High-temperature-resistant anti-rutting asphalt mixture

An asphalt mixture, anti-rutting technology, applied in the field of asphalt mixture to achieve the effect of improving anti-cracking, high practicability and excellent anti-rutting ability

Active Publication Date: 2021-04-20
唐山天跃建材有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of high temperature resistant anti-rutting asphalt mixture and its preparation method, to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] S1: Prepare materials;

[0049] S2: Preparation of porous additives:

[0050] Take 2-bromoisobutyryl bromide, dissolve it in ether, and stir for 10 minutes to obtain solution A; take ethylene glycol, dissolve it in ether, stir for 10 minutes, then place it in an ice-water bath, slowly add solution A dropwise, and stir at room temperature for 16 hours to obtain trigger agent;

[0051] Take the initiator, catalyst, 1,1,4,7,10,10-hexamethyltriethylenetetramine and styrene, mix and stir for 10 minutes, freeze, vacuumize, heat under nitrogen atmosphere until the materials are dissolved, and place Heat in an oil bath at 110°C for 7 hours, add toluene and alumina, continue to stir for 15 minutes, then add ethanol, collect the precipitate, and dry it in vacuum at 60°C to obtain modified polystyrene;

[0052] Take modified polystyrene, dissolve in toluene, add triethylaluminum toluene solution, stir for 12 hours, add L-lactide under nitrogen environment, continue to freeze, va...

Embodiment 2

[0064] S1: Prepare materials;

[0065] S2: Preparation of porous additives:

[0066] Take 2-bromoisobutyryl bromide, dissolve it in ether, and stir for 15 minutes to obtain solution A; take ethylene glycol, dissolve it in ether, stir for 15 minutes, then place it in an ice-water bath, slowly add solution A dropwise, and stir at room temperature for 18 hours to obtain Initiate agent;

[0067] Take the initiator, catalyst, 1,1,4,7,10,10-hexamethyltriethylenetetramine and styrene, mix and stir for 15 minutes, freeze, vacuumize, heat under nitrogen atmosphere until the materials are dissolved, and place Heat in an oil bath at 112°C for 7.2h, add toluene and alumina, continue to stir for 18min, then add ethanol, collect the precipitate, and dry it in vacuum at 60°C to obtain modified polystyrene;

[0068] Take modified polystyrene, dissolve in toluene, then add the toluene solution of triethylaluminum, stir for 13 hours, add L-lactide under nitrogen atmosphere, continue to freeze...

Embodiment 3

[0080] S1: Prepare materials;

[0081] S2: Preparation of porous additives:

[0082] Take 2-bromoisobutyryl bromide, dissolve it in ether, and stir for 20 minutes to obtain solution A; take ethylene glycol, dissolve it in ether, stir for 20 minutes, then place it in an ice-water bath, slowly add solution A dropwise, and stir at room temperature for 20 hours to obtain trigger agent;

[0083] Take the initiator, catalyst, 1,1,4,7,10,10-hexamethyltriethylenetetramine and styrene, mix and stir for 20 minutes, freeze, vacuumize, heat under nitrogen atmosphere until the materials are dissolved, and place Heat in an oil bath at 115°C for 7.5h, add toluene and alumina, continue to stir for 20min, then add ethanol, collect the precipitate, and dry it in vacuum at 60°C to obtain modified polystyrene;

[0084]Take modified polystyrene, dissolve in toluene, then add the toluene solution of triethylaluminum, stir for 14 hours, add L-lactide under nitrogen environment, continue to freeze,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature-resistant anti-rut asphalt mixture which comprises the following raw materials in parts by weight: 15-18 parts of pretreated asphalt, 30-35 parts of zinc chloride, 5-10 parts of heat conduction material, 8-12 parts of glass fiber, 5-10 parts of admixture and 90-100 parts of aggregate. The pretreated asphalt is prepared from the following raw materials in parts by weight: 8-14 parts of modified asphalt, 6-8 parts of dihydroxyl-terminated polydimethylsiloxane, 14-16 parts of polycaprolactone glycol, 2-4 parts of 1, 6-hexamethylene diisocyanate, 0.5-1 part of dibutyltin dilaurate and 4-6 parts of 4, 4'-dimethyl-2, 2'-dipyridyl, and 0.5-0.8 part of 1, 4-butanediol. The preparation method is reasonable in process design and proper in component proportion, the prepared asphalt mixture has excellent anti-rutting capacity, the high-temperature stability and the water stability of the asphalt mixture are improved, and the asphalt mixture can be applied to roads with large traffic volume and more heavy-load and overload vehicles and has higher practicability.

Description

technical field [0001] The invention relates to the technical field of asphalt mixture, in particular to a high-temperature-resistant and rutting-resistant asphalt mixture. Background technique [0002] Asphalt mixture is a composite material, mainly composed of asphalt, coarse aggregate, fine aggregate, mineral powder, and some polymers and wood cellulose are added; different structures are formed by mixing these materials with different qualities and quantities. And have different mechanical properties; the material is widely used in road traffic and housing construction in various cities. [0003] Today's asphalt pavement is exposed to the outdoors for a long time, and factors such as temperature changes and ultraviolet radiation will cause the aging of the asphalt mixture. At the same time, higher requirements are placed on the high temperature stability and rutting resistance of the asphalt mixture. [0004] Aiming at this problem, we have designed a high-temperature-r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32C04B111/20
CPCC04B26/32C04B24/36C04B24/283C04B24/125C04B24/40C04B24/128C04B24/026C04B24/281C04B24/282C04B2103/0068C04B24/2676C04B24/045C04B22/12C04B22/085C04B22/0013C04B22/124C04B14/42C04B14/02C04B18/146C04B18/08C04B14/00Y02W30/91
Inventor 马瓯丽
Owner 唐山天跃建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com