Streak fish belly white quartz stone plate and preparation method thereof

A technology of quartz stone slabs and fish-belly white, which is applied in stone processing equipment, stone processing tools, building materials, etc., can solve problems such as unnaturalness, hardness, and large color difference, and achieve bright and translucent colors, simple manufacturing processes, and high production efficiency. Effect

Inactive Publication Date: 2021-02-09
广东河源住方高分子材料有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the production process of artificial stone, especially fish-belly white, the plate produced by the background technology has stiff, stiff, unnatural, large color difference, etc., and it is difficult to achieve the natural effect of natural fish-belly white

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Streak fish belly white quartz stone plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The rhyolite fish maw white quartz stone plate is composed of different components. The content of each component of the rhyolite fish maw white quartz stone plate is calculated by weight percentage: 32% of 60-mesh quartz sand, 50% of 400-mesh quartz powder, unsaturated polyester resin 8.56%, 40 mesh glass particles 8%, the weight of coupling agent is 1% of unsaturated polyester resin weight, the weight of curing agent is 1% of unsaturated polyester resin weight, the weight of color paste is unsaturated polyester resin 1% of the weight of the resin, the weight of the accelerator is 15% of the weight of the curing agent.

[0031] The curing agent includes a medium temperature curing agent and a room temperature initiator, wherein the medium temperature curing agent is tert-butyl peroxide diethylhexanoate, and the room temperature initiator is methyl ethyl ketone peroxide.

[0032] The accelerator is cobalt naphthenate.

[0033] The coupling agent is a silane coupling ag...

Embodiment 2

[0035] The flow pattern fish maw white quartz stone plate is composed of materials with different components. The content of each component of the flow pattern fish maw white quartz stone plate is calculated by weight percentage: 40% of 70 mesh quartz sand, 34% of 500 mesh quartz powder, and 10.32% of unsaturated polyester resin. %, 60 mesh glass particles 13%, the weight of the coupling agent is 2% of the weight of the unsaturated polyester resin, the weight of the curing agent is 1.5% of the weight of the unsaturated polyester resin, and the weight of the color paste is the weight of the unsaturated polyester resin 5% by weight, the weight of accelerator is 25% by weight of curing agent.

[0036] The curing agent includes a medium temperature curing agent and a room temperature initiator, the medium temperature curing agent is tert-butyl diethyl hexanoate or tert-butyl peroxide, and the room temperature initiator is methyl ethyl ketone peroxide.

[0037] The accelerator is c...

Embodiment 3

[0040] The rhyolite fish maw white quartz stone plate is composed of different components. The content of each component of the rhyolite fish maw white quartz stone plate is calculated by weight percentage: 80 mesh quartz sand 33.5%, 600 mesh quartz powder 33.5%, unsaturated polyester resin 11.64% %, 80 mesh glass particles 18%, the weight of the coupling agent is 3% of the weight of the unsaturated polyester resin, the weight of the curing agent is 2% of the weight of the unsaturated polyester resin, the weight of the color paste is the weight of the unsaturated polyester resin 10% by weight, the weight of accelerator is 30% by weight of curing agent.

[0041] The curing agent includes a medium temperature curing agent and a room temperature initiator, the medium temperature curing agent is tert-butyl diethyl hexanoate or tert-butyl peroxide, and the room temperature initiator is methyl ethyl ketone peroxide.

[0042] The accelerator is cobalt naphthenate.

[0043] The coupl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a streak fish belly white quartz stone plate and a preparation method thereof. The streak fish belly white quartz stone plate is prepared from, by weight, 30%-50% of 60-80-meshquartz sand, 30%-50% of 400-600-mesh quartz powder, 8%-12% of unsaturated polyester resin, 1%-3% of a curing agent, 1%-3% of a coupling agent, 8%-18% of 40-80-mesh glass particles; the weight of thecoupling agent accounts for 1%-3% of the weight of the unsaturated polyester resin, the weight of the curing agent accounts for 1%-2% of the weight of the unsaturated polyester resin, the weight of the color paste accounts for 1%-10% of the weight of the unsaturated polyester resin, and the weight of the accelerant accounts for 15%-30% of the weight of the curing agent. Unsaturated polyester resinserves as an auxiliary material and is fully and evenly stirred with quartz sand, quartz powder, glass particles, a coupling agent, a curing agent, color paste, an accelerant and the like, and then the quartzite flower plate is prepared through the procedures of material distribution, pressing, heating curing shaping, thickness fixing, polishing and the like.

Description

technical field [0001] The invention relates to the technical field of building material preparation, in particular to a flow pattern fish maw white quartz stone plate and a preparation method thereof. Background technique [0002] Artificial quartz stone is composed of more than 90% of natural quartz and about 10% of colorants, resins and other additives for adjusting bonding and curing. It is a plate processed by negative pressure vacuum, high frequency vibration molding, heating and curing (the temperature is determined by the production method according to the type of curing agent, in the field of architectural decoration, stone is beautiful, elegant, decorative, etc. Features have become one of the main decorative materials. [0003] Artificial quartz stone slabs have the advantages of high brightness, bending resistance, good hardness, and no pollution. They are widely used in interior decoration, floors, interior walls, kitchens, bathrooms, hotels, banks, etc. In th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18B24B1/00B28D1/00B29C67/24E04C2/04C04B111/54
CPCB24B1/00B28D1/00B29C67/244C04B26/18C04B2111/542E04C2/04C04B14/06C04B14/22C04B24/42C04B24/008C04B24/045C04B2103/54C04B24/04
Inventor 杨康肖炳平龚峰
Owner 广东河源住方高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com