Preparation method of carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material

A three-dimensional fabric and polyimide technology is applied in the field of preparation of carbon fiber three-dimensional fabric reinforced polyimide-carbon-based dual-element matrix composite materials, which can solve the problems of inability to serve for a long time and the reduction of mechanical properties of materials, and achieve an optimized interface. Mechanical properties, optimized fracture toughness, improved efficiency

Active Publication Date: 2019-10-01
SHANGHAI UNIV
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although C / C F The short-term use temperature reaches 3000°C, but oxidation begins to occur at 370°C in an aerobic environment, resulting in a decrease in the mechanical properties of the material and making it unable to serve for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material
  • Preparation method of carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material
  • Preparation method of carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Example 1 Carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite (PI-C / C F ) preparation

[0061] In this implementation case, a method for preparing a carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite material includes the following steps:

[0062] 1) Using carbon fiber three-dimensional fabric as a prefabricated body, the carbon matrix is ​​introduced through chemical vapor infiltration (CVI) and liquid phase impregnation-pyrolysis (PIP) processes to prepare a carbon-based composite blank with a density of 1.30g / cm3.

[0063] 2) Put the carbon-based composite material blank prepared in step (1) into the impregnation reaction kettle, and vacuumize at room temperature to make the pressure in the kettle reach 10 2 Pa, then the polyamic acid resin A (chemical structural formula as shown in formula I) that solid content is 40% is introduced in the still, impregnates blank 1.0h; Subseq...

Embodiment 2

[0066] Example 2 Preparation of carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite (PI-C / CF)

[0067] In this embodiment, a method for preparing a carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite material comprises the following steps:

[0068] 1) Using carbon fiber three-dimensional fabric as a prefabricated body, the carbon matrix is ​​introduced through chemical vapor infiltration (CVI) and liquid phase impregnation-pyrolysis (PIP) processes to prepare a carbon-based composite material blank with a density of 1.40g / cm3.

[0069] 2) Put the carbon-based composite material blank prepared in step (1) into the impregnation reaction kettle, and vacuumize at room temperature to make the pressure in the kettle reach 10 3 Pa, then the polyamic acid resin B (chemical structural formula as shown in formula II) with a solid content of 38% is introduced into the still, and the blank is impregn...

Embodiment 3

[0072] Example 3 Preparation of carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite (PI-C / CF)

[0073] In this implementation case, a method for preparing a carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite material includes the following steps:

[0074] 1) Using carbon fiber three-dimensional fabric as a prefabricated body, the carbon matrix is ​​introduced through chemical vapor infiltration (CVI) and liquid phase impregnation-pyrolysis (PIP) processes to prepare a carbon-based composite blank with a density of 1.45g / cm3.

[0075] 2) Put the carbon-based composite material blank prepared in step (1) into the impregnation reaction kettle, and vacuumize at room temperature to make the pressure in the kettle reach 10 2 Pa, then the polyamic acid resin C (chemical structural formula as shown in formula III) that solid content is 35% is imported in the still, impregnates blank 0.5h; Subseq...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wear rateaaaaaaaaaa
densityaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material (PI-C / CF) which comprises carbon fiber three-dimensional fabric prefabricated bodies, carbon substrates and polyimide resin substrates. The carbon fiber three-dimensional fabric enhanced polyimide-carbon based dual substrate composite material prepared according to theembodiment has the advantages of excellent high-temperature resistance and excellent wear-resistant performance; the friction coefficient is small; the material belongs to a high-intensity high-temperature-resistant wear-resistant novel composite material, and the requirement in the fields of military science, aerospace and the like on the high-temperature wear-resistant structure element materials can be met.

Description

technical field [0001] The invention relates to the preparation of a carbon fiber three-dimensional fabric reinforced polyimide-carbon-based binary matrix composite material, and belongs to the technical field of composite material preparation and performance regulation. Background technique [0002] Polyimide (PI) is a kind of polymer containing characteristic imide ring and aromatic hydrocarbon group structure on the main chain, which has good corrosion resistance, excellent mechanical strength, outstanding heat resistance and self-lubricating properties, some PI It has no obvious melting point and the thermal deformation temperature can reach 350°C. It is an important high-temperature self-lubricating and wear-resistant material in the aerospace field. At present, more fillers such as graphite, fiber and fiber woven cloth are added to PI to obtain PI-based composites with better mechanical properties and friction properties. But the important thing is that none of them c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/83C04B35/84C04B41/83C08L79/08C08K3/04C08K7/06
CPCC04B35/83C04B41/009C04B41/4892C04B41/83C04B2235/77C04B2235/96C08K3/04C08K7/06C08L2201/08C08L79/08
Inventor 俞鸣明张传媛方琳任慕苏孙晋良
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap