Brominated butyl/chlorinated butyl rubber composition and preparation method thereof

A technology of chlorinated butyl rubber and brominated butyl rubber, which is applied in the field of rubber vulcanizate preparation, can solve the problems of high price, low tensile strength of gas mask cover material, and high cost of cover material, achieving low cost, Excellent anti-virus performance and excellent heat and oxygen aging resistance

Inactive Publication Date: 2015-04-22
NANJING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Guo Yuexin et al. (BIIR gas mask mask rubber formula design, 2010, Volume 57: 623) used brominated butyl rubber as the mask material, and the formula was 100 parts of BIIR, 3 parts of ZnO, 40 parts of N330, 15 parts of N220, 1 part of Vaseline, 2 parts of paraffin oil, 2 parts of DOS, 2 parts of DOP, 0.5 part of KH-550, 1 part of SA, 1 part of antioxidant, 1 part of TMTD and 0.6 part of DM, the tensile strength of the obtained material is 15.4MPa, The tear strength is 42KN.m-1, the brittleness temperature is -45℃, and the duration of anti-mustard gas of the sample is greater than 480min; the anti-virus prepared by bromobutyl rubber The tensile strength of the mask shell material is low, while the price of bromobutyl rubber is high, and the cost of the shell material is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh 80g of BIIR2222 and 20g of CIIR1066 raw rubber and place them in a blast oven at a constant temperature of 40°C for 24 hours. After plasticizing on the open mill for 10 minutes, blend BIIR2222 and CIIR1066 for 5 minutes, and add 1g of anti-aging agent in turn. and 0.5g of MgO, 1g of stearic acid, 55g of carbon black N220, 1g of paraffin oil, 0.5g of DOP and 0.5g of DBP, 1g of M and 1g of DM, 5g of zinc oxide and 0.3g of sulfur After the surface of the rubber material is smooth and shiny, thin the film. Put the mixed rubber at room temperature for 24 hours, measure its positive vulcanization time at 165°C with a vulcanizer, and vulcanize according to the positive vulcanization time on a 50t plate vulcanizer to obtain vulcanized rubber. The prepared vulcanizate has a tensile strength of 18.50MPa, an elongation at break of 539%, a 300% modulus of 9.30MPa, and a tear strength of 39.45KN . m -1 , the Shore hardness is 55, the tensile permanent deformation is only 10%...

Embodiment 2

[0036] The rubber matrix in the formula of Example 2 is 100g of BIIR raw rubber. During the operation, the plasticizing time on the BIIR rubber mill is 15min. Other formulas and operating steps are the same as in Example 1. The tensile strength of the prepared vulcanized rubber is 17.24MPa , the elongation at break is 567%, the 300% elongation strength is 8.24MPa, and the tear strength reaches 38.19KN . m -1 , the Shore hardness is 55, the tensile permanent deformation is only 10%, and the brittleness temperature is -50°C. After the vulcanized rubber is aged in hot air (70°C×72h), the tensile strength is 17.91MPa, and the elongation at break is 543%. The aging coefficient is 100%, and the sustainable time of vulcanized rubber against mustard gas is greater than 3600min.

Embodiment 3

[0038]In the formula of Example 3, the rubber matrix is ​​100g of CIIR raw rubber. During the operation, the plasticizing time on the CIIR rubber compound mill is 15min. Other formulas and operating steps are the same as in Example 1. The tensile strength of the prepared vulcanized rubber is 17.60MPa, the elongation at break is 518%, the 300% elongation strength is 9.88MPa, and the tear strength reaches 36.63KN . m -1 , the Shore hardness is 54, the tensile permanent deformation is only 9%, and the brittle temperature is -45°C. After the vulcanized rubber is aged in hot air (70°C×72h), the tensile strength is 17.62MPa, and the elongation at break is 507%. The aging factor is 98%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a brominated butyl / chlorinated butyl rubber composition for gas masks. The composition comprises the following components in parts by weight: 100 parts of rubber matrix, 50-60 parts of carbon black N220, 5 parts of zinc oxide, 0.1-0.5 part of sulfur, 1 part of stearic acid, 1-4 parts of plasticizer (paraffin oil: DOP (dioctyl phthalate): DBP (dibutyl phthalate) is 2: 1: 1), 2 parts of promoter, 1 part of anti-aging agent and 0.5 part of anti-scorching agent, wherein the rubber matrix is composed of brominated butyl rubber and chlorinated butyl rubber. As for vulcanized rubber prepared by using the brominated butyl / chlorinated butyl rubber composition, the tensile strength is 18.50MPa, the elongation at fracture is 539%, the 300% stretching strength is 9.30MPa, the tearing strength is 39.45kN.m<-1>, the Shore hardness is 54, the tension set is 10%, and the brittleness temperature is -50 DEG C; and after the vulcanized rubber is aged in hot air (70 DEG C * 72h), the tensile strength is 17.91MPa, the elongation at fracture is 569%, the aging coefficient achieves 100%, the sustainable time of resisting mustard gas of the vulcanized rubber is greater than 3600min, and the comprehensive performances of the vulcanized rubber can completely meet the performance requirements of cover body materials of the gas masks.

Description

technical field [0001] The invention relates to the technical field of rubber vulcanizate preparation, in particular to a blend of brominated butyl rubber and chlorinated butyl rubber used in gas mask rubber. Background technique [0002] Gas masks appeared after the use of poison in Germany in World War I. They are mainly used to protect the user's face, eyes and respiratory system from toxic gases and liquids, and to regulate the air. Therefore, it is usually required that the gas mask mask material has a long protection time against toxic gas or liquid, good weather aging resistance and thermal oxygen aging resistance, good low temperature resistance, good elasticity, small deformation, and should not change with temperature. It has large fluctuations, is non-toxic, harmless, non-irritating to the skin, has no special smell, has good process performance, and is convenient for processing and manufacturing. [0003] Early gas mask masks were made of natural rubber. Later, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/28C08K13/02C08K3/04C08K3/22C08K3/06C08K5/09
Inventor 贾红兵张佳佳王经逸张旭敏刘鹏章俆子钦何俊宽殷标房尔园李健
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products