Hard alloy used for producing 3D curved surface glass and preparation method thereof

A technology of curved glass and cemented carbide, applied in the field of cemented carbide and its preparation, can solve the problems of poor corrosion resistance, poor wear resistance, and high brittleness.

Inactive Publication Date: 2020-05-08
株洲众诚新材料科技股份有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of existing materials are poor corrosion resistance, poor wear resistance, high brittleness, poor electrical conductivity and other defects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The present invention provides a cemented carbide for producing 3D curved glass and a preparation method thereof. Those skilled in the art can learn from the content of this article and appropriately improve the process parameters. In particular, it should be pointed out that all similar replacements and modifications are obvious to those skilled in the art, and they all fall within the protection scope of the present invention. The method and application of the present invention have been described through the preferred embodiments. It is obvious that relevant personnel can modify or appropriately change and combine the methods and applications herein without departing from the content, spirit and scope of the present invention to realize and apply the present invention. Invent technology.

[0025] A cemented carbide used to produce 3D curved glass. The components and mass percentages of each component are as follows:

[0026] Tungsten carbide: 81%;

[0027] Cobalt: 3%;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hard alloy used for producing 3D curved surface glass and a preparation method thereof. The hard alloy comprises the following components of, by mass, 81% of tungsten carbide, 3% of cobalt, 8% of nickel, 2% of chromium dicarbonate, 1% of vanadium, 2% of tantalum and 3% of titanium. The hard alloy used for producing the 3D curved surface glass has good wear resistance, strength, and good conductivity, and further comprises the characteristics of strong corrosion resistance and excellent high-temperature strength under the working environment, the material can work continuously for 90 days or above, and the service life of the material is greatly prolonged.

Description

Technical field [0001] The invention relates to a hard alloy for producing 3D curved glass and a preparation method thereof. Background technique [0002] At present, the technology of manufacturing 3D curved glass is mainly hot bending technology, that is, the glass is bent and shaped by high pressure under high temperature and molten state, and then processed and polished to form 3D glass, which is widely used in 5G mobile phone screens, back covers, and wearable devices , Automotive glass, optical glass and other fields. The glass is at a high temperature during hot bending. At this time, the glass is strongly corrosive. Therefore, the soaking plate material used is required to have corrosion resistance, high temperature resistance, high strength and wear resistance. The materials used in the existing market are mainly tungsten-cobalt cemented carbide and cermet. Cemented carbide materials have good high temperature performance and good electrical conductivity, but their wear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C29/08C22C1/05C22C1/10
CPCC22C1/051C22C29/067C22C29/08
Inventor 李明欣莫立华彭江王水清李明华
Owner 株洲众诚新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products