Treating and processing method of fraxinus mandshurica wood in furniture production

A processing method and technology of Fraxinus mandshurica, applied in wood processing, wood processing appliances, wood processing details, etc., can solve the problems of reduced dye penetration, high dyeing temperature, long dyeing time, etc.

Inactive Publication Date: 2020-10-23
ANHUI CHANGFA IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the tight structure of Ash wood, the permeability of dyestuffs in wood is reduced, and dye molecules can...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A method for processing mandshurica wood in furniture production, specifically, comprising the following steps:

[0014] Step 1: Put the cut ash wood into the prepared softener and pressurize and seal it for soaking. The pressure soaking pressure is 1.25MPa, the soaking time is 16 minutes, and the soaking temperature is 95°C. After soaking, put it in an oven at 66°C Drying in medium for 12 hours, the softener is made of the following components in terms of mass percentage: OP-10 accounts for 0.30%, ammonium persulfate accounts for 0.8%, polyvinyl alcohol accounts for 1.5%, sodium carbonate accounts for 0.75%, triethanolamine accounts for 0.35% , calcium carbonate accounts for 0.8%, lauryl acrylate accounts for 0.2%, and the rest is water;

[0015] Step 2: Preparation of penetrating agent: Mix 36 grams of tetraethyl orthosilicate and absolute ethanol at a mass ratio of 1.5:1.9, stir evenly, add 20 milliliters of deionized water, add 1.5 grams of boron oxide, 2.6 grams o...

Embodiment 2

[0021] A method for processing mandshurica wood in furniture production, specifically, comprising the following steps:

[0022] Step 1: Put the cut ash wood into the prepared softener and pressurize and seal it for soaking. The pressure soaking pressure is 1.27MPa, the soaking time is 18 minutes, and the soaking temperature is 96°C. After soaking, put it in an oven at 68°C Drying in medium for 14 hours, the softener is made of the following ingredients in terms of mass percentage: OP-10 accounted for 0.31%, ammonium persulfate accounted for 0.9%, polyvinyl alcohol accounted for 1.6%, sodium carbonate accounted for 0.80%, triethanolamine accounted for 0.40% , calcium carbonate accounts for 0.9%, lauryl acrylate accounts for 0.3%, and the rest is water;

[0023] Step 2: Preparation of penetrating agent: Mix 37 grams of tetraethyl orthosilicate and absolute ethanol at a mass ratio of 1.5:2.0, stir evenly, add 25 milliliters of deionized water, add 1.6 grams of boron oxide, 2.8 g...

Embodiment 3

[0029] A processing method for ash wood in furniture production, specifically, comprising the following steps:

[0030]Step 1: Put the trimmed ash wood into the prepared softener and pressurize and seal it for soaking. The pressure soaking pressure is 1.30MPa, the soaking time is 20 minutes, and the soaking temperature is 97°C. After soaking, put it in an oven at 70°C. Drying in medium for 16 hours, the softener is made of the following components in terms of mass percentage: OP-10 accounts for 0.32%, ammonium persulfate accounts for 1.0%, polyvinyl alcohol accounts for 1.7%, sodium carbonate accounts for 0.85%, triethanolamine accounts for 0.45% , calcium carbonate accounts for 1.0%, lauryl acrylate accounts for 0.4%, and the rest is water;

[0031] Step 2: Preparation of penetrating agent: mix 38 grams of tetraethyl orthosilicate and absolute ethanol at a mass ratio of 1.5:2.2, stir well, add 30 milliliters of deionized water, add 1.8 grams of boron oxide, 3.0 grams of tart...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a treating and processing method of fraxinus mandshurica wood in furniture production. The method comprises the following steps that fraxinus mandshurica wood is placed in a prepared softening agent to be soaked for 16-20 min, and then a prepared penetrating agent is used for conducting dipping treatment on the fraxinus mandshurica wood. Adsorption of the interior of the fraxinus mandshurica wood to dye can be improved, and the problems that the dye stays on the surface to color the fraxinus mandshurica wood , the dyeing rate is low, dyeing is uneven and fading occurseasily are solved. The treating and processing flow is simple, environmentally friendly and low in cost, the treated fraxinus mandshurica wood has an excellent dyeing effect, the colors of various rare wood can be imitated, the dyeing rate is high, use of dye is reduced, the dyeing temperature is low, the dyeing time is shortened, and the method has important significance in reducing environmentalpollution. Moreover, dyeing is firm, the durability is good, dye seepage and fading are not likely to happen, and the sense of reality of the wood grain color is achieved.

Description

technical field [0001] The invention relates to the technical field of furniture wood treatment and processing, in particular to a treatment and processing method of ash wood in furniture production. Background technique [0002] Mandshurica mandshurica has a round shape, tall and straight, strong adaptability, and has the ability to resist severe cold, drought, smoke and dust, diseases and insect pests, and is an excellent greening and ornamental tree species. At the same time, it can form a mixed forest with many coniferous and broad-leaved tree species to form a forest ecosystem with a composite structure, which is of great significance and effect on improving the water conservation of the entire forest, maintaining water and soil, and preventing environmental degradation. Ash wood has very good overall strength properties, good shock resistance and steam bending strength. Heartwood has moderate penetration resistance to preservative treatments, white wood has penetratio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/08B27K3/52B27K5/04B27K5/06
CPCB27K3/08B27K3/52B27K5/04B27K5/06
Inventor 张大昌
Owner ANHUI CHANGFA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap