Reactive graphtic carbon nanofiber reinforced polymeric composites

a graphene carbon nanofiber and polymer composite technology, applied in the preparation of carboxylic acid halides, carboxylic acid halide preparations, liquid carbonaceous fuels, etc., can solve the problems of preventing the efficient transfer of nanofiber properties to the composite matrix, affecting the wetting efficiency and high dispersion of carbon nanofibers within the polymer matrix, and affecting the uniform dispersion of nanofibers

Inactive Publication Date: 2012-03-15
LUKEHART CHARLES M +3
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Those studies show that efficient wetting and high dispersion of carbon nanofibers within a polymer matrix continues to be problematic.
Obtaining uniform dispersions of nanofiber reinforcement within a polymer-matrix is another critical issue in nanocomposite processing.
Nanofiber agglomeration inhibits their uniform dispersion in composite materials and prevents efficient transfer of nanofiber properties to the composite matrix.
Greatly enhanced performance of nanocomposite materials reinforced with nanotube or nanofiber additives has not been fully achieved because of difficulties in achieving efficient dispersion and wetting of the nanoscale component within the matrix material, even when using surface-functionalized additives.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reactive graphtic carbon nanofiber reinforced polymeric composites
  • Reactive graphtic carbon nanofiber reinforced polymeric composites
  • Reactive graphtic carbon nanofiber reinforced polymeric composites

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0095]Preparation of GCNFs Surface-Derivatized with Oxydianiline (GCNFODA) Herringbone-type carbon nanofibers were synthesized as disclosed in U.S. Pat. No. 6,537,515 B1 and U.S. Patent Publication No. 2002 / 0054849 AI. A sample of as-prepared herringbone GCNFs was heated with concentrated nitric acid at 140° C. for 4 h. The collected oxidized GCNFs were washed with deionized water until the filtrate reached a pH value near 7 and then were dried at reduced pressure at room temperature. The dry, oxidized GCNFs were activated by reaction with thionyl chloride containing a small amount of dimethylformamide (DMF) at 70° C. for 24 h.

[0096]The reaction mixture was cooled and then filtered. The collected fibers were washed with tetrahydrofuran (THF) under nitrogen until the supernatant was colorless. The black solid was dried at room temperature and then reacted with excess oxydianiline (ODA) at 100° C. under nitrogen for 96 h. The mixture was cooled to room temperature. Excess oxydianiline...

example 2

[0098]Surface-derivatized GCNF-ODA nanofibers having dimensions of 50 to 200 nm wide and 5 to 10 microns long were reduced in length by ultrasonication using a commercial sonifier at a power level of 70 watts for a 60-min duration. Unexpectedly, ultrasonication of the surface-derivatized nanofibers has resulted in the production of composites having unusually high degrees of flexural strength. A diluent, butyl glycidyl ether (Aldrich Chemical Co.), was used as dispersant for this cutting procedure. The cut fiber / diluent mixture was stored in a sealed vessel for over 30 h at room temperature and was then divided into two parts. One portion was directly added into an epoxy resin, the other part was first dried in a vacuum oven at 100° C. for 2 days and then dispersed in epoxy resin. For each procedure, nanocomposites with fiber loadings of 0.3 wt % and 1.3 wt % were prepared. Two commercial liquid bisphenol A based epoxy resins, Epon® 828 with viscosity of 110-150 poise and 826 with v...

example 3

[0102]In one example of the present invention, r-GCNF-ODA derivatized nanofibers were found to be useful as reactive reinforcement for epoxy resin composite materials. Such fibers are “reactive” GCNF formed when GCNF-ODA fibers are reacted with epoxy monomer. (These fibers are shown in FIG. 4.) Mild sonication readily dispersed the shortened nanofiber segments throughout an epoxy resin. In addition, extension of the original ODA linker molecule to an ODA(glycidyl)n linker enhanced the wettability of the GCNF reinforcement material and reduced or eliminated any possible steric hindrance by the nanofiber bulk on further chemical reactivity at the linker molecule terminus, thereby facilitating covalent coupling across the GCNF / epoxy matrix interface during thermal curing.

[0103]Both r-GCNF-ODA / epoxy mixtures and the thermally cured r-GCNFODA / epoxy composite monoliths were found to exhibit a uniform, black appearance with no visual evidence of phase separation.

[0104]TGA degradation curve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthsaaaaaaaaaa
lengthsaaaaaaaaaa
lengthsaaaaaaaaaa
Login to view more

Abstract

Composites comprising at least one graphite-carbon nanofiber (GCNF) and a polymer phase covalently linked to a surface thereof.

Description

CROSS-REFERENCE(S) TO RELATED APPLICATION(S)[0001]This application is a divisional of, and claims a benefit of priority under 35 U.S.C. 120 from co-pending utility patent application U.S. Ser. No. 11 / 177,481, filed Jul. 11, 2005, which in-turn claims a benefit of priority under 35 U.S.C. 119(e) from provisional patent application U.S. Ser. No. 60 / 586,688, filed Jul. 9, 2004, both of which are hereby expressly incorporated herein by reference for all purposes.FIELD OF THE INVENTION[0002]The present invention relates to covalently bonded GCNF-polymer composites.BACKGROUND OF THE INVENTION[0003]Carbon fibers are widely used as reinforcement for advanced polymeric matrix composites in many high-technology applications because of their high specific stiffness, strength, and excellent electrical and thermal properties. Carbon fibers have many forms, depending on the synthesis methods used. Conventional carbon fibers such as those obtained by pyrolyzing polyacrylonitrile (PAN) resins or ot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(United States)
IPC IPC(8): C08K9/04C08L25/06C08L77/00C08L63/00C07C53/128C07C51/16C07C51/60C07C233/00C07C231/02C08L23/02C07C53/42B82Y30/00B82Y40/00
CPCC08K3/04C08K3/046C08L63/00C08L101/00
Inventor LUKEHART, CHARLES M.ZHONG, WEI HONGLI, JIANGMOWLES, ERIC D.
Owner LUKEHART CHARLES M
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka