A kind of carbon nanotube/nanometer silver solder paste heat conduction material and preparation method thereof

A technology of carbon nanotubes and heat-conducting materials, applied in the direction of welding/cutting media/materials, welding equipment, manufacturing tools, etc., to achieve the effect of improving wettability, good application prospects, and simple process flow

Active Publication Date: 2021-09-28
GUILIN UNIV OF ELECTRONIC TECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, diamond, micro-copper, and graphene have been used as the reinforcing phase of nano-silver solder paste. Although the sintering temperature and overall thermal conductivity required in the silver paste preparation process have been improved, it is still not possible. Fully meet the development needs of existing fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of carbon nanotube/nanometer silver solder paste heat conduction material and preparation method thereof
  • A kind of carbon nanotube/nanometer silver solder paste heat conduction material and preparation method thereof
  • A kind of carbon nanotube/nanometer silver solder paste heat conduction material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Carrying out oxidation treatment and activation treatment on the carbon nanotube particles. Add 0.8g nano-carbon nanotube particles to the K of 0.35mol / L 2 Cr 2 o 7 Solution mixed with 0.25mol / L HCl solution, boiled at 70°C for 8h for oxidation treatment. Then place the oxidized carbon nanotubes in 0.024mol / L PdCl 2 Activation treatment is carried out in the solution, and finally the activated carbon nanotubes are repeatedly washed with deionized water until they become neutral;

[0031] (2) Electroless silver plating is performed on the carbon nanotube particles. At room temperature, add 0.06mol / L silver nitrate solution dropwise to analytically pure ammonia water with a concentration of 25% to configure the silver ammonia solution, then add activated carbon nanotube particles to the silver ammonia solution, and magnetically Stir, adjust the pH value of the mixed oxidation solution to 8, and finally add dropwise a formaldehyde solution with a concentration of ...

Embodiment 2

[0036] Other conditions are the same as in Example 1, and the properties of the materials prepared at different redox reaction temperatures are tested. The experimental results are shown in Table 1.

[0037] Table 1 Performance of thermally conductive materials at different redox reaction temperatures

[0038]

[0039] From the above results, it can be seen that the temperature ratio of the oxidation-reduction reaction is preferably 20° C. (Example 1).

Embodiment 3

[0041] Other conditions are the same as in Example 1, and the properties of the materials prepared with different pH values ​​of the mixed oxidation solution systems are tested, and the experimental results are shown in Table 2.

[0042] Table 2 The pH value of the mixed oxidation solution system on the performance of thermally conductive materials

[0043]

[0044]

[0045] From the above results, it can be seen that the pH ratio of the mixed oxidation solution system is preferably 8.0 (Example 1).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbon nanotube / nano-silver solder paste heat-conducting composite material and a preparation method thereof. Carbon nanotubes coated with silver on the surface are used as a reinforcing phase, and are doped into the nano-silver solder paste to make the nano-silver particles effective. Evenly adsorbed on the surface of silver-plated carbon nanotubes, the heat-conducting material has the advantages of high thermal conductivity, high bonding strength and shear strength, and the present invention overcomes the gap between carbon nanotubes and nano-silver particles. Weak interface binding ability, simple preparation process.

Description

technical field [0001] The invention relates to the technical field of preparation of composite nanomaterials, in particular to a carbon nanotube / nanometer silver solder paste heat-conducting material and a preparation process thereof. Background technique [0002] Nano-silver solder paste is prepared by mixing nano-silver particles with organic solvents such as dispersants, adhesives, and diluents, through mechanical stirring, ultrasonic oscillation, and other methods. And in recent years, relying on its own excellent thermal, electrical, mechanical properties and reliability, it has been paid more and more attention to electronic packaging such as light-emitting diodes (LEDs), semiconductor lasers, and IGBTs. However, the impact of high temperature on the reliability, life, stress-strain behavior and creep behavior of electronic products, as well as the temperature cycle caused by frequent switching of power devices will cause product failure. At the same time, the bondin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/40B23K35/22B23K35/24B23K35/36
CPCB23K35/22B23K35/24B23K35/36B23K35/40
Inventor 张平许晖周漫姜雄杨培培杨道国
Owner GUILIN UNIV OF ELECTRONIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com