Carbonization-resistant waterproof slurry

A waterproof slurry and anti-carbonization technology, which is applied in the direction of cement coatings, etc., can solve the problem of unsatisfactory anti-carbonization ability and achieve the effect of avoiding losses

Active Publication Date: 2014-02-26
西卡德高(上海)建材有限公司
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Some published patent applications, such as CN 102503300A disclose a kind of ordinary Portland cement, dispersible latex powder, quartz sand, quartz powder, cellulose ether, One-component polymer cement waterproof mortar composed of silica fume, water reducing agent and defoamer; CN 10343969 A discloses a kind of ordinary Portland cement 52.5, granulated blast furnace powder 95#, penetrating agent (fatty alcohol polyoxygen Vinyl ether), expansion agent (ettringite or calcium hydroxide, magnesium hydroxide), silica fume, quartz sand, modified bentonite, modified sodium silicate, complexing agent (polyacrylic acid), crystal precipitation agent (polyethylene Diol) to prevent cement leakage crystalline waterproof coatings, etc., its anti-carbonization ability is still not ideal enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbonization-resistant waterproof slurry
  • Carbonization-resistant waterproof slurry
  • Carbonization-resistant waterproof slurry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Example 1 Prepare the anti-carbonization waterproof slurry of the present invention according to the following formula and steps:

[0055] (1) Accurately weigh the following materials according to the ratio:

[0056]

[0057] (2) The carbonization inhibitor is prepared by the following steps: conduct ultrasonic atomization at a frequency of 60kHz, first atomize mineral oil in the atomization chamber; then put calcium oxide and calcium-based montmorillonite powder into a high-speed mixer according to the formula ratio Mix uniformly in the medium to obtain a mixture powder of calcium oxide and calcium-based montmorillonite powder; then pass the prepared mixture powder into the atomization chamber through the feed port, and stay for 5 seconds to obtain the carbonization inhibitor;

[0058] (3) Put the cement, quartz powder and other materials of component A into the high-speed disperser, stir for 3 minutes, until the mixture is uniform, pack it, and then it can be m...

Embodiment 2

[0062] Example 2 Prepare the anti-carbonization waterproof slurry of the present invention according to the following formula and steps:

[0063] (1) Accurately weigh the following materials according to the ratio:

[0064]

[0065] (2) The carbonization inhibitor is prepared by the following steps: conduct ultrasonic atomization at a frequency of 55kHz, first atomize mineral oil in the atomization chamber; then put calcium oxide and calcium-based montmorillonite powder into a high-speed mixer according to the formula ratio Mix uniformly in the medium to obtain a mixture powder of calcium oxide and calcium-based montmorillonite powder; then pass the prepared mixture powder into the atomization chamber through the feed port, and stay for 10 seconds to obtain the carbonization inhibitor;

[0066] (3) Put the cement, quartz powder and other materials of component A into the high-speed disperser, stir for 2 minutes, until the mixture is uniform, pack it, and then it can be...

Embodiment 3

[0069] Example 3 Prepare the anti-carbonization waterproof slurry of the present invention according to the following formula and steps:

[0070] (1) Accurately weigh the following materials according to the ratio:

[0071]

[0072] (2) The carbonization inhibitor is prepared by the following steps: using compressed air atomization technology, the mineral oil is first atomized in the atomization chamber with a pressure of 0.25 MPa; then calcium oxide and calcium-based montmorillonite powder are placed in the high-speed Mix evenly in a mixer to obtain a mixture powder of calcium oxide and calcium-based montmorillonite powder; then pass the prepared mixture powder through the feed port into the atomization chamber, and stay for 1 second to obtain a carbonization inhibitor;

[0073] (3) Put the cement, quartz powder and other materials of component A into the high-speed disperser, stir for 3 minutes, until the mixture is uniform, pack it, and then it can be made into powd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a carbonization-resistant waterproof slurry. The carbonization-resistant waterproof slurry is a double-component organic / inorganic material composite slurry, and comprises cement, quartz powder, redispersible latex powder, cellulose ether, a super plasticizer, a water repellent, a carbonization inhibitor, an emulsion, water, an antifoaming agent, and an antiseptic. The carbonization inhibitor is prepared by modifying a mixture of calcium oxide and calcium montmorillonite powder with mineral oil, and effect controlling on release of active ingredients of the carbonization inhibitor can be realized via modification, so that compact and uniform waterproof layers are formed from the surface to the internal part of a coating thin layer, moisture penetration is prevented with high efficiency, excellent carbonization resistance and water resistance are obtained, and service life of the coating layer and concrete protection term are prolonged. Compatibility of the carbonization-resistant waterproof slurry with inorganic materials such as cement is excellent, and excellent carbonization resistance and water resistance can be obtained by a functional thin layer with a thickness of 1 to 2mm.

Description

technical field [0001] The invention relates to a waterproof slurry, in particular to an anti-carbonization waterproof slurry, which belongs to the technical field of waterproof materials in the construction industry. Background technique [0002] The so-called "carbonation" refers to the generation of Ca(OH) after the cement of the mixed concrete is hydrated. 2 , most of which exist in the concrete in a crystalline state, and become a reserve of pore fluid to maintain high alkalinity, and its pH value is 12.5~13.5. CO exists in the air 2 and moisture, CO in the air 2 It will penetrate into the concrete under the action of water and Ca(OH) 2 Reaction, reduce the pH value to 8.5~9.0, at this time the concrete has been carbonized. Carbonation of concrete is essentially a process in which the pH value of concrete decreases and loses its alkalinity. [0003] Concrete maintaining an alkaline environment is an important condition for the preservation of concrete structures an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B14/06
CPCC04B28/02C04B28/04C04B2111/00482C04B2111/22C09D1/08C04B14/06C04B14/324C04B24/2641C04B24/383C04B40/065C04B2103/32C04B2103/50C04B2103/65C04B14/104C04B14/322C04B22/064
Inventor 董峰亮方楚燕邓德安徐英陈激扬胡程丁天华梁至柔周碧平万德刚严昌俊阿那梁卓钧陈学静薛静
Owner 西卡德高(上海)建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products