Waterproof concrete compacting agent and preparation method thereof

A waterproof and dense concrete technology, applied in the field of building material additives, can solve the problems of inability to achieve the effect of waterproofing agent, poor waterproof effect, and easy to corrode steel bars, etc., to reduce construction costs, prevent water molecule penetration, and improve strength.

Active Publication Date: 2012-10-10
北京龙阳伟业科技股份有限公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many types of waterproofing agent products in our country, which are mainly used to improve the impermeability and crack resistance of concrete and reduce shrinkage. However, these products contain more chloride components because chloride ions are harmful to concrete. Use It is easy to corrode the steel bars later, and the waterproof effect is not good in the later stage, or because the waterproofing agent will increase shrinkage after use, causing concrete cracking, or the waterproofing agent is a powder product, and it needs to be mixed in more during use. Therefore, due to various objective factors, the waterproofing agent products in the current market often have many adverse reactions in the actual use of the project, and cannot achieve the ideal effect of using the waterproofing agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Consists of raw material components in the following weight ratios:

[0012] Potassium hydroxide 10%-13%;

[0013] Volcanic ash 0.5%-1%;

[0014] Potassium oleate 0.5%-1%;

[0015] Sulfur 10%-12%;

[0016] Glycerol 0.5%-1%;

[0017] Aminotriethanol 4%;

[0018] Citric acid 0.5%-1%;

[0019] Ferric oxide 1%;

[0020] Sodium fluorosilicate 0.5%-1%;

[0021] The rest is water.

Embodiment 2

[0023] Consists of raw material components in the following weight ratios:

[0024] Potassium hydroxide 13%;

[0025] Volcanic ash 1%;

[0026] Potassium oleate 1%;

[0027] Sulfur 12%;

[0028] Glycerol 1%;

[0029] Aminotriethanol 5%;

[0030] Citric acid 1%;

[0031] Ferric oxide 0.5%;

[0032] Sodium fluorosilicate 0.5%;

[0033] The rest is water.

Embodiment 3

[0035] Consists of raw material components in the following weight ratios:

[0036] Potassium hydroxide 10%;

[0037] Volcanic ash 0.5%;

[0038] Potassium oleate 0.5%;

[0039] Sulfur 10%;

[0040] Glycerol 0.5%;

[0041] Aminotriethanol 3%;

[0042] Citric acid 0.5%;

[0043] Ferric oxide 1%;

[0044] Sodium fluorosilicate 0.5%-1%;

[0045] The rest is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof concrete compacting agent and a preparation method thereof. The compacting agent consists of the following raw material components in percentage by weight: 10 to 13 percent of potassium hydroxide, 0.5 to 1 percent of volcanic ash, 0.5 to 1 percent of potassium oleate, 10 to 12 percent of sulfur, 0.5 to 1 percent of glycerol, 3 to 5 percent of triethanolamine, 0.5 to 1 percent of citric acid, 0.5 to 1.5 percent of ferric oxide, 0.5 to 1 percent of sodium fluosilicate, and the balance of water. Chemical crystal or colloid generated by chemical reaction of components in the compacting agent and silicon, calcium, sodium, magnesium and the like in cement can effectively prevent permeation of water molecules and effectively control cracking. The compacting agent contains extremely low harmful substances, particularly has extremely low chlorine ion content and ammonia content, reduces damage to steel bars and concrete, and is beneficial to environmental protection.

Description

Technical field: [0001] The invention relates to a building material additive, in particular to a concrete waterproof compacting agent widely used in basements, swimming pools, canals, tunnels, cable trench projects and building structures for waterproofing and anti-seepage and a preparation method thereof. Background technique: [0002] At present, there are many types of waterproofing agent products in our country, which are mainly used to improve the impermeability and crack resistance of concrete and reduce shrinkage. However, these products contain more chloride components because chloride ions are harmful to concrete. Use It is easy to corrode the steel bars later, and the waterproof effect is not good in the later stage, or because the waterproofing agent will increase shrinkage after use, causing concrete cracking, or the waterproofing agent is a powder product, and it needs to be mixed in more during use. Therefore, due to various objective factors, the current wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/50C04B24/12
Inventor 王伟高惠子
Owner 北京龙阳伟业科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products