Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for steel parts and steel, applied in the field of material surface treatment, can solve the problems of uncoordinated consideration and inability to take into account the corrosion resistance of blackened film, and achieve the effects of ensuring adhesion, reducing poor blackening, and controlling the production process.
Pending Publication Date: 2021-04-06
东莞市慧泽凌化工科技有限公司
View PDF7 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Through the two-step treatment, the adhesion problem of the blackening film has been greatly improved. However, most of the pre-treatment and blackening treatment are not coordinated. The subsequent blackening treatment is only for the blackening film with color correction, and the blackening film Corrosion resistance can not be balanced
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] A method for blackening steel parts, comprising the following steps:
[0029]1) Carry out pre-treatment on the steel parts to expose the clean and active surface of the steel parts;
[0030] a) Degreasing: Put the steel parts to be treated in a commercially available steel degreasing agent (CW-6008 produced by Dongguan Huizeling Chemical Technology Co., Ltd.) for ultrasonic cleaning for 5 minutes, set the temperature to 60°C, and wash them with water after degreasing ;
[0031] b) Activation or derusting: soak the degreasing steel parts in 30% hydrochloric acid aqueous solution for 3 minutes, set the temperature to normal temperature, and rinse with water after activation;
[0032] 2) Soak the steel parts after pretreatment in the pretreatment potion for 1 minute, set the temperature to normal temperature, and wash them with water after pretreatment; wherein, the pretreatment potion consists of 2g / l phosphoric acid, 5g / l dihydrogen phosphate Zinc, 1g / l titanate coupli...
Embodiment 2
[0036] The difference with embodiment 1 is:
[0037] In this embodiment, the pretreatment potion is adjusted to 2g / l of phosphoric acid, 5g / l of manganese dihydrogen phosphate, 1g / l of γ-(2,3-epoxypropoxy)propyltrimethoxysilane coupling agent, It is prepared by dissolving 1g / l dodecylamine polyoxyethylene ether and 1g / l sodium fluoride in pure water.
[0038] The rest are the same as in Embodiment 1, and will not be repeated here.
Embodiment 3
[0040] The difference with embodiment 1 is:
[0041] In this embodiment, the blackening potion is adjusted to 3g / l copper sulfate, 3g / l ammonium molybdate, 3g / l dithiodiacetic acid, 1g / l benzoic acid and 1g / l zirconate coupling Prepared by dissolving in water.
[0042] The rest are the same as in Embodiment 1, and will not be repeated here.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the technical field of material surface treatment, and particularly relates to a steel piece blackening method. The steel piece blackening method comprises the following steps of (1) pretreating a steel piece to expose a clean and active surface of the steel piece; (2) soaking the pretreated steel piece in a preliminary treatment solution to finish preliminary treatment; (3) soaking the steel piece completing preliminary treatment in a blackening solution to finish blackening treatment; (4) putting the blackened steel piece product into hot water for hot washing, then soaking the blackened steel piece product in dehydrating anti-rust oil, and finally drying the blackened steel piece product by cold air; wherein the preliminary treatment solution comprises phosphoric acid or phosphate, a coupling agent, an amine surfactant and a film forming accelerator, and the blackening solution comprises main salt, a complexing agent, a blackening agent, a pH value stabilizer and a coupling agent. Compared with the prior art, the steel piece blackening method can ensure that the formed blackening film has good adhesive force and corrosion resistance.
Description
technical field [0001] The invention belongs to the technical field of material surface treatment, and in particular relates to a method for blackening steel parts. Background technique [0002] Steel structural products have become an indispensable raw material for the rapid development of today's society, and the steel blackening process is one of the most important surface treatment processes for steel parts. The traditional steel blackening process uses strong alkali and nitrate or nitrite at 130 Blackening at ~150°C for 30 to 50 minutes has many disadvantages such as long processing time, high energy consumption, and low efficiency, which have been criticized by practitioners. With the development of science and technology, in the past ten years, many normal temperature iron and steel blackening agents have emerged on the market. If the film is not well controlled, there will be disadvantages such as poor adhesion and poor corrosion resistance. Therefore, how to make ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.