Method for degrading organic pollutants by activating persulfate with supported alumina particles

A technology for activating persulfate and alumina particles, which is applied in the field of environmental pollutant treatment, can solve the problems of low activation efficiency and uneven mixing of agents, and achieve the effects of improving degradation effect, high catalytic activation activity, and avoiding agglomeration

Pending Publication Date: 2022-04-12
王晶晶
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method is prone to problems such as uneven mixing of agents and low activation efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for activating persulfate to degrade organic pollutants with supported alumina particles, characterized in that it comprises the following steps:

[0031] Step S101, loading of transition metal active components: the alumina quantum dots and activated alumina x-ρ Al 2 o 3 After mixing evenly, the carrier is obtained; then the carrier is dispersed in ethanol, triethoxysilylacetic acid is added to it, stirred and reacted at 50°C for 3 hours, and the ethanol is removed by rotary evaporation to obtain a modified carrier, and then the modified The carrier was added to the transition metal ion salt solution, stirred vigorously for 1 hour to form a uniform suspoemulsion, evaporated to dryness with a rotary evaporator, and then dried to a constant weight in a 105°C drying oven, and finally placed in a 600°C muffle Burn in the furnace for 1 hour to obtain the intermediate product;

[0032]Step S102. Ionized modification of 2,5-bis(diethylamino)phenyl-1,3,4-oxadiazole ...

Embodiment 2

[0042] A method for activating persulfate to degrade organic pollutants with supported alumina particles, characterized in that it comprises the following steps:

[0043] Step S101, loading of transition metal active components: the alumina quantum dots and activated alumina x-ρ Al 2 o 3 After mixing evenly, the carrier is obtained; then the carrier is dispersed in ethanol, triethoxysilylacetic acid is added to it, stirred and reacted at 55°C for 3.5 hours, and the ethanol is removed by rotary evaporation to obtain a modified carrier, and then the modified The carrier was added to the transition metal ion salt solution, stirred vigorously for 1.2 hours to form a uniform suspoemulsion, evaporated to dryness with a rotary evaporator, and then dried to a constant weight in a 108°C drying oven, and finally in a 620°C muffle Burn in the furnace for 1.2 hours to obtain the intermediate product;

[0044] Step S102. Ionized modification of 2,5-bis(diethylamino)phenyl-1,3,4-oxadiazol...

Embodiment 3

[0053] A method for activating persulfate to degrade organic pollutants with supported alumina particles, characterized in that it comprises the following steps:

[0054] Step S101, loading of transition metal active components: the alumina quantum dots and activated alumina x-ρ Al 2 o 3 After mixing evenly, the carrier is obtained; then the carrier is dispersed in ethanol, triethoxysilylacetic acid is added to it, stirred and reacted at 60°C for 4 hours, and the ethanol is removed by rotary evaporation to obtain a modified carrier, and then the modified The carrier was added to the transition metal ion salt solution, stirred vigorously for 1.5 hours to form a uniform suspoemulsion, evaporated to dryness with a rotary evaporator, and then dried to a constant weight in a 110°C drying oven, and finally in a 650°C muffle Burn in the furnace for 1.5 hours to obtain the intermediate product;

[0055] Step S102. Ionized modification of 2,5-bis(diethylamino)phenyl-1,3,4-oxadiazole ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for degrading organic pollutants by activating persulfate with supported alumina particles, which comprises the following steps: step S101, loading of active components of transition metal, step S102, ionization modification of 2, 5-bis (diethylamino) phenyl-1, 3, 4-diazole with chloromethyl triethoxy silane, step S103, loading of a copper metal organic framework, and step S104, degradation of organic pollutants. The method for degrading the organic pollutants by activating the persulfate with the supported alumina particles, disclosed by the invention, is high in organic pollutant degradation efficiency, remarkable in effect, small in agent mixing amount and good in environmental protection property.

Description

technical field [0001] The invention relates to the technical field of environmental pollutant treatment, in particular to a method for degrading organic pollutants by activating persulfate with supported alumina particles. Background technique [0002] In recent years, with the rapid development of my country's economy and the advancement of global industrialization, a large number of toxic and harmful organic pollutants have entered the environmental water body in the process of production and use, causing serious water pollution. Among them, a variety of organic pollutants have low-dose effects, persistence, and bioaccumulation, and can be transmitted between populations through the food chain. They have obvious teratogenic, carcinogenic, and mutagenic effects, which seriously threaten aquatic organisms and even human health. , it can be seen that efficient and convenient water treatment technology is urgently needed in this field for pollution control. [0003] At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/72B01J31/22C02F101/30
CPCY02W10/37
Inventor 王晶晶
Owner 王晶晶
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com