Heat-resistant non-cured rubber asphalt waterproof coating, preparation method and coiled material thereof

A kind of asphalt waterproof coating and non-curing rubber technology, which is applied in the direction of asphalt coating, recycled rubber coating, coating, etc., can solve the problems of low heat resistance, easy slipping, and poor creep performance, so as to improve heat resistance , good creep effect

Inactive Publication Date: 2021-01-29
北新防水(四川)有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, non-curing rubber asphalt waterproof coatings are widely used at present, but the traditional non-curing rubber asphalt waterproof coatings have low heat resistance, basically around 65-70 degrees, and the façade construction is easy to flow and slip under high temperature in summer. For this kind of heat resistance, the general stress relaxation is also above 0.25, and the creep property is not very good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant non-cured rubber asphalt waterproof coating, preparation method and coiled material thereof
  • Heat-resistant non-cured rubber asphalt waterproof coating, preparation method and coiled material thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A heat-resistant non-curing rubber asphalt waterproof coating, its preparation method is as follows:

[0023] (1) will be 70 # After mixing 55 parts of asphalt, 1 part of tackifying resin, 20 parts of naphthenic oil, 1 part of modified SBR, 10 parts of desulfurized rubber powder, and 2 parts of silane coupling agent KH550, the temperature was raised to 125 °C at a heating rate of 2 °C / min. Stir for 40 min at a stirring rate of 1100 r / min.

[0024] (2) Add 0.2 parts of allyl methacrylate, raise the temperature to 160°C at a heating rate of 1°C / min, stir for 1 hour at a stirring rate of 400r / min, make it evenly mixed, then cool to room temperature, and the preparation is completed , inspection, barreling, storage.

Embodiment 2

[0026] A heat-resistant non-curing rubber asphalt waterproof coating, its preparation method is as follows:

[0027] (1) will be 90 # After mixing 65 parts of asphalt, 5 parts of tackifying resin, 35 parts of naphthenic oil, 5 parts of modified SBR, 17 parts of desulfurized rubber powder, and 4 parts of silane coupling agent KH560, the temperature was raised to 140 °C at a heating rate of 2 °C / min. Stir for 50 min at a stirring rate of 1100 r / min.

[0028] (2) Then add 0.5 parts of heat-resistant modifier 8903, raise the temperature to 170°C at a heating rate of 2°C / min, stir at a stirring rate of 500r / min for 1.2h, make it evenly mixed, and then cool to room temperature to prepare Completion, inspection, barreling, storage.

Embodiment 3

[0030] A heat-resistant non-curing rubber asphalt waterproof coating, its preparation method is as follows:

[0031] (1) will be 70 # After mixing 60 parts of asphalt, 4 parts of tackifying resin, 25 parts of naphthenic oil, 4 parts of modified SBR, 15 parts of desulfurized rubber powder, and 2 parts of silane coupling agent KH570, the temperature was raised to 130 °C at a heating rate of 1 °C / min. Stir for 45min at a stirring rate of 1100r / min.

[0032] (2) Then add 0.3 parts of heat-resistant modifier 8903, raise the temperature to 165°C at a heating rate of 1°C / min, stir at a stirring rate of 500r / min for 1.1h, make it evenly mixed, then cool to room temperature, and prepare Completion, inspection, barreling, storage.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Heat resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a heat-resistant non-cured rubber asphalt waterproof coating, a preparation method and a coiled material thereof. The heat-resistant non-cured rubber asphalt waterproof coatingcomprises the following components in parts by weight: 55-65 parts of asphalt, 1-5 parts of tackifying resin, 1-5 parts of SBS, 20-35 parts of a plasticizer, 1-5 parts of modified SBR, 10-17 parts ofdesulfurized rubber powder, 2-4 parts of a silane coupling agent and 0.2-0.5 part of a heat-resistant modifier. The product obtained by adopting the technical scheme of the invention is green and environment-friendly, not only can keep a never-cured form, but also has higher heat resistance and cohesiveness, the heat resistance can reach 100 DEG C, the thermal aging property is good, and long-termand reliable waterproof and heat-resistant functions can be exerted.

Description

technical field [0001] The invention belongs to the field of building engineering materials, and in particular relates to a heat-resistant non-curing rubber asphalt waterproof coating, a preparation method and a coiled material thereof. Background technique [0002] In building waterproofing engineering, the vibration of the building, thermal expansion and contraction, subsidence, deformation and cracking of the base will cause the waterproof layer to break and cause leakage. In practical engineering applications, for waterproof projects with large deformation of the base, the waterproof layer is generally constructed using the empty laying method or the point-bonding method to alleviate the damage to the waterproof layer caused by deformation and cracking of the base, but it is still prone to local leakage and Cause water leakage and so on. Therefore, there is an urgent need for a new type of creep material in the field of building waterproofing. The property can well abs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D195/00C09D191/00C09D117/00C09D7/65C09D7/63E04B1/66E02D31/02E04D5/10
CPCC08L2201/08C08L2205/035C09D195/00C09D7/63C09D7/65E02D31/02E04B1/66E04D5/10C08L91/00C08L17/00C08K5/544C08K5/101
Inventor 骆晓彬
Owner 北新防水(四川)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com