Spraying preparation method for aluminum profile processing

A technology for aluminum profile processing and aluminum profiles, which is applied to the surface coating liquid device, pretreatment surface, coating, etc., can solve the problem of poor bonding between the sprayed coating and the surface of the aluminum profile, bubbles and wrinkles on the surface of the aluminum profile It is easy to produce problems such as paint adhesion needs to be improved, so as to achieve better spraying effect, prevent bubbles and wrinkles, and increase the protection ability

Inactive Publication Date: 2020-12-25
肇庆新联昌金属实业有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of spray coating preparation method for aluminum profile processing, to solve the problem that the paint surface adhesion of spray coating proposed in the above-mentioned background technology needs to be improved, after long-term use, the paint surface changes color, and the aluminum profile surface bubbles And wrinkles are easy to produce, and the problem of poor bonding between the sprayed coating and the surface of the aluminum profile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spraying preparation method for aluminum profile processing
  • Spraying preparation method for aluminum profile processing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A spraying preparation method for processing aluminum profiles, comprising the following steps:

[0033] S1. Substrate pretreatment: pretreat the aluminum profile before spraying, derust the rust layer and rust spots on the surface of the aluminum profile, use equipment to remove the welding points and welding slag of the aluminum profile, and use a rust remover To remove the rust layer and rust spots on the surface of aluminum profiles, high-efficiency corrosion inhibitors are added to the rust remover, and the welding points and welding slag are removed by grinding equipment, and the dust collection equipment is used to reduce dust flying while grinding;

[0034] S2. Water washing and alkali washing: Pour pure water and cleaning agent into the cleaning equipment. The cleaning agent is an industrial degreasing cleaning agent. Put the aluminum profiles into the cleaning equipment for cleaning. After cleaning, put the aluminum profiles in the aluminum washing tank for use...

Embodiment 2

[0041] A spraying preparation method for processing aluminum profiles, comprising the following steps:

[0042] S1. Substrate pretreatment: pretreat the aluminum profile before spraying, derust the rust layer and rust spots on the surface of the aluminum profile, use equipment to remove the welding points and welding slag of the aluminum profile, and use a rust remover To remove the rust layer and rust spots on the surface of aluminum profiles, high-efficiency corrosion inhibitors are added to the rust remover, and the welding points and welding slag are removed by grinding equipment, and the dust collection equipment is used to reduce dust flying while grinding;

[0043] S2. Water washing and alkali washing: Pour pure water and cleaning agent into the cleaning equipment. The cleaning agent is an industrial degreasing cleaning agent. Put the aluminum profiles into the cleaning equipment for cleaning. After cleaning, put the aluminum profiles in the aluminum washing tank for use...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of aluminum profile spraying, in particular to a spraying preparation method for aluminum profile processing. The method comprises the following steps that S1, basematerial pretreatment is conducted, specifically, an aluminum profile is pretreated before spraying, rust layers and rust points on the surface of the aluminum profile are removed, and welding pointsand welding slag of the aluminum profile are ground and removed through equipment; S2, water washing and alkali washing are conducted, specifically, pure water and a cleaning agent are poured into cleaning equipment, the aluminum profile is placed into the cleaning equipment to be cleaned, after cleaning, the aluminum profile is placed into an aluminum washing tank to be subjected to alkali washing through alkali liquor, pure water is used again for thoroughly cleaning the aluminum profile, and the aluminum profile is aired after water washing; and S3, chromizing treatment is conducted, specifically, a chromizing solution is used for reacting with the aluminum profile, and a protective layer is formed on the surface of the aluminum profile. According to the method, a spraying primer has high adhesive force, toughness and hardness, the surface adhesive force of finish paint is extremely high, fluorocarbon varnish has super weather resistance, the fluorocarbon varnish takes fluororesin as a base material, the durability and the anti-ultraviolet function are high, and the paint surface of the aluminum profile is prevented from discoloring.

Description

technical field [0001] The invention relates to the field of spray coating of aluminum profiles, in particular to a spray coating preparation method for processing aluminum profiles. Background technique [0002] With the rapid development of economy and high technology, the aluminum smelting and aluminum profile processing industries have developed rapidly. Aluminum profiles are aluminum materials with different cross-sectional shapes obtained by hot melting and extrusion of aluminum rods. After spraying treatment, their corrosion resistance can be improved. resistance, heat resistance and wear resistance, increase its thickness or repair the size, etc. [0003] When the aluminum profile is sprayed, the adhesion of the sprayed paint surface needs to be improved. After a long time of use, the paint surface will change color, and bubbles and wrinkles on the surface of the aluminum profile will easily occur. The bonding force between the sprayed layer and the surface of the al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14B05D7/16B05D7/24B05D3/10
CPCB05D3/102B05D7/14B05D7/16B05D7/24B05D7/582B05D7/584B05D2202/25B05D2350/60B05D2501/00B05D2502/00B05D2504/00B05D2420/01B05D2420/02B05D2420/03
Inventor 邝次昭区耀灿
Owner 肇庆新联昌金属实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com