Hard alloy connecting piece

A cemented carbide and connector technology, applied in welding equipment, metal layered products, metal processing equipment, etc., can solve the problems that high-end cemented carbide tools and precision instrument tile alloys cannot meet or cannot meet, and achieve good high temperature The effect of red hardness, smooth transition and high wear resistance

Inactive Publication Date: 2010-06-16
SHANGHAI UNIV OF ENG SCI
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the prior art and provide a cemented carbide connector to solve the problem that the existing cemented carbide connector cannot meet the requirements of high-precision and high-reliability high-end cemented carbide tools and precision instruments. The difficulty that Invar alloys cannot meet the strength requirements of special occasions and the requirements of high temperature red hardness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Select WC-Co cemented carbide with a thickness of 2mm (with a Co content of 18%) as the welded material 1, and select an Invar alloy with a thickness of 2mm (its composition and composition mass percentage are: 42% Ni and 58% Fe) For the material to be welded 2, choose a tungsten argon arc welding machine of the model NASTERTIG AC / DC 2500, and operate according to the conventional argon tungsten arc automatic welding process. The welding process parameters are: welding current 90A, welding voltage 11V, welding speed 4mm / sec, tungsten rod gun tip diameter 0.5~2mm, tungsten rod gun tip extension length 3~8mm, argon gas flow rate 10L / min, argon gas pressure 0.35Mpa at room temperature, welding process adopts direct current connection method.

[0015] After testing: the welded joint between the high-binder phase cemented carbide and the Invar alloy prepared in this example has no air holes, cracks, no η carbide formation at the interface, and the microhardness of the weld zo...

Embodiment 2

[0017] The WC-Co cemented carbide (wherein the Co content is 40%) with a thickness of 2mm is selected as the welded material 1, and the NiFeC-based rare earth Invar alloy with a thickness of 2mm is selected (its composition and composition mass percentage are: 30% Ni, 1 %C, 3.4% Mn, 5% Nb and 60.6% Fe) are the materials to be welded 2, and the argon tungsten arc welding machine model NASTERTIG AC / DC 2500 is selected, and the operation is performed according to the conventional argon tungsten arc automatic welding process. But no pre-weld preheating and post-weld heat treatment, no bevel opening and no filler material added, the welding process parameters are: welding current 180A, welding voltage 20V, welding speed 7mm / sec, tungsten rod tip diameter 0.5~2mm, tungsten The protruding length of the gun tip is 3-8mm, the flow rate of argon gas is 15L / min, the pressure of argon gas is 0.35Mpa at room temperature, and the welding process adopts the direct current connection method. ...

Embodiment 3

[0020] Select WC-Co cemented carbide with a thickness of 4mm (with a Co content of 30%) as the welded material 1, and select a NiFeC-based rare earth Invar alloy with a thickness of 2mm (its composition and composition mass percentage are: 35% Ni, 0.8 %C, 3.4% Mn, 4% Nb and 56.8% Fe) are the materials to be welded 2, and the argon tungsten arc welding machine model NASTERTIG AC / DC 2500 is selected, and the operation is performed according to the conventional argon tungsten arc automatic welding process. But no pre-weld preheating and post-weld heat treatment, no bevel opening and no filler material added, the welding process parameters are: welding current 130A, welding voltage 15V, welding speed 1mm / sec, tungsten rod tip diameter 0.5~2mm, tungsten The protruding length of the gun tip is 3-8mm, the flow rate of argon gas is 3L / min, the pressure of argon gas is 0.35Mpa at room temperature, and the welding process adopts the direct current connection method.

[0021] After testi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
microhardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cemented carbide connector, which is formed by welding a high-cementing-phase cemented carbide with an invar alloy through argon tungsten-arc automatic welding process. The cemented carbide connector not only has high-strength structure by making use of the high strength, high wearing resistance and good red hardness of cemented carbide; but also has low-expansion function by making use of the constant thermal expansion property having invar effect in a specific temperature scope of the invar alloy, therefore the connector meets the special requirements of high-end cemented carbide tool and invar alloy precise instrument for materials, namely the connector has the characteristics of high wearing resistance, good high-temperature red hardness and high-temperature resistance, as well as keeps constant or deforms slightly in a specific temperature scope with the temperature changes. According to welding process of the invention, the interface of the welded samplehas no pores, crackles or crisp eta carbide, the microscopic constitution and microhardness which is greater than 400HV0.2 transit smoothly.

Description

technical field [0001] The invention relates to a hard alloy connecting piece, in particular to a connecting piece between hard alloy with high bonding phase and Invar alloy. Background technique [0002] Because WC-Co cemented carbide has high strength, good wear resistance, low thermal expansion coefficient and good high temperature red hardness, it is required that the material has wear resistance, high temperature resistance, and deformation changes with temperature within a certain temperature range. It plays a very important role in the research and development of high-end carbide tools or precision instruments that remain constant or do not change much. However, the tool materials or precision small deformation materials currently used for connection are usually high-speed steel or stainless steel, such as high-speed steel tools, Invar alloy and stainless steel connectors, etc. Most of these cemented carbide weldments exist due to excessive stress of heterogeneous mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/02B32B15/01B32B7/00B23K9/167B23K9/23B23K103/18
Inventor 徐培全赵秀娟何建萍
Owner SHANGHAI UNIV OF ENG SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com