Starlight dry granules and preparation method thereof, glazed ceramic tile with starlight effect and preparation method and application of glazed ceramic tile

A technology of ceramic tiles and starlight, which is applied in the field of ceramic wall and floor tiles, can solve problems such as limitations, and achieve the effect of outstanding decorative effect, strong artistic atmosphere and high-efficiency process.

Active Publication Date: 2022-08-05
GUANGDONG NEWPEARL CERAMIC GRP CO LTD +4
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, with the industrialized mass production of antique wall and floor tiles, their homogeneity is serious, and the gloss is generally between 8 and 12 degrees. Limited by product category

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Starlight dry granules and preparation method thereof, glazed ceramic tile with starlight effect and preparation method and application of glazed ceramic tile
  • Starlight dry granules and preparation method thereof, glazed ceramic tile with starlight effect and preparation method and application of glazed ceramic tile
  • Starlight dry granules and preparation method thereof, glazed ceramic tile with starlight effect and preparation method and application of glazed ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0085] According to a second aspect of the present invention, there is provided a preparation method of star dry granules, comprising the following steps:

[0086] The components are mixed in proportion and melted into a liquid, then quenched, and then pulverized and sieved to obtain star dry granules.

[0087] The preparation method of star dry granules provided by the present invention is simple and efficient.

[0088] The components of the starlight dry particles of the present invention include waste glass (SiO 2 ), corundum (Al 2 O 3 ), tremolite, kaolin, potassium feldspar, albite, borax, potassium carbonate, sodium carbonate, barium carbonate and fluorite. , has a high silicon-alumina ratio, and the presence of tremolite can greatly improve the reflectivity of dry particles. When it is used in ceramic products, the pits left after brushing and polishing have high reflectivity, so that the The ceramic products have the effect of starry sky under the illumination of l...

Embodiment 1

[0158] A preparation method of a glazed ceramic tile with starlight effect, comprising the following steps:

[0159] 1. To prepare the green body powder and press the ceramic tile blanks, the powder materials used are ordinary antique type, large slab body powder or slate green body powder. The used green body powder or pressing specifications will not affect the starry sky glaze effect. ;

[0160] 2. Prepare the base glaze:

[0161] The base glaze consists of the following components: SiO 2 58.6%, Al 2 O 3 24.5%, CaO 1.8%, MgO 4.2%, K 2 O 2.8%, Na 2 O 3.9% and ZnO 4.2%;

[0162] The ingredients are mixed in proportion, and then ball milled to control the fineness at 325 mesh sieve and 0.6%;

[0163] 3. Preparation of protective glaze:

[0164] The protective glaze includes the following components in parts by weight:

[0165] 45 parts of frit, 10 parts of air knife clay, 7 parts of calcined kaolin, 9 parts of calcite, and 4 parts of zinc oxide;

[0166] Wherein, the...

Embodiment 2

[0192] The difference between this example and Example 1 is that the star dry particles in this example include the following components in parts by weight:

[0193] 18 parts of waste glass, 8 parts of corundum, 15 parts of tremolite, 30 parts of kaolin, 30 parts of potassium feldspar, 25 parts of albite, 4 parts of borax, 6 parts of potassium carbonate, 12 parts of sodium carbonate, 10 parts of barium carbonate, and 7 copies of fluorite;

[0194] The rest are the same as in Example 1, and a glazed ceramic tile with starlight effect is obtained.

[0195] Compared with Example 1, in this example, by adjusting the formula, the consumption of waste glass is reduced, and the consumption of albite is increased at the same time, and the obtained product also has a starry sky effect. figure 2 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides starlight dry granules and a preparation method thereof, a glazed ceramic tile with a starlight effect and a preparation method and application of the glazed ceramic tile, and relates to the technical field of ceramic wall and floor tiles. The starlight dry granules are prepared from the following components in parts by weight: 18 to 30 parts of waste glass, 5 to 8 parts of corundum, 10 to 15 parts of tremolite, 15 to 30 parts of kaolin, 20 to 30 parts of potassium feldspar, 20 to 30 parts of albite, 3 to 5 parts of borax, 5 to 10 parts of potassium carbonate, 8 to 16 parts of sodium carbonate, 8 to 10 parts of barium carbonate and 5 to 8 parts of fluorite. The problems that traditional glazed ceramic tiles are single in type, and consequently selection of consumers is limited are solved, and the technical effects that the ceramic tiles have the effect like stars in the sky, the artistic atmosphere is strong, and the types of the ceramic tiles are increased are achieved.

Description

technical field [0001] The invention relates to the technical field of ceramic wall and floor tiles, in particular to a starlight dry particle and a preparation method thereof, a glazed ceramic tile with starlight effect, and a preparation method and application thereof. Background technique [0002] With the application of various new materials, the types and effects of building wall and floor tiles are becoming more and more abundant. For example, full-throw wall and floor tiles have high gloss, which can achieve magnificent effects after being applied to home decoration. . However, with changes in aesthetic concepts, wall and floor tile products with antique-like effects are becoming more and more popular. [0003] At present, with the industrialized mass production of antique wall and floor tile products, the homogeneity is relatively serious, and the gloss is generally between 8-12 degrees, which makes consumers choose matt antique wall and floor tile products. Limite...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/06C04B41/89B28B11/04B28B11/06B28B11/00B28B11/08B24B1/00
CPCC03C8/06C04B41/52C04B41/89C04B41/009B28B11/044B28B11/06B28B11/001B28B11/0845B24B1/00C04B33/00C04B35/00C04B41/5022C04B41/4545Y02P40/60
Inventor 黄春林陈育昆仝松贞徐雪英朱光耀谢怡伟宁毓胜傅建涛刘光荣曾惠孙彭中华戴志梅袁小娣简润桐叶德林
Owner GUANGDONG NEWPEARL CERAMIC GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com