Self-brazing material for welding aluminum-copper member

A component and self-brazing technology, used in welding/cutting media/materials, welding media, welding equipment, etc., can solve the problems of not meeting engineering application requirements, low strength of solder brazing joints, and high melting point of solder, and achieve plasticity. Good, improve the mechanical properties, the effect of high brazing seam strength

Active Publication Date: 2013-02-20
ZHENGZHOU RES INST OF MECHANICAL ENG CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current aluminum-silicon self-brazing filler metal has some shortcomings: the silicon content in the filler metal is high, the filler metal is brittle, and the processability is poor; the melting point of the solder filler metal is high (solidus temperature 577 ° C, liquidus temperature above 600 ° C) , which is very close to the melting point of 3-series and 6-series high-strength aluminum alloys, and brazing is more difficult; the strength of brazing joints with brazing filler metals is low, which cannot meet the requirements of engineering applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The proportioning of self-brazing filler metal of the present invention comprises 85% metal component and 15% fluoride component, and wherein metal component gets by weight percentage: 0.05%Hf, 0.1%Ge, 0.5%Ni, 1%Cu, 8%Si, the balance is Al; the fluoride is taken by weight percentage: 80%AlF 3 , 15%CsF, 5%KF;

[0029] The preparation method is:

[0030] In the first step, metal Ge and part of Al are smelted in an intermediate frequency furnace to form master alloy A1, the weight ratio of Ge and Al in the master alloy A1 is Al:Ge=95:5; high melting point metal Hf and part of Al are smelted into Master alloy A2, the weight ratio of Hf and Al in this master alloy A2 is Al:Hf=99:1;

[0031] In the second step, after melting the remaining Al raw materials in a vacuum furnace, the temperature of the molten aluminum in the furnace rises to 650-800°C (preferably 800°C), and then the raw material Si (crystal block) is added, and the temperature is kept for 10-20 minutes (prefer...

Embodiment 2

[0039] The proportioning of self-brazing filler metal of the present invention comprises 86% metal component and 14% fluoride component, and wherein metal component gets by weight percentage: 0.05%Hf, 0.1%Ge, 0.8%Ni, 1%Cu, 9%Si, the balance is Al; the fluoride is taken by weight percentage: 70%AlF 3 , 25%CsF, 5%KF.

Embodiment 3

[0041] The proportioning of self-brazing filler metal of the present invention comprises 87% metal component and 13% fluoride component, and wherein metal component gets by weight percentage: 0.15%Hf, 0.2%Ge, 0.8%Ni, 1.2%Cu, 10%Si, the balance is Al; fluoride is taken by weight percentage: 65%AlF 3 , 30%CsF, 5%KF.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-brazing material for welding an aluminum-copper member. The self-brazing material comprises the following components: 12-15 percent of fluoride (30-80 percent of aluminum fluoride, 5-35 percent of caesium fluoride and the balance of potassium fluoride), 0.01-0.3 percent of hafnium, 0.01-0.8 percent of germanium, 0.05-2 percent of nickel, 0.8-3 percent of copper, 5-17 percent of silicon and the balance of aluminum. The self-brazing material is prepared through the following steps of: smelting and atomizing the raw materials of hafnium, the germanium, the nickel, the copper, the silicon and the aluminum in a vacuum furnace into fine powder; and then uniformly mixing with the fluoride, pressing into a composite ingot, directly extruding the composite ingot into a yarn or pipe, and winding the yarn into a coil or cutting the pipe into a ring to obtain the self-brazing material. The self-brazing material disclosed by the invention has the advantages that trace elements of Ge and Hf are introduced on the basis of the traditional Al-Si-Cu-Ni alloy system brazing material, so that the brazing material smelting temperature is lowered, the burning loss of an aluminum base material during welding is favorably avoided, the strength and plasticity of the brazing material are improved, the mechanical property of a brazing joint is favorably improved, and the improvement of the plasticity of the brazing material can ensure that the production efficiency is increased.

Description

technical field [0001] The invention relates to a brazing filler metal for aluminum-copper and its alloys, in particular to a self-brazing filler metal for welding aluminum-copper components. Background technique [0002] Aluminum alloys are widely used in industrial production and social life. Due to their small specific gravity, good electrical and thermal conductivity, excellent castability, plasticity and machinability, aluminum alloys play an irreplaceable role in modern industrial materials. The use of 3-series (such as 3003 aluminum alloy) and 6-series (such as 6061 aluminum alloy) high-strength aluminum alloys to manufacture all-aluminum structural parts to replace copper structural parts has become the development direction of the world's manufacturing industry. However, there are more and more welding problems for aluminum and copper components. [0003] The main problem in the welding of aluminum-copper components is not only that dense oxide films are easily for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/28B23K35/36B23K35/40
Inventor 龙伟民黄俊兰鲍丽钟素娟沈元勋孙华为朱坤张强程亚芳潘建军黄成志
Owner ZHENGZHOU RES INST OF MECHANICAL ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products