Ivory white glaze ceramic product with light brown ground glaze, and preparation method thereof

A technology of ceramic products and bottom glaze, which is applied in the field of ivory white glaze ceramic products and its preparation, can solve the problems of not meeting consumers' aesthetic standards and low surface gloss, and achieve improved thermal stability, more gloss, and improved effect of density

Inactive Publication Date: 2020-12-04
福建省春秋陶瓷实业有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the surface gloss of ivory white ceramic products on the market is generally not high, which cannot meet the increasingly high aesthetic standards of consumers. New technical solutions are needed to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of method for preparing above-mentioned ivory white glaze ceramic product with light brown bottom glaze, comprises the following steps:

[0019] S1 mud preparation: Weigh 64 parts of feldspar powder, 40 parts of glass powder, 10 parts of quartz, 5 parts of kaolin, 4 parts of barium carbonate, 3 parts of iron oxide, 3 parts of copper oxide, 1 part of zinc oxide and 12 parts of calcite according to parts by weight After grinding, pass through a 200-mesh sieve, add water and ball mill for 15 minutes to obtain the bottom glaze slurry, weigh 22 parts of potassium feldspar, 12 parts of quartz, 12 parts of albite feldspar, 6 parts of calcite, 4 parts of zinc oxide, 5 parts of talcum powder, glass 13 parts of powder, 15 parts of zirconium frit, 6 parts of transparent frit, and 5 parts of fluorite are ground and passed through a 200-mesh sieve, added with water and ball milled for 15 minutes, to obtain a glaze slurry;

[0020] S2 Glazing: Immerse the green body in the bot...

Embodiment 2

[0023] A kind of method for preparing above-mentioned ivory white glaze ceramic product with light brown bottom glaze, comprises the following steps:

[0024] S1 mud preparation: Weigh 68 parts of feldspar powder, 43 parts of glass powder, 11 parts of quartz, 6 parts of kaolin, 6 parts of barium carbonate, 4 parts of iron oxide, 5 parts of copper oxide, 2 parts of zinc oxide and 13 parts of calcite according to parts by weight After grinding, pass through a 200-mesh sieve, add water and ball mill for 17 minutes to obtain the bottom glaze slurry, weigh 29 parts of potassium feldspar, 19 parts of quartz, 14 parts of albite, 10 parts of calcite, 6 parts of zinc oxide, 7 parts of talcum powder, glass 15 parts of ground powder, 17 parts of zirconium frit, 8 parts of transparent frit, and 7 parts of sodium carbonate were ground and passed through a 200-mesh sieve, added with water and ball milled for 17 minutes to obtain a glaze slurry;

[0025] S2 Glazing: immerse the green body in...

Embodiment 3

[0028] A kind of method for preparing above-mentioned ivory white glaze ceramic product with light brown bottom glaze, comprises the following steps:

[0029] S1 mud preparation: Weigh 72 parts of feldspar powder, 45 parts of glass powder, 12 parts of quartz, 8 parts of kaolin, 9 parts of barium carbonate, 5 parts of iron oxide, 8 parts of copper oxide, 3 parts of zinc oxide and 15 parts of calcite according to parts by weight After grinding, pass through a 200-mesh sieve, add water and ball mill for 20 minutes to obtain the bottom glaze slurry, weigh 35 parts of potassium feldspar, 25 parts of quartz, 15 parts of albite feldspar, 13 parts of calcite, 9 parts of zinc oxide, 10 parts of talcum powder, glass 18 parts of powder, 20 parts of zirconium frit, 12 parts of transparent frit, and 9 parts of fluorite are ground and passed through a 200-mesh sieve, and then milled with water for 20 minutes to obtain a glaze slurry;

[0030] S2 Glazing: Immerse the green body in the bottom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ceramic preparation, and concretely relates to an ivory white glaze ceramic product with light brown ground glaze, and a preparation method thereof. Theceramic product comprises ground glaze and cover glaze, wherein the ground glaze is prepared from, by weight, 64-72 parts of feldspar powder, 40-45 parts of glass powder, 10-12 parts of quartz, 5-8 parts of kaolin, 4-9 parts of barium carbonate, 3-5 parts of iron oxide, 3-8 parts of copper oxide, 1-3 parts of zinc oxide and 12-15 parts of calcite; and the cover glaze comprises, by weight, 22-35 parts of potassium feldspar, 12-25 parts of quartz, 12-15 parts of albite, 6-13 parts of calcite, 4-9 parts of zinc oxide, 5-10 parts of talcum powder, 13-18 parts of glass powder, 15-20 parts of zirconium frit, 6-12 parts of transparent frit and 5-9 parts of fluxing agent. The preparation method comprises the following steps: S1, slurry preparation; S2, glazing; and S3 sintering. The ceramic disclosed by the invention has the characteristics of high glossiness and good light transmission.

Description

technical field [0001] The invention relates to the technical field of ceramic preparation, in particular to an ivory white glaze ceramic product with a light brown bottom glaze and a preparation method thereof. Background technique [0002] Ceramics has a long history in our country. Its characteristics of easy cleaning, thermal stability and chemical stability make it gradually become a material that is often used in people's daily life. It is deeply loved by the people and can be made into bowls, plates, Daily necessities such as cups and cups can also be made into exquisite handicrafts, and can also be made into flooring, lampshades and other decoration and decoration items, so they have high application and collection value. At present, the same glaze color of ceramic products can be roughly divided into matte glaze and glossy glaze in terms of gloss, so the gloss presented is relatively single. [0003] Ivory white is called "ivory white" because of its whiteness like...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C03C8/12C03C8/00C04B41/89
CPCC03C8/00C03C8/12C03C8/14C04B41/52C04B41/89
Inventor 徐昌毅
Owner 福建省春秋陶瓷实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap