated and reduces the magnetic loss through the improvement of a process and has the advantages of simple process and easiness for popularization and use.

Description

technical field [0001] The invention belongs to the field of electroplating alloy technology, and in particular relates to a method for electroplating zinc and nickel of neodymium-iron-boron materials. Background technique [0002] As a new production material, NdFeB has been widely used in electronics, home appliances and automobile industries due to its excellent magnetic properties and high cost performance, and has achieved rapid development. Due to its special loose and porous structure, NdFeB materials lead to poor corrosion resistance, and the surface coating will cause a decrease in their magnetic properties. At present, the surface treatment of NdFeB materials mainly adopts electroplating to improve their corrosion resistance. It is usually electro-galvanized, double-layer nickel, triple-layer nickel, electroless plating, and some other alloy plating and composite plating, but the above-mentioned plating methods cannot well meet the needs of the actual industry. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/56C25D5/34C25D5/48
Inventor 贾卫东魏军锋
Owner XIAN SANWEI SECURITY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com