Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Firing kiln and process for producing ceramic member therewith

A manufacturing method and component technology, applied in the direction of furnaces, furnace linings, muffle furnaces, etc., can solve problems such as the reduction of the effect of the heat insulation layer, the reduction of the heat insulation of the heat insulation layer, and the deformation of ceramic fibers, so as to prevent cracks, prevent damage, and heat insulation performance excellent effect

Inactive Publication Date: 2007-05-30
IBIDEN CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] If the thermal insulation performance of the thermal insulation layer is reduced in this way, there will be the following problems: due to the temperature rise of the outermost layer, the softening of the ceramic fiber itself will cause deformation, and the function as a thermal insulation layer will be reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Firing kiln and process for producing ceramic member therewith
  • Firing kiln and process for producing ceramic member therewith
  • Firing kiln and process for producing ceramic member therewith

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0100] (1) Fabricate a firing furnace as shown in FIG. 1, and make the innermost layer as a layer 13a made of carbon parts (FR200 / OS manufactured by Kureha Chemical Industry Co., Ltd., density: 0.16 g / cm 3 , thickness: 50mm), the second layer is made of a layer 13b made of carbon parts (FR200 / OS manufactured by Kureha Chemical Industry Co., Ltd., density: 0.16g / cm 3 , thickness: 50mm), while the outermost layer is made of carbon insulation material layer 130 (density: 0.16g / cm 3 , thickness: 25mm) and carbon fiber layer 131 (density: 0.1g / cm 3 , Thickness: 25mm) composite layer (manufactured by Kureha Chemical Industry Co., Ltd.), in an atmosphere of argon gas at normal pressure, set the maximum temperature in the muffle furnace to 2200 ° C, and pass through to the center of the heating chamber Thermocouples were inserted into the heat insulating material, and the temperature of the heat insulating layer 13 was measured at various positions shown in FIG. 2 .

[0101] As a r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

A firing kiln that is free from any substantial drop of heat insulating performance of heat insulating layer, being free from any splitting into two parts or exfoliation of heat insulating layer, and that excels in long-term durability and heat efficiency. There is provided a firing kiln comprising a muffle formed so as to ensure a space for accommodation of moldings to be fired, a heater, or heating element functioning as a heater, disposed outside the muffle and multiple heat insulating layers disposed so as to enclose the muffle and the heater, characterized in that the heat insulating layers are made of carbon and fixed by means of holdbacks of carbon.

Description

technical field [0001] This application claims priority based on Japanese Patent Application No. 2004-233626 filed on August 10, 2004. [0002] The present invention relates to a firing furnace used for producing ceramic components such as a ceramic honeycomb structure and a method for producing ceramic components using the firing furnace. Background technique [0003] Various exhaust gas-purifying honeycomb filters and catalyst supports for purifying exhaust gas discharged from vehicles such as buses and trucks and internal combustion engines of construction machinery have been proposed. [0004] As such a honeycomb filter for purifying exhaust gas, a honeycomb structure containing a non-oxide ceramic porous material such as silicon carbide, which is very excellent in heat resistance, is used. [0005] Conventionally, for example, Patent Document 1 and Patent Document 2 describe firing furnaces for producing such non-oxide ceramic components. [0006] A firing furnace for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F27B5/08C04B35/64F27D1/14
CPCF27D1/0003F27B5/08F27D1/14F27B5/14
Inventor 西城贵满广嵨裕一樋口宏司
Owner IBIDEN CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com