A kind of water-based ceramic paint and preparation method thereof

Abstract

The invention discloses a high-toughness water-based ceramic coating. The coating is a water-based, one-component, baking-drying product, composed of polyurethane modified nano-ceramic emulsion, silicone resin emulsion, high temperature resistant pigment, filler, auxiliary, p-toluenesulfonic acid amine neutralizer and water. Its construction is convenient, the VOC emission of coating is extremely low, and it has excellent flame retardant, heat resistance, corrosive medium shielding, bending resistance and impact resistance. It is an excellent choice for high temperature resistance and high durability anti-corrosion protective coating.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based ceramic coating with high temperature resistance, easy recoating, good corrosive medium shielding effect and bending resistance and a preparation method thereof. Background technique [0002] Ceramic coatings are a new class of coating materials based on organic-inorganic hybrid technology. Because its main structure is a covalently cross-linked inorganic (metal oxide, non-metal oxide, etc.) network, it has many traditional organic materials such as high hardness, friction resistance, flame retardancy, super weather resistance, low surface energy, and chemical solvent resistance. The incomparable performance advantages of coatings make it an excellent choice for preparing high-temperature-resistant and high-durability special coatings. [0003] Ceramic coatings are mainly based on sol-gel technology solutions, the core components of which are silica sol and silane...

AI Technical Summary

Problems solved by technology

[0005] (1) Poor storage stability: Since silane is prone to hydrolysis during storage, and then condenses with silica sol, pigments, and fillers to form insoluble matter, so in order to improve the stability of ceramic coatings, manufacturers can only use two-component or three-component Pack silane, silica sol, pigments and fillers in parts

At the same time, the shelf life of the product is also shorter than that of organic coatings

[0006] (2) Long curing time and short pot life: In order to obtain the ideal silanol prepolymer, promote the uniform film formation of ceramic coatings and avoid stress cracking, ceramic coatings need to be stirred and matured for a long time before application, and generally need to last for 2~ 8h; and the cured ceramic coating needs to be painted within a few hours, otherwise the product will gel and lose its performance

This cumbersome pre-mixing process puts forward higher requirements on the equipment and process control of coating companies

[0007] (3) Poor flexibility, no bending resistance, no impact resistance: Since the ceramic coating is a highly cross-linked inorganic network (hardness up to 9H), the coating is highly brittle

[0008] (4) Poor recoatability: due to the low surface energy of ceramic coatings and difficult wetting, the recoatability of the coating is poor

For unqualified products, it can only be reworked after grinding to the metal substrate, which seriously affects the coating efficiency, and it is impossible to obtain a high film thickness ceramic coating