Ceramic corundum grinding material containing complex-phase additive system

A technology of ceramic corundum and additives, applied in the field of ceramic corundum abrasives, can solve the problems of high pure alumina, grain growth, destructive properties, etc., and achieve the effects of reducing sintering temperature, improving compressive strength, and reducing energy consumption

Inactive Publication Date: 2014-09-17
QINGDAO GUOHANG XIANGYU TECH SERVICE
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although ceramic corundum abrasives have many advantages and broad application prospects, due to the high melting point (2050°C) of pure alumina, it is difficult to sinter at low temperatures during the preparation process, and excessively high temperatures can easily cause abnormal grain growth and damage performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A ceramic corundum abrasive containing a complex additive system, comprising the following materials in parts by weight: 20-30 parts of vein quartz, 10-19 parts of boric acid, 30-45 parts of feldspar, 15-30 parts of gypsum, and 10-30 parts of sandstone. 19 parts, 35-46 parts of copper nitrate, 5-14 parts of wollastonite, 29-40 parts of barium nitrate, 5-11 parts of bagasse, 3-8 parts of bunao powder, 15-39 parts of conch shell powder, aluminum nitrate 35-39 parts, 30-50 parts of ethyl orthosilicate, 15-20 parts of barium hydroxide octahydrate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic corundum grinding material containing a complex-phase additive system, which comprises the following components in parts by weight: 20-30 parts of vein quartz, 10-19 parts of boric acid, 30-45 parts of feldspar, 15-30 parts of gypsum, 10-19 parts of sandstone, 35-46 parts of copper nitrate, 5-14 parts of wollastonite, 29-40 parts of barium nitrate, 5-11 parts of bagasse, 3-8 parts of Baonao powder, 15-39 parts of trumpet shell powder, 35-39 parts of aluminum nitrate, 30-50 parts of ethyl orthosilicate and 15-20 parts of barium hydroxide octahydrate. The corundum grinding material has the advantages of wider additive selection range, wide additive sources, higher single-granule compression strength and higher impact toughness, and the sintering temperature of the corundum grinding material can be effectively lowered, thereby lowering the production cost, reducing the energy consumption and further optimizing the interior microstructure.

Description

technical field [0001] The invention relates to a ceramic corundum abrasive containing a complex additive system. Background technique [0002] Ceramic corundum abrasive (ie SG abrasive) is a high-purity corundum abrasive with fine crystal structure and composition prepared by sol-gel method. Compared with ordinary fused corundum abrasives, it not only has high hardness, but also because the abrasive grains have a microcrystalline structure, there are many cleavage surfaces that only microcrystalline fall off under the action of external force, and new cutting edges are continuously generated, with good self-sharpening properties. And less peeling; abrasive tools prepared with ceramic corundum abrasives have the advantages of good wear resistance, less grinding heat, long service life, large grinding ratio, high removal rate and good grinding quality. At the same time, the price is far lower than that of abrasive tools made of superhard materials such as cubic boron nitride...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/16C09K3/14
Inventor 王爱国
Owner QINGDAO GUOHANG XIANGYU TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products