A kind of tpu adhesive and hot melt adhesive film and application

A hot-melt adhesive film and adhesive technology, applied in the direction of adhesive, adhesive type, heat-activated film/sheet, etc., can solve the problems of not improving the quality and beauty of clothing, affecting the comfort of seamless sports clothing, and shortening the service life. , to achieve good adhesion and washing resistance, which is conducive to large-scale and rapid industrial operations, and overcomes the effects of poor resilience.

Active Publication Date: 2022-02-01
GUANGDONG YETOM NEW MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although the TPU hot-melt adhesive film on the market has a certain degree of elasticity and bonding strength, it still performs poorly in sportswear and underwear that require high elasticity, mainly due to low adhesion and poor washability. Poor, low tensile strength, large tensile deformation, etc.
Especially applied to the bottoms of seamless sports pants, bras, and side bones of sportswear, which affects the comfort of seamless sportswear, shortens the service life, and cannot improve the quality and appearance of clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tpu adhesive and hot melt adhesive film and application
  • A kind of tpu adhesive and hot melt adhesive film and application
  • A kind of tpu adhesive and hot melt adhesive film and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A TPU adhesive, including the following components of weight sharing:

[0048]

[0049] The dicate polyester TPU particles A are prepared from the following calculated raw materials: 70% polya-ethylene glycol esters 1000, 27% 4,4-dibenzene Okolin diisocyanate, 3% 1,4-butanediol

[0050] The diacorate polyester TPU particles B are prepared by the twin screw extruder by weight percentage of raw materials: 65% polycaricate butanol ester 1000, 30% 4,4-dibenzene Othane diisocyanate, 5% new pentylene glycol.

[0051] The preparation method of the above TPU adhesive includes the following steps:

[0052] The dicate polyester TPU particles A (the melt mass flow rate of 45 g / 10 minutes, the softening point is 110 ° C), the dicate polyester TPU particles B (the melt mass flow rate is 20g / 10) The minute, the softening point is 130 ° C), the modified copolyester 3112, the polycarbonate, the antioxidants 1010, the ultraviolet absorber UV-328 are mixed, and the granulation is extru...

Embodiment 2

[0058] A TPU adhesive, including the following components of weight sharing:

[0059]

[0060] The dicate polyester TPU particles are prepared by a double screw extruder by weight percentage of raw materials: 79% polya-ethylene glycol ester 2000, 18% 4,4-diphenyl group Methane diisocyanate and 3% 1,4-butanediol Download Adobe Reader

[0061] The polytetrahydrofuran polyether TPU particles are prepared from the following calculated raw material by a twin-screw extruder 1500, 29% isophorone diisocyanate, 2% 1, 4 - butanediol and 9% new pentylene glycol.

[0062] The preparation method of the above TPU adhesive includes the following steps:

[0063] The dicate polyester TPU particles (the melt mass flow rate of 35 g / 10 minutes, the softening point is 120 ° C), and the polytex hydrofuran polyether TPU granules (the melt mass flow rate is 25 g / 10 minutes, softened The point is 135 ° C), the polycarbonate, an antioxidant 1076, and the ultraviolet absorber UV-9 are mixed uniform, a...

Embodiment 3

[0069] A TPU adhesive, including the following components of weight sharing:

[0070]

[0071]

[0072] The diacorate polyester TPU particles A are prepared by the twin-screw extruder by weight percentage of raw materials: 70% polycaricate butanol ester 1000, 27% 4,4-dibenzene Okinane diisocyanate and 3% 1,4-butanediol;

[0073] The dicate polyester TPU particles B are prepared by the twin screw extruder by weight percentage of raw materials: 60% polycaric acid has been added 1000, 30% 4, 4'-two Cyclohexylmetane diisocyanate, 6% 1,4-butanediol and 7% neovanediol.

[0074] The preparation method of the above TPU adhesive includes the following steps:

[0075] The dicate polyester TPU particles A (the melt mass flow rate of 30 g / 10g / 10g, the softening point is 120 ° C), the dicate polyester TPU particles B (the melt mass flow rate is 50g / 10) The minute, the softening point is 115 ° C), the polybiimine, the modified copolyester 5120, the antioxidant 1076, the ultraviolet ab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of polymer adhesives, in particular to a TPU adhesive, a hot-melt adhesive film and its application. The TPU adhesive of the present invention comprises the following components by weight: 75-97 parts of TPU particles; 0-15 parts of modified polyester; 2-10 parts of anti-hydrolysis agent; 0.1-1 part of auxiliary agent. The hot-melt adhesive film of the present invention comprises a first adhesive layer, a substrate layer, and a second adhesive layer in sequence; the first adhesive layer is made of the above-mentioned TPU adhesive, and the second adhesive layer is made of the above-mentioned TPU adhesive Made; the base layer is mesh or film. The hot-melt adhesive film with a three-layer composite structure of the present invention is soft to the touch, has high tensile strength, excellent stretch recovery, good adhesion and washability, and can be widely used in underwear, underwear, and bras , mold cups, shoulder straps, shapewear, sportswear and other elastic clothing seamless bonding.

Description

Technical field [0001] The present invention relates to the field of polymer adhesive, particularly a hot melt adhesive film and the application of TPU. Background technique [0002] Polyurethane is a developmental rapid multifunctional polymer composite material, since the adjustability of the molecular structure and diverse variety of raw materials, and may be made of foams, elastomers, coatings, adhesives and other products in the form of extremely versatile . Similarly, by adjusting the raw materials and formulations can be designed for a variety of adhesive between the materials, a variety of different uses of a plurality of types of polyurethane adhesives. Polyurethane adhesive having excellent flexibility, impact resistance, chemical resistance, and particularly excellent low-temperature resistance and abrasion resistance. [0003] With the development of science and technology, knitwear has become increasingly broad market. In the conventional processing method, a knitted...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/06C09J175/08C09J167/00C09J11/08C09J11/06C09J7/21C09J7/25C09J7/35
CPCC09J175/06C09J11/08C09J11/06C09J7/35C09J7/255C09J175/08C09J7/21C09J7/25C09J2400/263C09J2467/006C09J2475/00C09J2475/006C09J2301/124C09J2301/304C08L75/06C08L67/00C08L79/00C08K5/1345
Inventor 梁坤焕欧阳效明梁锋
Owner GUANGDONG YETOM NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products